Method for lowering the surface energy of glass
Assignee: PPG Industries Inc
•
Filing: 1982-03-05
•
Granted: 1985-07-16
•
Expires: 2002-03-05
Abstract
Abstract The surface energy of a glass article is reduced by adsorbing multivalent cations such as chromium onto a glass surface, then treating the surface with an aqueous solution of an alkali metal alkylate such as sodium stearate or oleate to strongly bond the long chain paraffinic or olefinic acid anion to the glass surface by ionic bonding of the alkylate anion to the adsorbed multivalent cation thereby rendering the glass surface non-wettable and lubricated.
Inventors
- 👤 Helmut Franz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 06:46
CPC Classifications
C; C03; C03C; C03C17/00; C03C17/28; Y; Y10; Y10T; Y10T428/00; Y10T428/31; Y10T428/315
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
120 words
A method for treating a glass surface comprising the steps of: a. contacting the glass surface with a solution comprising multivalent metal cations capable of adsorption onto the glass surface and capable of formation of an insoluble alkylate at a temperature below the boiling point of the solution and for a time sufficient to result in adsorption of the metal cations by the glass; and b. contacting the glass surface, subsequent to the adsorption of multivalent cations, with a solution of a soluble alkylate compound comprising acid anions capable of reacting with the adsorbed metal cations to form an insoluble alkylate at a temperature below the boiling point of the solution and below the melting point of the alkylate compound.
Claim 2
Independent Claim
120 words
A method for treating a glass surface comprising the steps of: a. contacting the glass surface with a solution comprising multivalent metal cations capable of adsorption onto the glass surface and capable of formation of an insoluble alkylate at a temperature below the boiling point of the solution and for a time sufficient to result in adsorption of the metal cations by the glass; and b. contacting the glass surface, subsequent to the adsorption of multivalent cations, with a solution of a soluble alkylate compound comprising acid anions capable of reacting with the adsorbed metal cations to form an insoluble alkylate at a temperature below the boiling point of the solution and below the melting point of the alkylate compound.
Claim 3
Dependent Claim
43 words
The method according to claim 1, wherein the glass surface is contacted with an aqueous solution of a salt containing a multivalent cation selected from the group consisting of calcium, magnesium, barium, aluminum, strontium, chromium, copper, tin, iron, titanium, zirconium and zinc ions.
Claim 4
Dependent Claim
21 words
The method according to claim 2, wherein the salt is selected from the group consisting of chromic, stannic and ferric chlorides.
Claim 5
Dependent Claim
43 words
The method according to claim 2, wherein the glass surface is contacted, subsequent to the adsorption of a multivalent metal cation, with a solution of an alkali or alkaline earth metal alkylate wherein the acid anion comprises from 10 to 20 carbon atoms.
Claim 6
Dependent Claim
45 words
The method according to claim 1, claim 2 or claim 3, wherein the glass surface is contacted, subsequent to the adsorption of a multivalent metal cation, with a solution of an alkali metal alkylate selected from the group consisting of sodium stearate and sodium oleate.
Claim 7
Dependent Claim
11 words
A glass article produced according to the method of claim 5.
References Cited (Backward Citations)
US3161534A
Cited
US3460960A
Cited
US3414429A
Cited
US3743491A
Cited
US3920869A
Cited
US4130407A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-07-15 | 1989-01-14 | 1989-07-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-07-15 | 1993-01-14 | 1993-07-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-07-15 | 1997-01-14 | 1997-07-16 | $7700.00 | Window Closed / Lapsed |