Method of repairing breaks in sheet material
Assignee: Individual
•
Filing: 1984-05-29
•
Granted: 1985-07-02
•
Expires: 2004-05-29
Abstract
Abstract A method of repairing breaks in plastic sheet members such as those used on dashes of automobiles. The abutting edges of the crack formed at the break are coated with a liquid cyanoacrylate adhesive. The crack is filled with a particulate material, preferably hardened polyurethane foam or graphite which has been ground to a particle size corresponding roughly to that of common table salt. The particulate filler is soaked with the liquid cyanoacrylate adhesive and the liquid is then dried. For cracks of substantial depths, several layers of filler soaked with the adhesive may be utilized to completely fill the crack. After the filler composition has completely hardened and the repair smoothed by sanding, the immediate zone may be textured by spraying with a liquid vinyl lacquer. When the lacquer is dry, the region may be painted to blend with the remainder of the member.
Inventors
- 👤 Gerald J. Mader
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 09:09
CPC Classifications
B; B29; B29C; B29C73/00; B29C73/02; B29C73/24; B29C73/26; B29C2073/262; B29L; B29L2031/00; B29L2031/30; B29L2031/3005; B29L2031/3008; B29L2031/3014; Y; Y10; Y10T; Y10T428/00; Y10T428/20
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
86 words
A method of repairing breaks in sheet members resulting in a crack between the spaced apart portions of the members, said method comprising the steps of: coating the crack defining edges of said portions with a liquid cyanoacrylate adhesive; immediately thereafter and before said coating is dry, filling the crack with particulate material; soaking the particulate material in the crack with said liquid cyanoacrylate adhesive; and drying said adhesive to form a hardened filler in the crack and adhered to said edges, thereby joining the portions.
Claim 2
Independent Claim
86 words
A method of repairing breaks in sheet members resulting in a crack between the spaced apart portions of the members, said method comprising the steps of: coating the crack defining edges of said portions with a liquid cyanoacrylate adhesive; immediately thereafter and before said coating is dry, filling the crack with particulate material; soaking the particulate material in the crack with said liquid cyanoacrylate adhesive; and drying said adhesive to form a hardened filler in the crack and adhered to said edges, thereby joining the portions.
Claim 3
Dependent Claim
20 words
The method of claim 1, wherein said particulate material is derived by the step of grinding hardened cellular polyurethane foam.
Claim 4
Dependent Claim
29 words
The method of claim 2, wherein said particulate material is ground to reduce the size of said particles to about the size of the grains of common table salt.
Claim 5
Dependent Claim
12 words
The method of claim 1, wherein said particulate material is ground graphite.
Claim 6
Dependent Claim
20 words
The method of claim 1, wherein the graphite particles are about the size of the grains of common table salt.
Claim 7
Independent Claim
142 words
A method of repairing breaks in sheet members which result in a crack between spaced apart portions of the members, said method comprising the steps of: coating the crack defining edges of said portions with a liquid cyanoacrylate adhesive; before said adhesive coating has dried, placing a layer of particulate material in the crack, the particles of said material being about the size of common table salt; soaking the particles in the crack with liquid cyanoacrylate adhesive; drying said adhesive; repeating the steps of applying a layer of said particulate material followed by soaking said material with said adhesive and then letting the soaking adhesive dry until the crack is completely filled with hardened adhesive and particulate material composition; sanding the composition and adjacent regions of the member to smooth the junction therebetween; and applying a texturing coating over the repaired area.
Claim 8
Independent Claim
142 words
A method of repairing breaks in sheet members which result in a crack between spaced apart portions of the members, said method comprising the steps of: coating the crack defining edges of said portions with a liquid cyanoacrylate adhesive; before said adhesive coating has dried, placing a layer of particulate material in the crack, the particles of said material being about the size of common table salt; soaking the particles in the crack with liquid cyanoacrylate adhesive; drying said adhesive; repeating the steps of applying a layer of said particulate material followed by soaking said material with said adhesive and then letting the soaking adhesive dry until the crack is completely filled with hardened adhesive and particulate material composition; sanding the composition and adjacent regions of the member to smooth the junction therebetween; and applying a texturing coating over the repaired area.
Claim 9
Dependent Claim
13 words
The invention of claim 6, wherein said texturing coating is a vinyl lacquer.
Claim 10
Dependent Claim
26 words
The invention of claim 6, wherein said texturing coating is applied to the repaired area by the step of spraying liquid vinyl lacquer over said area.
Claim 11
Dependent Claim
22 words
The invention of claim 8, wherein is included the step of painting the repaired area to match the color of said member.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-07-01 | 1988-12-31 | 1989-07-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-07-01 | 1992-12-31 | 1993-07-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-07-01 | 1996-12-31 | 1997-07-02 | $7700.00 | Window Closed / Lapsed |