US4525374A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Treating hydrophobic filters to render them hydrophilic
Assignee: Manresa Inc
•
Filing: 1984-02-27
•
Granted: 1985-06-25
•
Expires: 2004-02-27
Abstract
Abstract A method is described for coating a hydrophobic filter membrane so as to render said membrane hydrophilic. This method is particularly for treating polypropylene or polytetrafluoroethylene in which the filter membrane is contemplated to have a pore size not larger than two (2) microns. The treating solution has Triethanolamine Dodecylbenzene Sulfonate (LAS) as the active ingredient. This treatment may use heated air (125° to 200° F.) as a drying assist which renders the membrane to have a substantially instantaneous "wet-out".
Inventors
- 👤 Vincent L. Vaillancourt
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 14:10
CPC Classifications
B; B01; B01D; B01D67/00; B01D67/0081; B01D67/0088; Y; Y10; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249953; Y10T428/249978; Y10T428/249979
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
52 words
A method of coating a hydrophilic filter membrane to render said membrane hydrophilic, said method including the steps of coating a polypropylene membrane whose pore size is not larger than two (2) microns with a Triethanolamine Dodecylbenzene Sulfonate (LAS) chemical solution so that said polypropylene membrane is rendered hydrophilic and medically acceptable.
Claim 2
Independent Claim
52 words
A method of coating a hydrophilic filter membrane to render said membrane hydrophilic, said method including the steps of coating a polypropylene membrane whose pore size is not larger than two (2) microns with a Triethanolamine Dodecylbenzene Sulfonate (LAS) chemical solution so that said polypropylene membrane is rendered hydrophilic and medically acceptable.
Claim 3
Dependent Claim
38 words
A method of coating a polypropylene membrane, as in claim 1, in which the dry coated weight of the deposited LAS is greater than one-tenth (0.1) milligrams and less than one and one-half (1.5) milligrams per square centimeter.
Claim 4
Dependent Claim
63 words
A method of coating a polypropylene membrane, as in claim 2, in which the applied treating solution is accelerated in its drying on the filter membrane by heating and moving air over the coated membrane, with said air heated from a low of about one hundred twenty-five degrees Fahrenheit (125° F.) to a higher temperature which is short of distorting said filter membrane.
Claim 5
Independent Claim
52 words
A method of coating a hydrophobic filter membrane to render said membrane hydrophilic, said method including the steps of coating a polytetrafluoroethylene membrane whose pore size is not larger than two (2) microns with a Triethanolamine Dodecylbenzene Sulfonate (LAS) chemical solution so that said polytetrafluoroethylene membrane is rendered hydrophilic and medically acceptable.
Claim 6
Independent Claim
52 words
A method of coating a hydrophobic filter membrane to render said membrane hydrophilic, said method including the steps of coating a polytetrafluoroethylene membrane whose pore size is not larger than two (2) microns with a Triethanolamine Dodecylbenzene Sulfonate (LAS) chemical solution so that said polytetrafluoroethylene membrane is rendered hydrophilic and medically acceptable.
Claim 7
Dependent Claim
38 words
A method of coating a polytetrafluorethylene membrane, as in claim 4, in which the dry coated weight of the deposited LAS is greater than one-tenth (0.1) milligrams and less than one and one-half (1.5) milligrams per square centimeter.
Claim 8
Dependent Claim
63 words
A method of coating a polytetrafluoroethylene membrane, as in claim 5, in which the applied treating solution is accelerated in its drying on the filter membrane by heating and moving air over the coated membrane, with said air heated from a low of about one hundred twenty-five degrees Fahrenheit (125° F.) to a higher temperature which is short of distorting said filter membrane.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-06-24 | 1988-12-24 | 1989-06-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-06-24 | 1992-12-24 | 1993-06-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-06-24 | 1996-12-24 | 1997-06-25 | $7700.00 | Window Closed / Lapsed |