Antistatic or electrically conductive thermoplastic polyurethanes: process for their preparation and their use
Assignee: BASF SE
•
Filing: 1984-06-14
•
Granted: 1985-07-02
•
Expires: 2004-06-14
Abstract
Abstract Antistatic and/or electrically conductive thermoplastic polyurethanes contain carbon black whose surface area determined by the BET method is from 600 to 1200 m 2 /g, have a dibutylphthalate absorption number of 300 to 450 cm 3 /100 g, a pour density of less than 250 kg/m 3 , and an average particle size less than 50 nm. Incorporation of the carbon black into the thermoplastic polyurethane produced by the continuous sheet method takes place at temperatures under the primary melt peak for the crystalline rigid segments, measured by means of differential calorimetry, preferably in an extruder. The products are suitable for preparing films for flat heating elements, antistatic hoses, cables, and profiles.
Inventors
- 👤 Gerhard Zeitler
- 👤 Gerhard Bittner
- 👤 Knud Faehndrich
- 👤 Hans M. Rombrecht
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 02:03
CPC Classifications
C; C08; C08K; C08K3/00; C08K3/02; C08K3/04; B; B29; B29C; B29C70/00; B29C70/88; B29C70/882; H; H01; H01B; H01B1/00; H01B1/20; H01B1/24; B29K; B29K2995/00; B29K2995/0003; B29K2995/0005; Y; Y10; Y10S; Y10S524/00; Y10S524/91
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
116 words
A process for the manufacture of antistatic or electrically conductive thermoplastic polyurethanes comprising incorporating carbon black into a thermoplastic polyurethane in an amount of from 2 weight percent to 35 weight percent, based on the weight at the finished polurethane, at a temperature below the thermoplastic polyurethane rigid crystalline segment melting point peak, wherein said carbon black is characterized by (1) a surface area of from 600 m 2 /g to 1200 m 2 /g; (2) a dibutyl phthalate absorption number of from 300 to 450 cm 3 per 100 g of carbon black; (3) a pour density of less than 250 kg/m 3 ; and (4) an average particle size of less than 50 nm.
Claim 2
Dependent Claim
116 words
A process for the manufacture of antistatic or electrically conductive thermoplastic polyurethanes comprising incorporating carbon black into a thermoplastic polyurethane in an amount of from 2 weight percent to 35 weight percent, based on the weight at the finished polurethane, at a temperature below the thermoplastic polyurethane rigid crystalline segment melting point peak, wherein said carbon black is characterized by (1) a surface area of from 600 m 2 /g to 1200 m 2 /g; (2) a dibutyl phthalate absorption number of from 300 to 450 cm 3 per 100 g of carbon black; (3) a pour density of less than 250 kg/m 3 ; and (4) an average particle size of less than 50 nm.
Claim 3
Dependent Claim
43 words
The process of claim 1 wherein said thermoplastic polyurethane comprises the catalyzed addition polymerization product of an organic diisocyanate, a polyol having a molecular weight of from 500 to 8000, and a chain extender having a molecular weight of from 60 to 400.
Claim 4
Dependent Claim
25 words
The process of claim 1 wherein the thermoplastic polyurethane has a hardness of Shore A 60 to Shore D 70 before incorporation of carbon black.
Claim 5
Dependent Claim
25 words
The process of claim 2 wherein the thermoplastic polyurethane has a hardness of Shore A 60 to Shore D 70 before incorporation of carbon black.
Claim 6
Dependent Claim
21 words
The process of claim 2 wherein said organic diisocyanate is selected from the group consisting of 4,4'-diphenylmethane diisocyanate and 1,5-naphthalene diisocyanate.
Claim 7
Dependent Claim
36 words
The process of claim 2 wherein the polyol is selected from the group consisting of: (a) a polyester polyol condensation polymer of adipic acid and a 2 to 6 carbon diol; (b) polycaprolactone; and (c) polytetrahydrofuran.
Claim 8
Dependent Claim
22 words
The process of claim 1 wherein said carbon black is incorporated into said thermoplastic polyurethane by mixing in a twin screw extruder.
Claim 9
Dependent Claim
14 words
An antistatic or electrically conductive thermoplastic polyurethane prepared by the process of claim 1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-07-01 | 1988-12-31 | 1989-07-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-07-01 | 1992-12-31 | 1993-07-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-07-01 | 1996-12-31 | 1997-07-02 | $7700.00 | Window Closed / Lapsed |