Photostable yellow composite pigments and process for their preparation
Assignee: Montedison SpA
•
Filing: 1983-12-05
•
Granted: 1985-06-18
•
Expires: 2003-12-05
Abstract
Abstract There are described organic-inorganic ternary composite pigments consisting of 70%-90% by weight of an inorganic binary titanium dioxide/aluminum hydrate component and, from 10% to 30% by weight, of a co-precipitated organic component consisting of an organic dye, containing in its structure at least one carboxylic and/or sulphonic acid function, having the formula: <IMAGE> (I) wherein R1 is selected from the group consisting of NO2 -SO3H and -COOH; R2 is selected from the group consisting of NO2, -SO3H, alkyl and alkoxyl; R3 is selected from the group consisting of H, halogen and alkyl; R4 and R5 are each selected from the group consisting of H, halogen, alkyl and alkoxyl; R6 is selected from the group consisting of H, halogen and alkoxyl; and wherein the -COOH and/or -SO3H group of dye (I) is salified with metal cations. The pigments are obtained by co-precipitation acidifying an aqueous solution and/or dispersion of acid dye (I) in sodium aluminate, in the presence of TiO2, maintained at 40 DEG -80 DEG C. and at pH=9.5-10.5, by then treating it with any aqueous solution of an alkaline-earth (Ca, Ma, Al, Ba, Sr) salt or of Mn or Zn.
Inventors
- 👤 Camillo Paffoni
- 👤 Filippo M. Carlini
- 👤 Giorgio Bottaccio
- 👤 Alberto Osti
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 03:24
CPC Classifications
C; C09; C09B; C09B63/00; C09B67/00; C09B67/0033; C09B67/0041
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
155 words
Composite ternary organic-inorganic pigments consisting of 70 to 90% by weight of a binary inorganic component of titanium dioxide and aluminum hydrate and, 10% to 30% by weight of an organic co-precipitated component consisting of an organic azoic dye containing in its structure at least one carboxylic (--COOH) and/or sulphonic (--SO 3 H) acid function, of the formula: ##STR13## wherein R 1 is selected from the group consisting of NO 2 --SO 3 H and --COOH; R 2 is selected from the group consisting of NO 2 , --SO 3 H, alkyl and alkoxyl; R 3 is selected from the group consisting of H, halogen and alkyl; R 4 and R 5 are each selected from the group consisting of H, halogen, alkyl and alkoxyl; R 6 is selected from the group consisting of H, halogen and alkoxyl, and wherein the --COOH and/or --SO 3 H group of dye (I) is salified with metal cations.
Claim 2
Dependent Claim
155 words
Composite ternary organic-inorganic pigments consisting of 70 to 90% by weight of a binary inorganic component of titanium dioxide and aluminum hydrate and, 10% to 30% by weight of an organic co-precipitated component consisting of an organic azoic dye containing in its structure at least one carboxylic (--COOH) and/or sulphonic (--SO 3 H) acid function, of the formula: ##STR13## wherein R 1 is selected from the group consisting of NO 2 --SO 3 H and --COOH; R 2 is selected from the group consisting of NO 2 , --SO 3 H, alkyl and alkoxyl; R 3 is selected from the group consisting of H, halogen and alkyl; R 4 and R 5 are each selected from the group consisting of H, halogen, alkyl and alkoxyl; R 6 is selected from the group consisting of H, halogen and alkoxyl, and wherein the --COOH and/or --SO 3 H group of dye (I) is salified with metal cations.
Claim 3
Dependent Claim
61 words
Composite pigments according to claim 1, characterized in that the salified azoic dye is present in the pigment in quantities ranging from 10% to 25% by weight ratio, with respect to the titanium dioxide, comprised between 1:1 and 1:5 but preferably comprised betwen 1:2 and 1:4, and with a by weight ratio with respect to the aluminum hydrate, of maximum 1.
Claim 4
Dependent Claim
41 words
Composite pigments according to 1 and 2 characterized in that the metals of the cations with which the carboxylic and/or the sulphonic group of the dye are salified, are selected from the groups consisting of alkaline earth metals, Mn and Zn.
