US4522652A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Machine base and process for manufacture thereof
Assignee: Dynamit Nobel AG
•
Filing: 1983-08-05
•
Granted: 1985-06-11
•
Expires: 2003-08-05
Abstract
Abstract A support or base for low-vibration mounting of machines or the like is made by hardening a molding material in a mold. The base contains a hardened inorganic material with a density of 2.2 to 3.0, particularly 2.5 to 2.7 g/cm 3 , is made from (a) 15 to 30 weight % of an aqueous 30 to 65% potassium hydroxide-potassium silicate solution in which the SiO 2 :K 2 O molar ratio is 1.0 to 2.0:1; (b) 15 to 35 weight % of an oxide mixture containing amorphous SiO 2 and aluminum oxide and/or hydrated amorphous silicic acid in the dispersed powder form and/or metakaolin; (c) 45 to 65 weight % of inorganic particulate fillers. The potassium silicate solution can be made by dissolving hydrated amorphous silicic acid in potassium hydroxide or its aqueous solution, and in this case, component (b) can consist entirely or partially of metakaolin.
Inventors
- 👤 Karl-Heinz Neuschaffer
- 👤 Hans-Werner Engels
- 👤 Hans-Jurgen Gebert
- 👤 Robert W. Laube
- 👤 Gunter Zoche
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 12:53
CPC Classifications
E; E02; E02D; E02D27/00; E02D27/32; E02D27/44; C; C04; C04B; C04B12/00; C04B12/04
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
132 words
A molded support structure for low-vibration mounting of machines or the like devices which exhibits a compressive strength of at least 60 N/mm 2 and a hardness according to the Mohs scale of 6 to 9 and which comprises a molded structure made by hardening a molding material in a mold to provide a hardened inorganic molding material with a density of 2.2 to 3.0 g/cm 3 , said molding material containing 15 to 30 weight % of an aqueous 30-65% potassium hydroxide-potassium silicate solution with an SiO 2 :K 2 O molar ratio of 1.0-2.0:1, 15-35 weight % of an oxide mixture containing amorphous SiO 2 and aluminum oxide and/or of hydrated amorphous silicic acid in the dispersed powder form and/or metakaolin; and 45 to 65 weight % inorganic particulate filler.
Claim 2
Dependent Claim
132 words
A molded support structure for low-vibration mounting of machines or the like devices which exhibits a compressive strength of at least 60 N/mm 2 and a hardness according to the Mohs scale of 6 to 9 and which comprises a molded structure made by hardening a molding material in a mold to provide a hardened inorganic molding material with a density of 2.2 to 3.0 g/cm 3 , said molding material containing 15 to 30 weight % of an aqueous 30-65% potassium hydroxide-potassium silicate solution with an SiO 2 :K 2 O molar ratio of 1.0-2.0:1, 15-35 weight % of an oxide mixture containing amorphous SiO 2 and aluminum oxide and/or of hydrated amorphous silicic acid in the dispersed powder form and/or metakaolin; and 45 to 65 weight % inorganic particulate filler.
Claim 3
Dependent Claim
111 words
A molded support structure according to claim 1, wherein said hardened inorganic molding material with a density of 2.2 to 3.0, made from a molding material containing 15-30 weight % of an aqueous 30-65% potassium hydroxide-potassium silicate solution with an SiO 2 :K 2 O molar ratio of 1.0-2.0:1, wherein the potassium hydroxide-potassium silicate solution is made by dissolving hydrated amorphous silicic acid in a dispersed powder form in potassium hydroxide or an aqueous solution thereof; 15-35 weight % of metakaolin and/or an oxide mixture containing amorphous SiO 2 and aluminum oxide and/or hydrated amorphous silicic acid in the dispersed powder form and 45-65 weight % of at least one filler.
Claim 4
Dependent Claim
60 words
A molded support structure according to claim 1, wherein said hardened inorganic molding material with a density of 2.2 to 3.0 g/cm 3 is made from 20-30 weight % of an aqueous 30-65% potassium hydroxide-potassium silicate solution with an SiO 2 :K 2 O molar ratio of 1.3-1.55:1, 15-25 weight % of metakaolin, and 45-65 weight % of inorganic fillers.
Claim 5
Dependent Claim
33 words
A molded support structure according to claim 1, wherein said filler comprises aluminum oxide, heavy spar, zirconium sand, mica, bauxite smelting tailings, ground basalt, quartz, feldspar, quarried granite, lead compounds, or mixtures thereof.
Claim 6
Dependent Claim
75 words
A molded support structure according to claim 3, wherein said molding material contains 22-27 weight % of an aqueous 30-65% potassium hydroxide-potassium silicate solution, in which the SiO 2 :K 2 O molar ratio is 1.3-1.55:1; 18-23 weight % metakaolin; 10-25 weight % aluminum oxide in the form of corundum; 10-15 weight % heavy spar; 10-15 weight % zirconium sand; 10-15 weight % bauxite tailings; and 0-10 weight % mica, ground slate or ground quartz.
