Production of composite membranes
Assignee: EIDP Inc
•
Filing: 1984-10-31
•
Granted: 1985-07-16
•
Expires: 2004-10-31
Abstract
Abstract A process is disclosed for producing a composite reverse osmosis membrane. The process involves forming a porous polysulfone membrane from a solution of polysulfone followed by quenching the polysulfone membrane in an aqueous solution of m-phenylenediamine followed by reacting the m-phenylenediamine on the polysulfone membrane with either trimesoyl chloride or cyclohexane-1,3,5-tricarbonyl chloride in a water immiscible solution thereof.
Inventors
- 👤 Sherman A. Sundet
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 09:31
CPC Classifications
B; B01; B01D; B01D69/00; B01D69/12; B01D71/00; B01D71/06; B01D71/56; Y; Y10; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249953; Y10T428/249978; Y10T428/31504; Y10T428/31533
Claims Analysis
Total Claims: 2
Claim 1
Independent Claim
101 words
A thin film composite membrane prepared by forming a membrane from a solution of a polysulfone in a polar, organic solvent containing from 10 to 20% by weight polysulfone, quenching the resulting membrane in an aqueous bath containing 0.1 to 10% weight/volume m-phenylenediamine, removing the resulting porous polysulfone film containing m-phenylenediamine from the aqueous bath, and immersing said porous polysulfone film in a water immiscible solution comprising 0.05 to 5% weight/volume trimesoyl chloride, cyclohexane-1,3,5-tricarbonyl chloride, or mixtures thereof whereby the m-phenylene diamine reacts with the trimesoyl chloride or cyclohexane-1,3,5-tricarbonyl chloride to form a continuous layer supported by the porous polysulfone membrane.
Claim 2
Dependent Claim
101 words
A thin film composite membrane prepared by forming a membrane from a solution of a polysulfone in a polar, organic solvent containing from 10 to 20% by weight polysulfone, quenching the resulting membrane in an aqueous bath containing 0.1 to 10% weight/volume m-phenylenediamine, removing the resulting porous polysulfone film containing m-phenylenediamine from the aqueous bath, and immersing said porous polysulfone film in a water immiscible solution comprising 0.05 to 5% weight/volume trimesoyl chloride, cyclohexane-1,3,5-tricarbonyl chloride, or mixtures thereof whereby the m-phenylene diamine reacts with the trimesoyl chloride or cyclohexane-1,3,5-tricarbonyl chloride to form a continuous layer supported by the porous polysulfone membrane.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-07-15 | 1989-01-14 | 1989-07-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-07-15 | 1993-01-14 | 1993-07-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-07-15 | 1997-01-14 | 1997-07-16 | $7700.00 | Window Closed / Lapsed |