Claim 5
Dependent Claim
41 words
Composite pigments according to 1 and 2 characterized in that the metals of the cations with which the carboxylic and/or the sulphonic group of the dye are salified, are selected from the groups consisting of alkaline earth metals, Mn and Zn.
Claim 6
Dependent Claim
40 words
Composite ternary pigments according to claim 1, characterized in that the inorganic binary component consists of aluminum hydrate and titanium dioxide selected from the groups consisting of rutile TiO 2 , anatase TiO 2 and rutile anatase TiO 2 .
Claim 7
Dependent Claim
26 words
Composite ternary pigments according to claim 4, characterized in that as a TiO 2 source there are used inorganic colored pigments based on TiO 2 .
Claim 8
Dependent Claim
34 words
Composite ternary pigments according to claim 1, characterized in that they have a specific surface comprised between about 20 and 100 m 2 /g and preferably comprised between 40 and 60 m 2 /g.
Claim 9
Dependent Claim
124 words
Process for the preparation of composite ternary pigments as defined in claim 1 characterized in that an organic azoic dye of formula (I), as defined in claim 1, is made to co-precipitate by acidification, wthin a time interval of between about 2 and 4 hours, starting from one of its aqueous solutions and/or dispersions with sodium aluminate, under controlled pH conditions comprised between 9.5 and 10.5, in the presence of titanium dioxide at a temperature comprised between about 40° and about 80° C., by then treating said dye with an aqueous solution of a salt of a metal selected from the group consisting of alkaline earth metal Mn and Zn, brought down to a pH value comprised between 6.6 and 7.5 and then separated.
Claim 10
Dependent Claim
129 words
Process according to claim 7, characterized in that a solution and/or suspension of the organic said dye (I) in an aqueous medium having a pH>10.5 by the presence of NaAlO 2 , after the introduction of the TiO 2 , is gradually brought up in an interval of time comprised between 0.5 and about 2 hours, to a pH comprised between 9.5 adn 10.5 and then, after the introduction of a salt of a metal selected from the group consisting of alkaline-earth metals and Mn and Zn, in quantities substantially superior to the stoichiometric quantity with respect to the acid dye, is brought down to a pH comprised between 6.5 and 7.5, by the addition of a mineral acid at a temperature comprised between about 40° and 80° C.
Claim 11
Dependent Claim
25 words
Process according to claim 7 or 8, characterized in that the titanium dioxide is selected from the group consisting of TiO 2 based colored pigments.
Claim 12
Dependent Claim
23 words
Process according to claim 7 or 8, characterized in that the sodium aluminate is used in association with minor quantities of sodium hydrate.
Claim 13
Dependent Claim
22 words
Process according to claim 7 or 8, characterized in that the co-precipitation temperature is preferably comprised between about 40° and 60° C.
Claim 14
Dependent Claim
32 words
Process according to claim 7 or 8, characterized in that the co-precipitation of the organic dye in aqueous soution and/or dispersion with sodium aluminate, is carried using HCl as a mineral acid.
Claim 15
Dependent Claim
29 words
Process according to claim 7 or 8, characterized in that the alkaline earth metal salt is selected from the group consisting of Ca, Mg, Al, Ba and Sr salts.
Claim 16
Dependent Claim
46 words
Process according to claim 7 or 8 characterized in that the alkaline earth metal salt or Mn or Zn is added in at least stoichiometric quantities with respect to the acid dye used, and preferably on the basis of a quantity 2 to 4 times greater.
Claim 17
Dependent Claim
21 words
A process for the coloring of plastic materials characterized in that a composite ternary pigment according to claim 1 is used.
Claim 18
Dependent Claim
32 words
A process for preparing a lacquer, stoving and air dried enamels, inka or pastes for the beprinting of textiles characterized in that a composite ternary pigment according to claim 1 is used.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-06-17 | 1988-12-17 | 1989-06-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-06-17 | 1992-12-17 | 1993-06-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-06-17 | 1996-12-17 | 1997-06-18 | $7700.00 | Window Closed / Lapsed |