Chemically treated glass fibers for reinforcing polymeric materials and processes

Claim 2

Glass fiber strands having a plurality of glass fibers where each glass fiber has at least a portion of its surface covered with the dried residue of an aqueous chemical treating composition, comprising: a. a film forming polymeric system, comprising: 1. an aqueous soluble, emulsifiable or dispersible epoxy-containing polymer or copolymer having an epoxy equivalent weight in the range of about 180 to about 230 grams of polymer per one gram of equivalent epoxide and present in the aqueous chemical treating composition in an amount of about 50 to about 70 weight percent of the solids of the aqueous chemical treating composition. 2. an aqueous soluble, emulsifiable or dispersible non-tacky film forming polymer which is compatible in the epoxy-containing polymer, 3. polyvinyl pyrrolidone in an amount of not greater than 25 weight percent of the solids of the aqueous chemical treating composition, b. methacryloxy alkyltrialkoxy silane coupling agent, c. cationic glass fiber lubricant in an effective lubricating amount, d. water in an amount to give a total solids in the range of about 1 to about 30 weight percent, wherein the aqueous chemical treating composition is essentially free of glass fiber lubricants which are water insoluble, hydrogenated or saturated fatty acid esters of glycerol or vegetable oils.

Claim 3

Glass fibers of claim 1, wherein the epoxy-containing polymer or copolymer is present in an aqueous emulsion prepared with one or more surfactants which are condensates of ethylene oxide with hydrophobic bases formed by condensation of propylene oxide with propylene glycol.

Claim 4

Glass fiber strands of claim 2. wherein the epoxy resin is a phenolic epoxy formed by the reaction of a stoichiometric excess of an epihalohydrin with bis(4-hydroxyphenyl)-2,2-propane, bis(hydroxyphenyl) methane.

Claim 5

Glass fibers of claim 1, that are chopped glass fiber strands having an apparent bulk density of greater than 30 pounds per cubic foot.

Claim 6

Glass fiber strands of claim 1, wherein the non-tacky film forming polymer is selected from the group consisting of bisphenolic polyester resins and high molecular weight saturated epoxy ester polymers.

Claim 7

Glass fiber strands of claim 3, wherein the amount of the non-tacky film forming polymer is in the range of about 1 to about 20 weight percent of the solids of the aqueous chemical treating composition.

Claim 8

Glass fiber strands of claim 1, wherein the non-tacky film forming polymer yields a dried film having an infrared absorption spectra of FIG. 1.

Claim 9

Glass fiber strands of claim 1, wherein the non-tacky film forming polymer is present in an aqueous emulsion and is a bisphenolic polyester resin in an anionic emulsion having a solids content of around 40 percent and a pH in the range of 4 to 5 and a viscosity at 23° C. in the range of 40 to 100 centipoise.

Claim 10

Glass fiber strands of claim 1, wherein the non-tacky film forming polymer is a high molecular weight saturated epoxy ester in a nonionic aqueous emulsion having a solids content of around 30 percent and a pH in the range of 4 to 5.5 and a viscosity at 23° C. of around 200 to around 500 centipoise where the epoxy resin polymer has a hydroxyl number of around 90 to 110 and an acid number of around 8 to 12 and an epoxy equivalent weight of around 8,000 to 10,000.

Claim 11

Glass fiber strands of claim 1, wherein the polyvinyl pyrrolidone has an average molecular weight in the range of about 5,000 to 100,000 and is present in an amount to give a ratio of the polyvinyl pyrrolidone to the epoxy-containing polymer or copolymer in the film forming system in the range of about 2.5 to about 3.5 based on the weight percent solids of the polymers.

Claim 12

Glass fiber strands of claim 1, wherein the methacryloxy alkyltrialkoxy silane is methacryloxy propyltrimethoxy silane which is hydrolyzed and present in an amount of about 0.1 to about 10 weight percent of the solids of the aqueous treating composition.

Claim 13

Glass fiber strands of claim 1, wherein the cationic glass fiber lubricant is a partially amidated, polyalkyl amine formed by the reaction of a mixture of fatty acids having about 2 to about 18 carbon atoms and a polyamine polymer having a molecular weight of about 1200 where the reaction product has a residual amine value of from about 300 to 400 and the amount of this glass fiber lubricant is in the range of about 0.05 to about 0.5 weight percent of the aqueous chemical treating composition.

Claim 14

Glass fiber strands of claim 1, wherein the dried residue of the aqueous chemical treating composition has a moisture content of about 0.01 to about 0.1 weight percent of the glass fiber strands.

Claim 15

Glass fiber strands of claim 1, wherein the amount of the dried residue on the glass fiber strands is in the range of about 0.5 to about 8 weight percent of the glass fiber strands.

Claim 16

Glass fiber strands of claim 1, wherein the film forming polymer system is essentially free of any poly(vinyl acetate) homopolymer.

Claim 17

Glass fiber strands of claim 1, wherein the glass fibers without the dried residue of the aqueous chemical treating composition have a refractive index in the range of about 0.549 to about 1.557.

