US4524036A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for the manufacture of polyurethane resin for electrostatic spinning
Assignee: University of Liverpool
•
Filing: 1984-04-09
•
Granted: 1985-06-18
•
Expires: 2004-04-09
Abstract
Abstract A process for the preparation of polyurethane resins particularly suitable for electrostatic spinning which comprises forming a prepolymer of polyether glycol and a diisocyanate reacted in a molar ratio of about 1:2, and thereafter reacting the prepolymer with additional diisocyanate and a diol extender, the final molar ratio of the polyether, isocyanate and diol reactants being approximately 1:3.7:2.5. The reaction is conducted in an organic solvent at a temperature of about 45° C. to obtain a polymer having an inherent viscosity of from about 2.0 to 2.4 in a solution of 25 to 30 percent solids. The solution is diluted to about 15 percent solids prior to spinning.
Inventors
- 👤 Denis K. Gilding
- 👤 Roy M. Clarke
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 22:21
CPC Classifications
D; D01; D01F; D01F6/00; D01F6/58; D01F6/70; C; C08; C08G; C08G18/00; C08G18/06; C08G18/08; C08G18/0838; C08G18/0842; C08G18/0847; C08G18/0852; C08G18/10; D01D; D01D5/00; D01D5/0007; D01D5/0015; D01D5/003; D01D5/0038; D04; D04H; D04H1/00; D04H1/40; D04H1/54; D04H1/56
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
182 words
In a process of electrostatic spinning of urethane polymers to form fine diameter fibers wherein a solution of a urethane polymer is introduced into an electrostatic field in the form of droplets which are attenauated into fibers while being drawn to an electrode where the fibers are collected, the improvement which comprises using as the said urethane polymer a polyurethane resin produced by a process which comprises the steps of: a. reacting in a volatile organic solvent a polyalkylene ether glycol and an organic diisocyanate in a molar ratio of about 1:2 to form a prepolymer; b. reacting said prepolymer with additional organic diisocyanate and an alkanediol extender in a volatile organic solvent to form a polyurethane resin, the final molar ratios of the polyalkylene ether glycol, organic diisocyanate, and alkanediol being about 1:3.7:2.5; c. continuing said reaction with incremental additions of volatile organic solvent until a 25 to 30 percent by weight solids solution of said polyurethane resin having an inherent viscosity of from about 2.0 to 2.4 is obtained; and d. terminating said reaction by the addition of an alcohol.
Claim 2
Dependent Claim
182 words
In a process of electrostatic spinning of urethane polymers to form fine diameter fibers wherein a solution of a urethane polymer is introduced into an electrostatic field in the form of droplets which are attenauated into fibers while being drawn to an electrode where the fibers are collected, the improvement which comprises using as the said urethane polymer a polyurethane resin produced by a process which comprises the steps of: a. reacting in a volatile organic solvent a polyalkylene ether glycol and an organic diisocyanate in a molar ratio of about 1:2 to form a prepolymer; b. reacting said prepolymer with additional organic diisocyanate and an alkanediol extender in a volatile organic solvent to form a polyurethane resin, the final molar ratios of the polyalkylene ether glycol, organic diisocyanate, and alkanediol being about 1:3.7:2.5; c. continuing said reaction with incremental additions of volatile organic solvent until a 25 to 30 percent by weight solids solution of said polyurethane resin having an inherent viscosity of from about 2.0 to 2.4 is obtained; and d. terminating said reaction by the addition of an alcohol.
Claim 3
Dependent Claim
13 words
A process of claim 1 wherein said reactions are conducted at 45° C.±2°.
Claim 4
Dependent Claim
14 words
A process of claim 1 wherein said polyalkylene ether glycol is polytetramethylene ether glycol.
Claim 5
Dependent Claim
12 words
A process of claim 1 wherein said organic diisocyanate is diphenylmethane diisocyanate.
Claim 6
Dependent Claim
12 words
A process of claim 1 wherein said alkanediol extender is 1,4-butane diol.
Claim 7
Dependent Claim
12 words
A process of claim 1 wherein said volatile organic solvent is dimethylformamide.
Claim 8
Dependent Claim
34 words
The process of claim 1 wherein said organic diisocyanate is present in an amount of from about 90% to not more than 105% of said molar ratio of 1:2 during formation of the prepolymer.
Claim 9
Dependent Claim
26 words
The process of claim 1 wherein said reaction of polyalkylene ether glycol and organic diisocyanate is conducted in a solution of about 75 weight percent solids.
