Abstract A chain extending agent for reaction injection molding (RIM) comprising a normally liquid blend of butanediol and a toluene diamine mono-substituted with an electron withdrawing group and having the formula ##STR1## wherein X is vicinal to an amino radical and is selected from the group of halogen, CN, NO 2 , acyl, carboxylate and isomeric mixtures thereof, and wherein the butanediol and diamine are combined in a critical mole ratio of from 4:1 to about 19:1. The above blend is particularly useful in the preparation of large moldings of polyurethane-polyurea elastomer by the RIM or RRIM (reinforced reaction injection molding) process wherein instant preformed blend is added to a mixture of polyol reactant and catalyst before polymerization in the mold with isocyanate to produce a urethane/urea polymer product of improved properties. Accordingly, the intention also concerns an enhanced RIM or RRIM process and improved product by the use of a mixture of the present chain extender blend and polyol reactant maintainable in the liquid state at ambient temperature.
A normally liquid polymer chain extender blend of butanediol and a mono-substituted toluene diamine mono-substituted with an electron-withdrawing group and having the formula ##STR4## wherein X is vicinal to an amino radical and is selected from the group of halo, CN, NO 2 , acyl, carboxylate and isomeric mixtures thereof, said blend having a mole ratio of from 4:1 to about 19:1 butanediol to said diamine.
Claim 2
Dependent Claim
66 words
A normally liquid polymer chain extender blend of butanediol and a mono-substituted toluene diamine mono-substituted with an electron-withdrawing group and having the formula ##STR4## wherein X is vicinal to an amino radical and is selected from the group of halo, CN, NO 2 , acyl, carboxylate and isomeric mixtures thereof, said blend having a mole ratio of from 4:1 to about 19:1 butanediol to said diamine.
Claim 3
Dependent Claim
17 words
The liquid blend of claim 1 wherein said mono-substituted toluene diamine is an isomeric mixture of monochlorotoluenediamine.
Claim 4
Dependent Claim
22 words
The liquid blend of claim 1 wherein the mole ratio of butanediol to said diamine is between about 6:1 and about 12:1.
Claim 5
Dependent Claim
42 words
A polyol reactant mixture suitable for use in the manufacture of polyurethane-polyurea products of manufacture by a RIM process which comprises a polyol reactant and the chain extender of claim 1 combined in a mole ratio between about 0.01:1 and about 0.9:1.
Claim 6
Dependent Claim
44 words
The reaction mixture of a RIM process for the preparation of polyurethane-polyurea elastomer product of manufacture which comprises a reactive polyol, a coreacting isocyanate and the chain extender blend of claim 1 wherein said blend is at least 5% by weight of said mixture.