Thermosettable compositions convertible to vitreous carbon and process for preparation thereof
Assignee: Plastics Engineering Co
•
Filing: 1983-03-01
•
Granted: 1985-07-02
•
Expires: 2003-03-01
Abstract
Abstract The compositions disclosed herein are suitable for thermosetting and conversion to vitreous carbon. They comprise intimate uniform mixtures of powder or otherwise blendable form of 20-80% by weight of a solid phenolic-aldehyde Novolak resin and of 20-80% by weight of a solid phenolic-aldehyde resol resin, the percentages being based on the combined weight of the Novolak and resol resins, and the aldehyde in said Novolak resin comprising at least 50 molar percent, preferably substantially 100 percent, furfuraldehyde, together with a carbonaceous filler, preferably graphite, in a proportion as high as 76% by weight based on the total composition. Generally the graphite may comprise 30-70%, advantageously 35-65% and preferably 40-60% of the molding composition. The vitreous carbon produced from these compositions have improved properties in electrical properties and in the capability of being suitably molded and carburized into large thin plates which are much more stress-free than otherwise produced. The composition may also contain 0-12 parts, preferably 0.12-8 parts hexamethylenetetramine per 100 parts of Novolak resin. The intimate mixture of these resins is advantageously made by blending resin components having a particle size of less than 40 mesh, preferably less than 100 mesh.
Inventors
- 👤 Louis L. Korb
- 👤 Phillip A. Waitkus
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 18:10
CPC Classifications
C; C08; C08K; C08K3/00; C08K3/02; C08K3/04; C08L; C08L61/00; C08L61/04; C08L61/06; Y; Y10; Y10S; Y10S524/00; Y10S524/904
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
87 words
A solid thermosettable intimate blend comprising 30-76 percent by weight of a finely divided carbonaceous particulate filler and 24-70 percent by weight of a finely divided phenolic resin mixture comprising 20-80 parts by weight of a phenolic-furfuraldehyde Novolak resin which is fusible upon heating, and 20-80 parts by weight of a phenolic-aldehyde resol resin, which is thermosettable upon heating, the sum of said parts of Novolak and resol resins totaling 100 parts by weight, the aldehyde in said Novolak comprising at least 50 molar percent of furfuraldehyde.
Claim 2
Dependent Claim
87 words
A solid thermosettable intimate blend comprising 30-76 percent by weight of a finely divided carbonaceous particulate filler and 24-70 percent by weight of a finely divided phenolic resin mixture comprising 20-80 parts by weight of a phenolic-furfuraldehyde Novolak resin which is fusible upon heating, and 20-80 parts by weight of a phenolic-aldehyde resol resin, which is thermosettable upon heating, the sum of said parts of Novolak and resol resins totaling 100 parts by weight, the aldehyde in said Novolak comprising at least 50 molar percent of furfuraldehyde.
Claim 3
Dependent Claim
20 words
The blend of claim 1 in which the carbonaceous filler is graphite and the phenolic in both resins is phenol.
Claim 4
Dependent Claim
33 words
The blend of claim 2 in which the graphite is present in the proportion of 35-65 percent by weight and the resin mixture is 35-65 percent by weight of the total resin composition.
Claim 5
Dependent Claim
21 words
The blend of claim 3 in which the phenolic-furfuraldehyde Novolak/phenolic-aldehyde resol resin ratio is in the range of 30/70 to 50/50.
Claim 6
Dependent Claim
19 words
The blend of any of claims 1 to 4 in which the aldehyde of the resol resin is formaldehyde.
Claim 7
Dependent Claim
22 words
The blend of any of claims 1 to 4 in which the aldehyde in said Novolak is substantially 100 molar percent furfuraldehyde.
Claim 8
Dependent Claim
19 words
The blend of claim 2 in which the aldehyde in said Novolak is at least 75 molar percent furfuraldehyde.
Claim 9
Dependent Claim
20 words
The blend of claim 1 which is formed from Novolak resin particles having a size no greater than 40 mesh.
Claim 10
Dependent Claim
20 words
The blend of claim 2 which is formed from resol resin particles having a size no greater than 40 mesh.
Claim 11
Dependent Claim
23 words
The blend of claim 5, in which said blend is derived from Novolak resin particles having a size no greater than 100 mesh.
Claim 12
Dependent Claim
23 words
The blend of claim 3 in which said blend is derived from Novolak resin particles having a size no greater than 32 microns.
Claim 13
Dependent Claim
27 words
The blend of claim 11 in which the resol aldehyde is formaldehyde and the graphite proportion is 40-60 percent by weight based on the total resin composition.
Claim 14
Dependent Claim
27 words
The blend of claim 4 in which the resol aldehyde is formaldehyde and the graphite proportion is 40-60 percent by weight based on the total resin composition.
Claim 15
Dependent Claim
23 words
The blend of claim 4, in which the furfuraldehyde/phenol molar ratio in said Novolak resin is in the range of 0.6/1 to 0.9/1.
Claim 16
Dependent Claim
29 words
The blend of claim 4, in which the resol aldehyde is formaldehyde and the formaldehyde/phenol molar ratio in said resol resin is in the range of 1.05/1 to 1.55/1.
Claim 17
Dependent Claim
29 words
The blend of claim 4, in which the resol aldehyde is formaldehyde and the furfuraldehyde/phenol molar ratio in said Novolak resin is in the range of 0.7/1 to 0.75/1.
Claim 18
Dependent Claim
144 words
A process for preparing a blend of claim 1, comprising the steps of: (1) grinding a solid phenolic furfuraldehyde Novolak resin to a particle size of less than 40 mesh on a U.S. Standard sieve; (2) grinding a solid phenolic-aldehyde resol resin, capable of thermosetting merely upon heating, to a particle size of less than 40 mesh on a U.S. Standard sieve; and (3) mixing said ground resins together with a finely divided carbonaceous powder to a homogeneous mixture suitable for molding, said carbonaceous powder being used in a proportion of 30-70 percent based on total weight of carbonaceous powder and resin powders, and said Novolak and resol powders being used in a proportion of 20-80 parts by weight of said Novolak and 20-80 parts by weight of said resol, the combined weight of said Novolak and said resol totaling 100 parts by weight.
Claim 19
Dependent Claim
14 words
The process of claim 17 in which the phenolic in both resins is phenol.
Claim 20
Dependent Claim
27 words
The process of claim 18 in which said phenolic-furfuraldehyde Novolak resin is a phenol-aldehyde resin in which at least 50 molar percent of the aldehyde is furfuraldehyde.
Claim 21
Dependent Claim
19 words
The process of claim 19 in which at least 75 molar percent of the said Novolak aldehyde is furfuraldehyde.
Claim 22
Dependent Claim
15 words
The process of claim 19 in which substantially all of said Novolak aldehyde is furfuraldehyde.
Claim 23
Dependent Claim
14 words
The process of claim 21 in which the aldehyde in said resol is formaldehyde.
Claim 24
Dependent Claim
14 words
The process of claim 18 in which the aldehyde in said resol is formaldehyde.
References Cited (Backward Citations)
US3109712A
Cited
GB1098029A
Cited
US3410718A
Cited
US3723368A
Cited
SU521294A1
Cited
US3969124A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-07-01 | 1988-12-31 | 1989-07-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-07-01 | 1992-12-31 | 1993-07-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-07-01 | 1996-12-31 | 1997-07-02 | $7700.00 | Window Closed / Lapsed |