Abstract
Abstract The invention relates to a process for preparing flat articles which are moulded in any desired shaped in dry moulds from defibrated components of wood. In this process, the moisture required to give good felting remains a constituent of the wood fibres until the moulding stage. These wood fibres are mixed with fibre- and/or moisture-reactive binders and, if appropriate, auxiliaries, are metered by means of a gravity-compensating air stream onto a preform sieve, and are then compression-moulded without a cooling cycle in sieve-free moulds between two surfaces which are smooth or embossed in any desired pattern.
Inventors
- 👤 Heinz Tonniges
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 22:25
CPC Classifications
B; B27; B27N; B27N5/00
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
117 words
In a process for manufacturing a three-dimensional article by compression-moulding under dry conditions into any desired shape where the walls are thin relative their area and which are based on defibrated wood fibres to which binders have been added and which have a moisture content of 1 to 30% by weight relative to all components of an article, the improvement wherein a proportioned amount of the moulding material disposed in an air stream is brought in contact with the bottom side of a preform sieve and a vacuum is applied from above said sieve whereby to form a fibre containing preform, and the thus preformed product is then compression-moulded into the desired final shape of the article.
Claim 2
Dependent Claim
117 words
In a process for manufacturing a three-dimensional article by compression-moulding under dry conditions into any desired shape where the walls are thin relative their area and which are based on defibrated wood fibres to which binders have been added and which have a moisture content of 1 to 30% by weight relative to all components of an article, the improvement wherein a proportioned amount of the moulding material disposed in an air stream is brought in contact with the bottom side of a preform sieve and a vacuum is applied from above said sieve whereby to form a fibre containing preform, and the thus preformed product is then compression-moulded into the desired final shape of the article.
Claim 3
Dependent Claim
19 words
Process according to claim 1, wherein in that a material containing a reactive polyfunctional isocyanate is admixed as binder.
Claim 4
Dependent Claim
39 words
Process according to claim 1, wherein in that the moisture content of the wood fibres is set to such a value that on removal from the airstream it is 10 to 24% relative to all components of an article.
Claim 5
Dependent Claim
9 words
Product manufactured by the process according to claim 1.
Claim 6
Dependent Claim
11 words
A process according to claim 1, wherein said surfaces are smooth.
Claim 7
Dependent Claim
19 words
A process according to claim 1, wherein at least one of said surfaces is embossed with a desired pattern.
Claim 8
Dependent Claim
41 words
A process according to claim 1 wherein the moulding composition contains an agent selected from the group consisting of flame-retarding agents, water repellents, lubricants, antistats, colorants, mould-release agents, blowing agents, corrosion inhibitors, pourability-preserving agents, reinforcing agents, active fillers and inert fillers.
Claim 9
Dependent Claim
15 words
A process according to claim 1 wherein the preform product is compression-moulded between two surfaces.
Claim 10
Dependent Claim
16 words
A process according to claim 8 wherein the preform product is compression-moulded in a sieve-free mould.
Claim 11
Dependent Claim
11 words
A process according to claim 1 wherein said sieve is contoured.
Claim 12
Dependent Claim
13 words
A process according to claim 10 wherein said sieve has a convex contour.
Claim 13
Dependent Claim
13 words
A process according to claim 10 wherein said sieve has a concave contour.
Claim 14
Dependent Claim
29 words
A process according to claim 10 wherein said moulding material is deposited onto said preform sieve to form a preform whose thickness is 1.0 mm to about 350 mm.
Claim 15
Dependent Claim
34 words
A process according to claim 10 wherein said moulding material is disposed on said preform sieve so as to form a preform whose density is 10 kg/m 3 to about 150 kg/m 3 .
Claim 16
Dependent Claim
34 words
A process according to claim 11 wherein said moulding material is disposed on said preform sieve so as to form a preform whose density is 10 kg/m 3 to about 150 kg/m 3 .
Claim 17
Dependent Claim
34 words
A process according to claim 12 wherein said moulding material is disposed on said preform sieve so as to form a preform whose density is 10 kg/m 3 to about 150 kg/m 3 .
Claim 18
Dependent Claim
71 words
A process according to claim 10 wherein said moulding material consists essentially of said fibres, up to 10% by weight water repellant, up to 10% by weight of dyestuff or colored pigment, up to 2% by weight of a reaction accelerator, up to 40% by weight of a fire-retardant, up to 10% by weight of a mould-release agent or lubricant and up to 18% by weight of a polyurethane curing agent.
References Cited (Backward Citations)
US4257995A
Cited
US4375448A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-06-24 | 1988-12-24 | 1989-06-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-06-24 | 1992-12-24 | 1993-06-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-06-24 | 1996-12-24 | 1997-06-25 | $7700.00 | Window Closed / Lapsed |