High tear strength flexible urethane foam composition and method of preparation
Assignee: LINAMAR MACHINE Ltd
•
Filing: 1984-07-02
•
Granted: 1985-06-25
•
Expires: 2004-07-02
Abstract
Abstract A flexible polyurethane foam composition characterized by high tensile or tear strength is prepared by reacting an MDI prepolymer, prepared by reacting a MDI having a low functionality with an ethylene oxide-capped polypropylene glycol polyol, with a small amount of a tetraethylene glycol as a cross-linking agent and an ethylene oxide-capped polypropylene glycol polyol, the reaction carried out in the presence of a blowing amount of a blowing agent, such as water or a halocarbon, and a catalytic amount of a polyurethane catalyst, such as a combination of an amine and tetravalent tin catalyst. The addition of a small amount of a chlorinated phosphate flame-retardant agent mixed with the reaction provides for a polyurethane foam composition of good fire retardancy and which when exposed to open flame does not melt, but chars. Further, the addition of a trimerization catalyst provides a foam composition with reduced shrinkage.
Inventors
- 👤 Stuart B. Smith
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 12:55
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/70; C08G18/72; C08G18/74; C08G18/76; C08G18/7657; C08G18/7664; C08G18/08; C08G18/10; C08G18/28; C08G18/40; C08G18/48; C08G18/4833; C08G18/4837; C08G18/4841; C08G18/65; C08G18/66; C08G18/6666; C08G18/667; C08G18/6674; C08G2110/00; C08G2110/0008; C08G2110/0041; C08G2110/005; C08G2110/0058; C08G2110/0083; C08G2115/00; C08G2115/02; C08G2150/00; C08G2150/60; Y; Y10; Y10S; Y10S521/00; Y10S521/902; Y10S521/914
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
124 words
A flexible polyurethane foam composition characterized by a high tensile or tear strength, which foam composition is prepared by reacting (a) 100 parts by weight of a MDI-polyol prepolymer, which prepolymer is prepared by reacting 100 parts of MDI having a functionality of about 2.4 or less with from about 35 to 75 parts by weight of an ethylene oxide-capped polyol; (b) about 2 to 10 parts by weight of a tetraethylene glycol; and (c) about 90 to 120 parts by weight of an ethylene oxide-capped polypropylene glycol polyol, the reaction carried out in the presence of a blowing amount of a blowing agent and a catalytic amount of a polyurethane catalyst to produce a flexible polyurethane foam of high tensile or tear strength.
Claim 2
Dependent Claim
124 words
A flexible polyurethane foam composition characterized by a high tensile or tear strength, which foam composition is prepared by reacting (a) 100 parts by weight of a MDI-polyol prepolymer, which prepolymer is prepared by reacting 100 parts of MDI having a functionality of about 2.4 or less with from about 35 to 75 parts by weight of an ethylene oxide-capped polyol; (b) about 2 to 10 parts by weight of a tetraethylene glycol; and (c) about 90 to 120 parts by weight of an ethylene oxide-capped polypropylene glycol polyol, the reaction carried out in the presence of a blowing amount of a blowing agent and a catalytic amount of a polyurethane catalyst to produce a flexible polyurethane foam of high tensile or tear strength.
Claim 3
Dependent Claim
19 words
The foam composition of claim 1 wherein the MDI has a functionality ranging from about 2.0 to about 2.2.
Claim 4
Dependent Claim
23 words
The foam composition of claim 1 wherein the ethylene oxide-capped polypropylene glycol polyol has a hydroxyl number ranging from about 25 to 50.
Claim 5
Dependent Claim
20 words
The foam composition of claim 1 wherein the ethylene oxide-capped polyol of the prepolymer is an ethylene oxide-capped polypropylene polyol.
Claim 6
Dependent Claim
29 words
The foam composition of claim 1 wherein the ethylene oxide-capped polyol employed in preparing the prepolymer in the reaction is the same as the ethylene oxide-capped polypropylene glycol polyol.
Claim 7
Dependent Claim
24 words
The foam composition of claim 1 wherein th ethylene oxide-capped polyol employed in the prepolymer ranges from about 40 to 65 parts by weight.
