Corrosion resistant coating
Assignee: National Aeronautics and Space Administration
•
Filing: 1983-09-30
•
Granted: 1985-06-11
•
Expires: 2003-09-30
Abstract
Abstract Disclosed is a method of coating a substrate with an amorphous metal comprising the step of bombarding a solid piece of the metal with ions of an inert gas in the presence of a magnetic field to provide a vapor of the metal which is deposited on the substrate at a sufficiently low gas pressure so that there is formed on the substrate a thin, uniformly thick, essentially pinhole-free film of the metal.
Inventors
- 👤 Satish K. Khanna
- 👤 Anilkumar P. Thakoor
- 👤 Roger M. Williams
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 13:43
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/06; C23C14/14
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
115 words
A method of providing a substrate with a thin, corrosion-resistant coating comprising the steps of: (a) selecting one or more transition metals; (b) selecting one or more metalloids; (c) thoroughly mixing said metals and metalloids to form a solid material in the shape of a target suitable for deposition sputtering; (d) bombarding the target with ions of an inert gas in the presence of a magnetic field to provide a vapor of the target material and deposit the vaporous target material onto the substrate; and (e) maintaining the pressure of the gas sufficiently low to cause the target material to deposit onto the substrate in a thin, uniformly thick, essentially pinhole-free amorphous metallic alloy film.
Claim 2
Independent Claim
115 words
A method of providing a substrate with a thin, corrosion-resistant coating comprising the steps of: (a) selecting one or more transition metals; (b) selecting one or more metalloids; (c) thoroughly mixing said metals and metalloids to form a solid material in the shape of a target suitable for deposition sputtering; (d) bombarding the target with ions of an inert gas in the presence of a magnetic field to provide a vapor of the target material and deposit the vaporous target material onto the substrate; and (e) maintaining the pressure of the gas sufficiently low to cause the target material to deposit onto the substrate in a thin, uniformly thick, essentially pinhole-free amorphous metallic alloy film.
Claim 3
Dependent Claim
54 words
The method of claim 1 wherein the metal is selected from the group scandium, yttrium, lanthanum, titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, tungsten, manganese, technetium, rhenium, iron, ruthenium, osmium, cobalt, rhodium, iridium, nickel, palladium and platinum and the metalloids are selected from the group consisting of silicon, boron, carbon, germanium and phosphorus.
Claim 4
Dependent Claim
18 words
The method of claim 1 wherein the gas pressure is no greater than about 10 micrometers of mercury.
Claim 5
Dependent Claim
36 words
The method of claim 1 wherein the target material is (Mo 0 .6 Ru 0 .4) 82 B 18 ; (Mo) 82 B 18 ; or (W 0 .6 Re 0 .4) 76 B 24 .
Claim 6
Dependent Claim
14 words
The method of claim 1 wherein the substrate is glass, plastic ceramic, or metal.
Claim 7
Dependent Claim
19 words
The method of claim 1 wherein the bombarding is conducted in an electric field which ionizes the inert gas.
Claim 8
Dependent Claim
25 words
The method of claim 6 wherein the electric field is established between an anode and a cathode, with the target being positioned adjacent the anode.
Claim 9
Dependent Claim
16 words
The method of claim 1 wherein the substrate is cleaned prior to applying the thin film.
Claim 10
Dependent Claim
21 words
The method of claim 1 wherein the metal piece is cleaned by bombarding the substrate with ions of the inert gas.
Claim 11
Independent Claim
163 words
A method of coating a substrate with a corrosion-resistant coating comprising the steps of: (a) selection one or more transition metals from the group consisting of scandium, yttrium, lanthanum, titanium, zirconium, hafnium, vanadium niobium, tantalum, chromium, molybdenum, tungsten manganese, technetium, rhenium, iron, ruthenium, osmium, cobalt, rhodium, iridium, nickel, palladium and platinum; (b) selection one or more metalloids from the groups consisting of silicon, boron, carbon, germanium and phosphorus; (c) mixing the selected transition metals and metalloids together; (d) pressing the mixture of selected metals and metalloids into a solid shape in the form of a target; (e) surrounding the target and substrate with an inert gas having a pressure no greater than about 10 micrometers of mercury; and (f) bombarding the target with ions of the inert gas in the presence of a magnetic field to provide a vapor of the target material and deposit the vaporous target material onto the substrate in a thin, uniformly thick, essentially pinholefree amorphous metallic alloy film.
Claim 12
Independent Claim
163 words
A method of coating a substrate with a corrosion-resistant coating comprising the steps of: (a) selection one or more transition metals from the group consisting of scandium, yttrium, lanthanum, titanium, zirconium, hafnium, vanadium niobium, tantalum, chromium, molybdenum, tungsten manganese, technetium, rhenium, iron, ruthenium, osmium, cobalt, rhodium, iridium, nickel, palladium and platinum; (b) selection one or more metalloids from the groups consisting of silicon, boron, carbon, germanium and phosphorus; (c) mixing the selected transition metals and metalloids together; (d) pressing the mixture of selected metals and metalloids into a solid shape in the form of a target; (e) surrounding the target and substrate with an inert gas having a pressure no greater than about 10 micrometers of mercury; and (f) bombarding the target with ions of the inert gas in the presence of a magnetic field to provide a vapor of the target material and deposit the vaporous target material onto the substrate in a thin, uniformly thick, essentially pinholefree amorphous metallic alloy film.
Claim 13
Dependent Claim
37 words
The method of claim 10 wherein the target material is one of (Mo 0 .6 Ru 0 .4) 82 B 18 ; (Mo) 82 B 13 and (W 0 .6 Re 0 .4) 76 B 24 .
Claim 14
Dependent Claim
22 words
The method of claim 10 wherein the target is bombarded with ions until the coating is about 2 to 4 micrometers thick.
Claim 15
Dependent Claim
27 words
The method of claim 10 wherein the inert gas is argon and the pressure of said gas is maintained at about 5 to 10 micrometers of mercury.
References Cited (Backward Citations)
US4094764A
Cited
US4108751A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-06-10 | 1988-12-10 | 1989-06-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-06-10 | 1992-12-10 | 1993-06-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-06-10 | 1996-12-10 | 1997-06-11 | $7700.00 | Window Closed / Lapsed |