Method for making impact resistant molding compositions
Assignee: Roehm GmbH Darmstadt
•
Filing: 1984-08-06
•
Granted: 1985-06-04
•
Expires: 2004-08-06
Abstract
Abstract A method for making impact resistant molding compositions wherein a hard phase having a glass transition temperature above 25° C. and consisting principally of methyl methacrylate is polymerized at least partially in a first stage, following which the monomers of a rubbery phase whose polymers have a glass transition temperature below 25° C. are added in a second stage and the polymerization is carried to completion, polymerization of the hard phase in the first stage being performed in a presence of an oil soluble free radical initiator and of an organosulfur chain transfer agent having at least two thiol groups in the molecule, and polymerization of the monomers of the rubbery phase in the second stage being carried out with graft crosslinkers in the presence of the previously formed hard phase.
Inventors
- 👤 Peter J. Arndt
- 👤 Walter Ludwig
- 👤 Manfred Munzer
- 👤 Werner Siol
- 👤 Franz Wenzel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 15:23
CPC Classifications
C; C08; C08F; C08F265/00; C08F265/04; Y; Y10; Y10S; Y10S525/00; Y10S525/902
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
197 words
A method for making an impact resistant molding composition, which method comprises polymerizing, in a first stage, a monomer mixture comprising from 70 to 100 percent by weight of methyl methacrylate, 0 to 30 percent by weight of an ester formed between acrylic acid and an aliphatic alcohol having from 1 to 8 carbon atoms and/or an ester formed between methacrylic acid with an alcohol having from 2 to 8 carbon atoms, and from 0 to 10 percent by weight of at least one further different vinyl monomer copolymerizable with the aforementioned comonomers, to form a hard phase polymer having a glass transition temperature above 25° C., the polymerization in said first stage being carried out in the presence of an oil soluble free radical initiator and of an organosulfur chain transfer agent having at least two thiol groups per molecule, and then in a second stage adding, to said hard phase polymer, monomers forming a rubbery phase and further polymerizing the mixture of monomers and polymer to completion in the presence of a graft crosslinking agent, the monomers of said rubbery phase being monomers the homopolymers of which have a glass transition temperature below 25° C.
Claim 2
Independent Claim
197 words
A method for making an impact resistant molding composition, which method comprises polymerizing, in a first stage, a monomer mixture comprising from 70 to 100 percent by weight of methyl methacrylate, 0 to 30 percent by weight of an ester formed between acrylic acid and an aliphatic alcohol having from 1 to 8 carbon atoms and/or an ester formed between methacrylic acid with an alcohol having from 2 to 8 carbon atoms, and from 0 to 10 percent by weight of at least one further different vinyl monomer copolymerizable with the aforementioned comonomers, to form a hard phase polymer having a glass transition temperature above 25° C., the polymerization in said first stage being carried out in the presence of an oil soluble free radical initiator and of an organosulfur chain transfer agent having at least two thiol groups per molecule, and then in a second stage adding, to said hard phase polymer, monomers forming a rubbery phase and further polymerizing the mixture of monomers and polymer to completion in the presence of a graft crosslinking agent, the monomers of said rubbery phase being monomers the homopolymers of which have a glass transition temperature below 25° C.
Claim 3
Dependent Claim
23 words
A method as in claim 1 wherein the polymerization of said first stage is performed in an aqueous medium as a bead polymerization.
Claim 4
Dependent Claim
22 words
A method as in claim 1 wherein the polymerizations of said first and second stages are both carried out as bead polymerizations.
Claim 5
Dependent Claim
30 words
A method as in claim 1 wherein the monomers of the rubbery phase are polymerized by a bead polymerization process within the hard phase polymer prepared in the first stage.
Claim 6
Dependent Claim
30 words
A method as in claim 1 wherein the monomers of the rubbery phase are polymerized in the second stage after dissolving the polymer of the hard phase in said monomers.
Claim 7
Dependent Claim
19 words
A method as in claim 1 wherein said organosulfur chain transfer agent has from 2 to 40 carbon atoms.
Claim 8
Dependent Claim
99 words
A method as in claim 1 wherein said organosulfur chain transfer agent has the formula HS--CH.sub.2 --A--CH.sub.2 --SH, wherein A is a hydrocarbon chain having from 3 to 16 carbon atoms in which one or more carbon atoms can be replaced by --S--, or is ##STR5## wherein n is 0 or an integer from 1 to 8 and Y is a hydrocarbon chain having from 2 to 16 carbon atoms or is such a chain which is substituted by ##STR6## wherein n' has the same meaning as n, and m is 0 or an integer from 1 to 8.
Claim 9
Dependent Claim
15 words
A method as in claim 1 wherein said organosulfur chain transfer agent is pentaerythritol tetrathioglycolate.
Claim 10
Dependent Claim
28 words
A method as in claim 1 wherein said organosulfur chain transfer agent is present in an amount from 0.05 to 5 percent by weight of the hard polymer.
Claim 11
Dependent Claim
24 words
A method as in claim 1 wherein said graft crosslinker is a monomer having at least two polymerizable groups of different reactivity per molecule.
Claim 12
Dependent Claim
28 words
A method as in claim 1 characterized in that said graft crosslinker is an allyl, methallyl, crotyl, or vinyl ester of an α,β-unsaturated monocarboxylic acid or dicarboxylic acid.
Claim 13
Dependent Claim
25 words
A method as in claim 12 wherein said graft crosslinker is an allyl, methallyl, crotyl, or vinyl ester of acrylic acid or of methacrylic acid.
Claim 14
Dependent Claim
20 words
A method as in claim 1 wherein said graft crosslinker is a monomer having at least three similar polymerizable groups.
Claim 15
Dependent Claim
18 words
A process as in claim 1 wherein said graft crosslinker contains at least three acrylic and/or methacrylic groups.
Claim 16
Dependent Claim
32 words
A method as in claim 1 wherein the amount of oil soluble free radical initiator employed is from 0.01 to 5 percent by weight of the monomers of the hard phase polymer.
Claim 17
Dependent Claim
27 words
A method as in claim 1 wherein addition of the monomers in said second stage is started at the earliest when the rate of polymerization is decelerating.
Claim 18
Dependent Claim
69 words
A method as in claim 1 wherein said monomers of the rubbery phase added in the second stage comprise 100 to 80 percent of at least one ester of acrylic acid with a C 1 -C 8 alcohol and from 0 to 20 percent, by weight of the monomers of the second stage, of at least one ester of acrylic acid with a C 1 to C 18 alcohol.
Claim 19
Dependent Claim
60 words
A method as in claim 1 wherein the refractive index of the rubbery phase is matched with the refractive index of the hard polymer phase by the copolymerization, in the rubbery phase, of a suitable amount of a monomer having an optical density greater than the optical density of the aliphate esters of acrylic acid and/or methacrylic acid used therein.
Claim 20
Dependent Claim
20 words
A method as in claim 18 wherein said monomer having higher optical density comprises an aromatic group in the molecule.
Claim 21
Dependent Claim
31 words
A method as in claim 1 wherein the ratio by weight of monomers in the hard polymer phase to the monomers polymerized in the rubbery phase is from 1:0.15 to 1:3.
Claim 22
Dependent Claim
24 words
A method as in claim 1 wherein no further free radical initiator is added for polymerization of the rubbery phase in the second stage.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-06-03 | 1988-12-03 | 1989-06-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-06-03 | 1992-12-03 | 1993-06-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-06-03 | 1996-12-03 | 1997-06-04 | $7700.00 | Window Closed / Lapsed |