Claim 8
Dependent Claim
23 words
The foam composition of claim 1 wherein the polyurethane catalyst comprises a combination of a tetravalent organo tin catalyst and an amine catalyst.
Claim 9
Dependent Claim
18 words
The foam composition of claim 1 wherein the blowing agent comprises water, a halocarbon or a combination thereof.
Claim 10
Dependent Claim
28 words
The foam composition of claim 1 wherein the polyurethane composition includes from about 2 to 12 parts by weight per 100 parts of MDI as a flame-retardant agent.
Claim 11
Dependent Claim
14 words
The foam composition of claim 8 wherein the flame-retardant agent comprises a chlorinated phosphate.
Claim 12
Dependent Claim
17 words
The foam composition of claim 1 which includes a cell control amount of a silicone cell-control agent.
Claim 13
Dependent Claim
25 words
The foam silicone cell control agent composition of claim 1 wherein the blowing agent comprises water and the foam prepared is an open cell foam.
Claim 14
Dependent Claim
27 words
The foam composition of claim 1 wherein the blowing agent comprises a halocarbon and which foam composition includes a shrinkage reducing amount of a surface-metal trimerization catalyst.
Claim 15
Dependent Claim
33 words
The foam composition of claim 13 wherein the trimerization catalyst comprises a potassium fatty acid salt in an amount of from about 0 to 3 parts per 100 parts of a MDI prepolymer.
Claim 16
Dependent Claim
26 words
The foam composition of claim 13 which inludes a silicone cell control agent in an amount to promote the formation of a flexible closed cell foam.
Claim 17
Dependent Claim
29 words
The foam composition of claim 13 which inludes a reactive accelerating amount of an organo-lead compound to reduce the cream time and tack free time of the foam composition.
Claim 18
Dependent Claim
43 words
The foam composition of claim 1 which includes a blowing amount of a fluorocarbon as a blowing agent, a silicone agent to provide a closed cell foam, and a shrinkage-reducing amount of potassium octoate, and a cream time reducing amount of lead octoate.
Claim 19
Dependent Claim
191 words
A flexible closed cell polyurethane foam composition characterized by high tensile or tear strength and reduced shrinkage which foam composition is prepared by reacting: (a) an A side composition comprising 100 parts by weight of an MDI-polyol prepolymer, which prepolymer is prepared by reacting 100 parts of MDI having an average functionality of about 2.0 to 2.2 with from about 40 to 65 parts by weight of an ethylene oxide-capped polypropylene polyol with a B side composition comprising (b) from about 4 to 8 parts by weight of a tetraethylene glycol; (c) about 90 to 120 parts by weight of the ethylene oxide-capped polypropylene glycol polyol employed to prepare the prepolymer; and (d) the reaction carried out in the presence of about 1 to 15 parts by weight of a liquid fluorocarbon blowing agent; a catalytic amount of a co-catalyst system comprising an amine catalyst and a tetravalent organo-tin catalyst; a cell control amount of a silicone agent; a shrink reducing amount of a potassium fatty acid salt, and a cream time reducing amount of a lead fatty acid salt to reduce the cream time to less than about 1 second.
Claim 20
Dependent Claim
191 words
A flexible closed cell polyurethane foam composition characterized by high tensile or tear strength and reduced shrinkage which foam composition is prepared by reacting: (a) an A side composition comprising 100 parts by weight of an MDI-polyol prepolymer, which prepolymer is prepared by reacting 100 parts of MDI having an average functionality of about 2.0 to 2.2 with from about 40 to 65 parts by weight of an ethylene oxide-capped polypropylene polyol with a B side composition comprising (b) from about 4 to 8 parts by weight of a tetraethylene glycol; (c) about 90 to 120 parts by weight of the ethylene oxide-capped polypropylene glycol polyol employed to prepare the prepolymer; and (d) the reaction carried out in the presence of about 1 to 15 parts by weight of a liquid fluorocarbon blowing agent; a catalytic amount of a co-catalyst system comprising an amine catalyst and a tetravalent organo-tin catalyst; a cell control amount of a silicone agent; a shrink reducing amount of a potassium fatty acid salt, and a cream time reducing amount of a lead fatty acid salt to reduce the cream time to less than about 1 second.