Claim 7
Dependent Claim
25 words
A molded support structure according to claim 1, wherein reinforcements made of metal, wire inserts or steel mesh are embedded within the hardened molding materials.
Claim 8
Dependent Claim
141 words
A process for making a molded support structure which comprises preparing a solids mixture from an oxide mixture containing amorphous SiO 2 and aluminum oxide and/or a hydrated amorphous silicic acid in dispersed powder form and/or metakaolin and inorganic particulate filler, then admixing an aqueous 30-65% potassium hydroxide-potassium silicate solution with the solids mixture during cooling to temperatures below 30° C., then placing the resulting admixture in a mold, and hardening the admixture at a temperature below 100° C.; said admixture containing 15-30 weight % of the aqueous 30-65% potassium hydroxide-potassium silicate solution with an SiO 2 :K 2 O molar ratio of 1.0-2.0:1, 15-35 weight % of the oxide mixture containing amorphous SiO 2 and aluminum oxide and/or of the hydrated amorphous silicic acid in the dispersed powder form and/or metakaolin, and 45-65 weight % of the inorganic particulate filler.
Claim 9
Dependent Claim
141 words
A process for making a molded support structure which comprises preparing a solids mixture from an oxide mixture containing amorphous SiO 2 and aluminum oxide and/or a hydrated amorphous silicic acid in dispersed powder form and/or metakaolin and inorganic particulate filler, then admixing an aqueous 30-65% potassium hydroxide-potassium silicate solution with the solids mixture during cooling to temperatures below 30° C., then placing the resulting admixture in a mold, and hardening the admixture at a temperature below 100° C.; said admixture containing 15-30 weight % of the aqueous 30-65% potassium hydroxide-potassium silicate solution with an SiO 2 :K 2 O molar ratio of 1.0-2.0:1, 15-35 weight % of the oxide mixture containing amorphous SiO 2 and aluminum oxide and/or of the hydrated amorphous silicic acid in the dispersed powder form and/or metakaolin, and 45-65 weight % of the inorganic particulate filler.
Claim 10
Dependent Claim
23 words
A process according to claim 7, wherein the admixture is deaerated before it is placed in the mold, or while in the mold.
Claim 11
Dependent Claim
40 words
A molded support structure according to claim 1, wherein said oxide mixture contains 70 to 95 weight % of amorphous SiO 2 and Al 2 O 3 and 30 to 5 weight % of different metal oxides and alkaline oxides.
Claim 12
Dependent Claim
34 words
A molded support structure according to claim 1, wherein said oxide mixture comprises 7 to 75 weight % of amorphous SiO 2 and 12 to 87 weight % of Al 2 O 3 .
Claim 13
Dependent Claim
34 words
A molded support structure according to claim 9, wherein said oxide mixture comprises 7 to 75 weight % of amorphous SiO 2 and 12 to 87 weight % of Al 2 O 3 .
Claim 14
Dependent Claim
111 words
A molded support structure for low-vibration mounting of machines or like devices which exhibits a compressive strength of at least 60 N/mm 2 and a hardness according to the Mohs scale of 6 to 9 and which comprises a molded structure made by hardening a molding material in a mold to provide a hardened inorganic molding material with a density of 2.2 to 3.0 g/cm 3 , said molding material containing 15 to 39 weight % of an aqueous 30-65% potassium hydroxide-potassium silicate solution with an SiO 2 :K 2 O molar ratio of 1.0-2.0:1, 15-35 weight % of an oxide mixture containing amorphous SiO 2 and aluminum oxide and/or metakaolin.
Claim 15
Dependent Claim
111 words
A molded support structure for low-vibration mounting of machines or like devices which exhibits a compressive strength of at least 60 N/mm 2 and a hardness according to the Mohs scale of 6 to 9 and which comprises a molded structure made by hardening a molding material in a mold to provide a hardened inorganic molding material with a density of 2.2 to 3.0 g/cm 3 , said molding material containing 15 to 39 weight % of an aqueous 30-65% potassium hydroxide-potassium silicate solution with an SiO 2 :K 2 O molar ratio of 1.0-2.0:1, 15-35 weight % of an oxide mixture containing amorphous SiO 2 and aluminum oxide and/or metakaolin.
Claim 16
Dependent Claim
41 words
A process according to claim 7, wherein the aqueous potassium hydroxide-potassium silicate solution is admixed with the solids mixture during cooling to temperatures below 25° C. and the resulting admixture is hardened at a temperature in the range of 60°-95° C.
References Cited (Backward Citations)
US2423231A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-06-10 | 1988-12-10 | 1989-06-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-06-10 | 1992-12-10 | 1993-06-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-06-10 | 1996-12-10 | 1997-06-11 | $7700.00 | Window Closed / Lapsed |