Assignee: New Energy Development Organization
•
Filing: 1983-07-19
•
Granted: 1985-07-23
•
Expires: 2003-07-19
Abstract
Abstract The present invention discloses a manufacturing method of a sodium-sulfur storage battery comprising battery components of metallic members jointed by means of a thermocompression method to an alpha -alumina ring which is jointed to a sodium ion conductive solid electrolytic tube using solder glass. According to the invention, thicknesses of the metallic members thermocompressively jointed to upper and lower surfaces of said alpha -alumina ring is in a range from about 0.2 mm to about 0.6 mm. Plate-shaped aluminum rings are disposed between said alpha -alumina ring and said metallic members respectively and are thermocompressively jointed in air under condition of a temperature in a range from about 600 DEG to about 625 DEG C. and a pressure in a range from about 1200 to about 1600 kg/cm2.
Inventors
- 👤 Hiroshi Kagawa
- 👤 Suminobu Iwabuchi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 10:30
CPC Classifications
H; H01; H01M; H01M10/00; H01M10/36; H01M10/39; H01M10/3909; H01M50/00; H01M50/10; H01M50/147; H01M50/148; H01M50/1535; Y; Y02; Y02E; Y02E60/00; Y02E60/10; Y02P; Y02P70/00; Y02P70/50; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49108
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
144 words
A method for manufacturing a sodium-sulfur storage battery having an alpha-alumina ring jointed with solder glass to a sodium ion conductive solid electrolyte tube, a cathodic cover of sulfur-resistant metal and an anodic cover of molten sodium-resistant metal, the cathodic and anodic covers each having a thickness in the range from 0.2 mm to 0.6 mm and each being thermocompressively jointed to respective lower and upper surfaces of the alpha-alumina ring, the method further comprising the steps of: disposing first and second plate-shaped aluminum rings between the lower and upper surfaces of the alpha-aluminum ring an the cathodic and anodic covers respectively; and in air and at a temperature in the range from 600° C. to 625° C., thermocompressively jointing the cathodic and anodic covers to the alpha-aluminum ring with an applied jointing pressure in the range from 1200 to 1600 kg/cm 2 .
Claim 2
Independent Claim
144 words
A method for manufacturing a sodium-sulfur storage battery having an alpha-alumina ring jointed with solder glass to a sodium ion conductive solid electrolyte tube, a cathodic cover of sulfur-resistant metal and an anodic cover of molten sodium-resistant metal, the cathodic and anodic covers each having a thickness in the range from 0.2 mm to 0.6 mm and each being thermocompressively jointed to respective lower and upper surfaces of the alpha-alumina ring, the method further comprising the steps of: disposing first and second plate-shaped aluminum rings between the lower and upper surfaces of the alpha-aluminum ring an the cathodic and anodic covers respectively; and in air and at a temperature in the range from 600° C. to 625° C., thermocompressively jointing the cathodic and anodic covers to the alpha-aluminum ring with an applied jointing pressure in the range from 1200 to 1600 kg/cm 2 .
Claim 3
Dependent Claim
52 words
The method according to claim 1 wherein the first and second plate-shaped aluminum rings each have a purity of at least 97.5% and a thickness in the range from 100 μm to 150 μm before thermocompresive jointing and a thickness after thermocompressive jointing in the range from 30 μm to 80 μm.
Claim 4
Dependent Claim
51 words
The method according to claim 1 wherein the first and second plate-shaped aluminum rings each have an inside diameter less than or equal to respective inside diameters of the cathodic and anodic covers, and an outer diameter greater than or equal to respective outer diameters of the cathodic and anodic covers.
Claim 5
Independent Claim
233 words
A method for manufacturing a sodium-sulfur storage battery having an alpha-alumina ring jointed with solder glass to a sodium ion conductive solid electrolyte tube, a cathodic cover of sulfur-resistant metal and an anodic cover of molten sodium-resistant metal, the cathodic and anodic covers each having a thickness in the range from 0.2 mm to 0.6 mm and each being thermocompressively jointed to respective lower and upper surfaces of the alpha-alumina ring, the method further comprising the steps of: disposing first and second plate-shaped aluminum rings between the respective lower and upper surfaces of the alpha-alumina ring and the cathodic and anodic covers, respectively; in air, pressing the cathodic and anodic covers and the first and second plate-shaped aluminum rings to the respective lower and upper surfaces of the alpha-alumina ring between lower and upper pressing means with an applied pressure not exceeding 150 kg/cm 2 ; in air, heating the alpha-alumina ring, the cathodic and anodic covers and the first and second plate-shaped aluminum rings pressed therebetween while applying pressing pressure thereto not exceeding 200 kg/cm 2 ; and in air, continuing to heat the alpha-alumina ring, the cathodic and anodic covers and the first and second plate-shaped alumium rings pressed therebetween until the temperature thereof increases to 600° C., whereupon the applied pressure thereon is increased to a pressure in the range from 1200 to 1600 kg/cm 2 to produce thermocompressive jointing.
Claim 6
Independent Claim
233 words
A method for manufacturing a sodium-sulfur storage battery having an alpha-alumina ring jointed with solder glass to a sodium ion conductive solid electrolyte tube, a cathodic cover of sulfur-resistant metal and an anodic cover of molten sodium-resistant metal, the cathodic and anodic covers each having a thickness in the range from 0.2 mm to 0.6 mm and each being thermocompressively jointed to respective lower and upper surfaces of the alpha-alumina ring, the method further comprising the steps of: disposing first and second plate-shaped aluminum rings between the respective lower and upper surfaces of the alpha-alumina ring and the cathodic and anodic covers, respectively; in air, pressing the cathodic and anodic covers and the first and second plate-shaped aluminum rings to the respective lower and upper surfaces of the alpha-alumina ring between lower and upper pressing means with an applied pressure not exceeding 150 kg/cm 2 ; in air, heating the alpha-alumina ring, the cathodic and anodic covers and the first and second plate-shaped aluminum rings pressed therebetween while applying pressing pressure thereto not exceeding 200 kg/cm 2 ; and in air, continuing to heat the alpha-alumina ring, the cathodic and anodic covers and the first and second plate-shaped alumium rings pressed therebetween until the temperature thereof increases to 600° C., whereupon the applied pressure thereon is increased to a pressure in the range from 1200 to 1600 kg/cm 2 to produce thermocompressive jointing.
Claim 7
Dependent Claim
50 words
The method according to claim 4, wherein the first and second plate-shaped aluminum rings each have a purity of at least 97.5%, a thickness before thermocompressive jointing in the range from 100 μm to 150 μm, and a thickness after thermocompressive jointing in the range from 30 μm to λμm.
Claim 8
Dependent Claim
53 words
The method according to claim 4, wherein the first and second plate-shaped aluminum rings each have an inner diameter less than or equal to respective inner diameters of the cathodic and anodic covers, respectively, and an outer diameter greater than or equal to respective outer diameters of the cathodic and anodic covers, respectively.
References Cited (Backward Citations)
US3070875A
Cited
US3296692A
Cited
US4037027A
Cited
US4236661A
Cited
US4245012A
Cited
US4419418A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-07-22 | 1989-01-21 | 1989-07-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-07-22 | 1993-01-21 | 1993-07-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-07-22 | 1997-01-21 | 1997-07-23 | $7700.00 | Window Closed / Lapsed |