Claim 21
Dependent Claim
178 words
A flexible open cell polyurethane foam composition characterized by high tensile or tear strength and improved flame retardancy, which foam composition is prepared by reacting: (a) an A side composition comprising 100 parts by weight of an MDI-polyol prepolymer, which prepolymer is prepared by reacting 100 parts of MDI having an average functionality of about 2.0 to 2.2 with from about 40 to 65 parts by weight of an ethylene oxide-capped polypropylene polyol with a B side mixture comprising: (b) from about 4 to 8 parts by weight of a tetraethylene glycol; (c) about 90 to 120 parts by weight of the ethylene oxide-capped polypropylene glycol polyol employed to prepare the prepolymer: (d) the reaction carried out in the presence of about 0.5 to 5 parts by weight of water as a blowing agent, a catalytic amount of a co-catalyst comprising a diamine catalyst in combination and a tetravalent organo tin catalyst, a cell control amount of a silicone agent, and from about 2 to 12 parts by weight of MDI of a phosphate as a flame-retardant agent.
Claim 22
Dependent Claim
178 words
A flexible open cell polyurethane foam composition characterized by high tensile or tear strength and improved flame retardancy, which foam composition is prepared by reacting: (a) an A side composition comprising 100 parts by weight of an MDI-polyol prepolymer, which prepolymer is prepared by reacting 100 parts of MDI having an average functionality of about 2.0 to 2.2 with from about 40 to 65 parts by weight of an ethylene oxide-capped polypropylene polyol with a B side mixture comprising: (b) from about 4 to 8 parts by weight of a tetraethylene glycol; (c) about 90 to 120 parts by weight of the ethylene oxide-capped polypropylene glycol polyol employed to prepare the prepolymer: (d) the reaction carried out in the presence of about 0.5 to 5 parts by weight of water as a blowing agent, a catalytic amount of a co-catalyst comprising a diamine catalyst in combination and a tetravalent organo tin catalyst, a cell control amount of a silicone agent, and from about 2 to 12 parts by weight of MDI of a phosphate as a flame-retardant agent.
Claim 23
Dependent Claim
95 words
An MDI-polyol prepolymer suitable for use in preparing a flexible polyurethane foam composition, which MDI prepolymer is prepared by admixing and reacting together 100 parts by weight of an MDI having an average functionality of about 2.4 or less with from about 35 to 75 parts by weight of an ethylene oxide-capped polypropylene polyol, the reaction carried out by admixing the MDI and the ethylene oxide-capped polyol and heating the reaction mixture to a temperature of 100° F. or more for a period of time sufficient to carry out the reaction to form the prepolymer.
Claim 24
Dependent Claim
95 words
An MDI-polyol prepolymer suitable for use in preparing a flexible polyurethane foam composition, which MDI prepolymer is prepared by admixing and reacting together 100 parts by weight of an MDI having an average functionality of about 2.4 or less with from about 35 to 75 parts by weight of an ethylene oxide-capped polypropylene polyol, the reaction carried out by admixing the MDI and the ethylene oxide-capped polyol and heating the reaction mixture to a temperature of 100° F. or more for a period of time sufficient to carry out the reaction to form the prepolymer.
Claim 25
Dependent Claim
35 words
The prepolymer of claim 21 wherein the MDI has an average functionality of from about 2.0 to 2.2 and wherein the ethylene oxide-capped polypropylene polyol has a hydroxyl number ranging from about 25 to 50.
Claim 26
Dependent Claim
19 words
The prepolymer of claim 20 wherein the MDI-prepolymer has a free NCO content of about 12 to 18 percent.
References Cited (Backward Citations)
US3336242A
Cited
US3385807A
Cited
US4301110A
Cited
US4393015A
Cited
US4365025A
Cited
US4436841A
Cited
US4452829A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-06-24 | 1988-12-24 | 1989-06-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-06-24 | 1992-12-24 | 1993-06-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-06-24 | 1996-12-24 | 1997-06-25 | $7700.00 | Window Closed / Lapsed |