Anti-corrosion treatment process
Assignee: United Kingdom Atomic Energy Authority
•
Filing: 1983-09-07
•
Granted: 1985-07-02
•
Expires: 2003-09-07
Abstract
Abstract An anti-corrosion treatment process for protecting alloys containing chromium and cobalt and/or nickel against corrosion by superheated water, which consists of heating the alloy in contact with a solution containing EDTA and ferrous ions to within a temperature range that forms a thick, chromium oxide-rich glassy film over the surface of the alloy. Where the EDTA is present in the form of one of its disubstituted alkali salts, the solution is preferably heated to 200° C. to 210° C. under chemically reducing conditions. Further heating of the solution to 225°-250° C. improves the corrosion resistance of the film, by increasing its iron oxides content and converting at least part of its structure to microcrystalline. Films produced by the present process are found to have a very low nickel and cobalt content.
Inventors
- 👤 John H. Carter
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 00:57
CPC Classifications
C; C23; C23C; C23C22/00; C23C22/05; C23C22/68; G; G21; G21C; G21C17/00; G21C17/02; G21C17/022; G21C17/0225
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
125 words
An anti-corrosion treatment process for protecting an alloy, containing chromium and at least one metal selected from nickel and cobalt, against corrosion by superheated water comprising exposing the alloy to an aqueous solution containing iron, preferably ferrous, ions and a complexone selected from at least one of EDTA, a salt of EDTA, a derivative of EDTA and a salt of the derivative, and heating the solution to such a temperature range that a corrosion resistant film, that contains chromium oxide and iron oxide but that is substantially free from cobalt, nickel and compounds of cobalt and nickel, in formed on the surface of the alloy, and maintaining the the solution within that temperature range until the corrosion resistant film is at least 300 nm thick.
Claim 2
Dependent Claim
125 words
An anti-corrosion treatment process for protecting an alloy, containing chromium and at least one metal selected from nickel and cobalt, against corrosion by superheated water comprising exposing the alloy to an aqueous solution containing iron, preferably ferrous, ions and a complexone selected from at least one of EDTA, a salt of EDTA, a derivative of EDTA and a salt of the derivative, and heating the solution to such a temperature range that a corrosion resistant film, that contains chromium oxide and iron oxide but that is substantially free from cobalt, nickel and compounds of cobalt and nickel, in formed on the surface of the alloy, and maintaining the the solution within that temperature range until the corrosion resistant film is at least 300 nm thick.
Claim 3
Dependent Claim
17 words
A process according to claim 1 wherein the complexone comprises a disubstituted alkali metal salt of EDTA.
Claim 4
Dependent Claim
14 words
A process according to claim 1 wherein the solution also contains a reducing agent.
Claim 5
Dependent Claim
12 words
A process according to claim 3 wherein the reducing agent comprise hydrazine.
Claim 6
Dependent Claim
27 words
A process according to claim 2 wherein the solution is heated to within the temperature range 175° C. to 225° C., preferably 200° C. to 210° C.
Claim 7
Dependent Claim
28 words
A process according to claim 5 wherein the solution is subsequently heated to within the temperature range 210° C. to 250° C., preferably 225° C. to 250° C.
Claim 8
Dependent Claim
43 words
A process according to claim 1 wherein the complexone is selected from at least one of a ferrous salt of EDTA, a chromium salt of EDTA, a ferrous salt of a derivative of EDTA, and a chromium salt of a derivative of EDTA.
Claim 9
Independent Claim
142 words
A method of treating the internal surfaces of a primary coolant circuit of a pressurised water reactor by an anti-corrosion treatment process for protecting an alloy, containing chromium and at least one metal selected from nickel and cobalt, against corrosion by superheated water comprising exposing the alloy to an aqueous solution containing iron, preferably ferrous, ions and a complexone selected from at least one of EDTA, a salt of EDTA, a derivative of EDTA and a salt of the derivative and heating the solution to such a temperature range that a corrosion resistant film, that contains chromium oxide and iron oxide but that is substantially free from cobalt, nickel and compounds of cobalt and nickel, is formed on the surface of the alloy, and maintaining the solution within that temperature range until the corrosion resistant film is at least 300 nm thick.
Claim 10
Independent Claim
142 words
A method of treating the internal surfaces of a primary coolant circuit of a pressurised water reactor by an anti-corrosion treatment process for protecting an alloy, containing chromium and at least one metal selected from nickel and cobalt, against corrosion by superheated water comprising exposing the alloy to an aqueous solution containing iron, preferably ferrous, ions and a complexone selected from at least one of EDTA, a salt of EDTA, a derivative of EDTA and a salt of the derivative and heating the solution to such a temperature range that a corrosion resistant film, that contains chromium oxide and iron oxide but that is substantially free from cobalt, nickel and compounds of cobalt and nickel, is formed on the surface of the alloy, and maintaining the solution within that temperature range until the corrosion resistant film is at least 300 nm thick.
Claim 11
Dependent Claim
17 words
A process according to claim 8 wherein the complexone comprises a disubstituted alkali metal salt of EDTA.
Claim 12
Dependent Claim
14 words
A process according to claim 8 wherein the solution also contains a reducing agent.
Claim 13
Dependent Claim
12 words
A process according to claim 10 wherein the reducing agent comprises hydrazine.
Claim 14
Dependent Claim
27 words
A process according to claim 9 wherein the solution is heated to within the temperature range 175° C. to 225° C., preferably 200° C. to 210° C.
Claim 15
Dependent Claim
28 words
A process according to claim 12 wherein the solution is subsequently heated to within the temperature range 210° C. to 250° C., preferably 225° C. to 250° C.
Claim 16
Dependent Claim
43 words
A process according to claim 8 wherein the complexone is selected from at least one of a ferrous salt of EDTA, a chromium salt of EDTA, a ferrous salt of a derivative of EDTA, and a chromium salt of a derivative of EDTA.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-07-01 | 1988-12-31 | 1989-07-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-07-01 | 1992-12-31 | 1993-07-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-07-01 | 1996-12-31 | 1997-07-02 | $7700.00 | Window Closed / Lapsed |