Claim 10
Dependent Claim
22 words
The process of claim 1 wherein said reaction of said prepolymer is initially in a solution of about 50 weight percent solids.
Claim 11
Dependent Claim
53 words
The process of claim wherein the incremental addition of solvent during the continuation of the reaction is effective to maintain the viscosity of the solution below about 500 poise until the solids level is reduced to 25 to 30 percent by weight and the reaction is allowed to go to the termination point.
Claim 12
Dependent Claim
205 words
In a process of electrostatic spinning of urethane polymers to form fine diameter fibers wherein a solution of a urethane polymer is introduced into an electrostatic field in the form of droplets which are attenuated into fibers while being drawn to an electrode where the fibers are collected, the improvement which comprises using as the said urethane polymer a polyurethane resin produced by a process which comprises the steps of: a. reacting in a first volatile organic solvent a polyalkylene ether glycol and an organic diisocyanate in a molar ratio of about 1:2 to form a prepolymer; b. reacting said prepolymer with additional organic diisocyanate and an alkanediol extender in said first volatile organic solvent to form a polyurethane resin, the final molar ratios of the polyalkylene ether glycol, organic diisocyanate, and alkanediol being about 1:3.7:2.5; c. continuing said reaction with incremental additions of said first volatile organic solvent until a 25 to 30 percent by weight solids solution of said polyurethane resin having an inherent viscosity of from about 2.0 to 2.4 is obtained; d. terminating said reaction by the addition of an alcohol; and e. diluting said polyurethane resin solution to about 15 percent by weight solids with a second volatile organic solvent.
Claim 13
Dependent Claim
205 words
In a process of electrostatic spinning of urethane polymers to form fine diameter fibers wherein a solution of a urethane polymer is introduced into an electrostatic field in the form of droplets which are attenuated into fibers while being drawn to an electrode where the fibers are collected, the improvement which comprises using as the said urethane polymer a polyurethane resin produced by a process which comprises the steps of: a. reacting in a first volatile organic solvent a polyalkylene ether glycol and an organic diisocyanate in a molar ratio of about 1:2 to form a prepolymer; b. reacting said prepolymer with additional organic diisocyanate and an alkanediol extender in said first volatile organic solvent to form a polyurethane resin, the final molar ratios of the polyalkylene ether glycol, organic diisocyanate, and alkanediol being about 1:3.7:2.5; c. continuing said reaction with incremental additions of said first volatile organic solvent until a 25 to 30 percent by weight solids solution of said polyurethane resin having an inherent viscosity of from about 2.0 to 2.4 is obtained; d. terminating said reaction by the addition of an alcohol; and e. diluting said polyurethane resin solution to about 15 percent by weight solids with a second volatile organic solvent.
Claim 14
Dependent Claim
12 words
A process of claim 11 wherein said reactions are conducted at 45°±2°.
Claim 15
Dependent Claim
14 words
A process of claim 11 wherein said polyalkylene ether glycol is polytetramethylene ether glycol.
Claim 16
Dependent Claim
12 words
A process of claim 11 wherein said organic diisocyanate is diphenylmethane diisocyanate.
Claim 17
Dependent Claim
12 words
A process of claim 11 wherein said alkanediol extender is 1,4-butane diol.
Claim 18
Dependent Claim
15 words
A process of claim 11 wherein said first and second volatile organic solvents are dimethylformamide.
Claim 19
Dependent Claim
23 words
A process of claim 11 wherein said first volatile organic solvent is dimethyl formamide and second volatile organic solvent is methyl ethyl ketone.
Claim 20
Dependent Claim
34 words
The process of claim 11 wherein said organic diisocyanate is present in an amount of from about 90% to not more than 105% of said molar ratio of 1:2 during formation of the prepolymer.
Claim 21
Dependent Claim
26 words
The process of claim 11 wherein said reaction of polyalkylene ether glycol and organic diisocyanate is conducted in a solution of about 75 weight percent solids.
Claim 22
Dependent Claim
22 words
The process of claim 11 wherein said reaction of said prepolymer is initially in a solution of about 50 weight percent solids.
Claim 23
Dependent Claim
54 words
The process of claim 20 wherein the incremental addition of solvent during the continuation of the reaction is effective to maintain the viscosity of the solution below about 500 poise until the solids level is reduced to 25 to 30 percent by weight and the reaction is allowed to go to the termination point.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-06-17 | 1988-12-17 | 1989-06-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-06-17 | 1992-12-17 | 1993-06-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-06-17 | 1996-12-17 | 1997-06-18 | $7700.00 | Window Closed / Lapsed |