Claim 18

Glass fiber strands having a plurality of glass fibers, where each glass fiber has at least a portion of its surface covered with the dried residue of an aqueous chemical treating composition, comprising: a. a film forming polymeric system, comprising:

Claim 19

Glass fiber strands having a plurality of glass fibers, where each glass fiber has at least a portion of its surface covered with the dried residue of an aqueous chemical treating composition, comprising: a. a film forming polymeric system, comprising:

Claim 20

an aqueous emulsion of an epoxy-containing polymer or copolymer having an epoxy equivalent weight in the range of about 180 to about 230 grams of polymer per one gram of equivalent epoxide present in a sufficient quantity to give an amount of the polymer in the aqueous chemical treating composition in the range of about 50 to about 70 weight percent of the solids of the aqueous chemical treating composition, wherein the emulsion is formed with one or more surfactants which are condensates of ethylene oxide with hydrophobic bases formed by condensation of propylene oxide with propylene glycol, 2. an aqueous emulsion of a non-tacky film forming polymer selected from the group consisting of an anionic aqueous emulsion of a bisphenolic polyester resin and a nonionic emulsion of a high molecular weight saturated epoxy ester wherein the amount of the emulsions in the aqueous chemical treating composition is sufficient to give an amount of the polymer in the range of about 1 to about 20 weight percent of the solids of the aqueous chemical treating composition, 3. polyvinyl pyrrolidone in an amount to give a ratio of the polyvinyl pyrrolidone to the epoxy-containing polymer or copolymer in the film forming system in the range of about 2.5 to about 3.5 based on the weight percent solids of the polymers, b. methacryloxy propyltrimethoxy silane coupling agent, c. partially amidated polyalkylene amine cationic lubricant in an effective lubricating amount, d. water in an amount to give a total solids in the range of about 1 to about 30 weight percent wherein the aqueous chemical treating composition is essentially free of glass fiber lubricants selected from the group consisting of water insoluble or hydrogenated or saturated fatty acid esters of glycerol, or vegetable oils.

Claim 21

an aqueous emulsion of an epoxy-containing polymer or copolymer having an epoxy equivalent weight in the range of about 180 to about 230 grams of polymer per one gram of equivalent epoxide present in a sufficient quantity to give an amount of the polymer in the aqueous chemical treating composition in the range of about 50 to about 70 weight percent of the solids of the aqueous chemical treating composition, wherein the emulsion is formed with one or more surfactants which are condensates of ethylene oxide with hydrophobic bases formed by condensation of propylene oxide with propylene glycol, 2. an aqueous emulsion of a non-tacky film forming polymer selected from the group consisting of an anionic aqueous emulsion of a bisphenolic polyester resin and a nonionic emulsion of a high molecular weight saturated epoxy ester wherein the amount of the emulsions in the aqueous chemical treating composition is sufficient to give an amount of the polymer in the range of about 1 to about 20 weight percent of the solids of the aqueous chemical treating composition, 3. polyvinyl pyrrolidone in an amount to give a ratio of the polyvinyl pyrrolidone to the epoxy-containing polymer or copolymer in the film forming system in the range of about 2.5 to about 3.5 based on the weight percent solids of the polymers, b. methacryloxy propyltrimethoxy silane coupling agent, c. partially amidated polyalkylene amine cationic lubricant in an effective lubricating amount, d. water in an amount to give a total solids in the range of about 1 to about 30 weight percent wherein the aqueous chemical treating composition is essentially free of glass fiber lubricants selected from the group consisting of water insoluble or hydrogenated or saturated fatty acid esters of glycerol, or vegetable oils.

Claim 22

Glass fiber strands of claim 17, wherein the dried residue is present in an amount of about 0.5 to about 8 weight percent of the treated glass fiber strands.

Claim 23

Glass fiber strands of claim 17, wherein the glass fibers without the aqueous chemical treating composition have a refractive index in the range of about 1.549 to about 1.557.

Claim 24

Method of forming fiber reinforced polymeric materials having good clarity and weatherability, comprising: A. preparing chemically treated glass fibers, wherein the glass fibers have applied to them an aqueous chemical treating composition so that at least a portion of the surface of each glass fiber is covered with the treating composition where the composition has: a. a film forming polymer system, comprising: 1. an aqueous soluble, emulsifiable or dispersible epoxy-containing polymer or copolymer having an epoxy equivalent weight in the range of about 180 to about 230 grams of polymer per one gram of equivalent epoxide and present in the aqueous chemical treating composition in an amount of about 50 to about 70 weight percent of the solids of the aqueous chemical treating composition, 2. an aqueous soluble, emulsifiable or dispersible non-tacky film forming polymer which is compatible in the epoxy-containing polymer, 3. polyvinyl pyrrolidone in an amount of not greater than 25 weight percent of the solids of the aqueous chemical treating composition, b. methacryloxy alkyltrialkoxy silane coupling agent, c. cationic glass fiber lubricant in an effective lubricating amount, d. water in an amount to give a total solids in the range of about 1 to about 30 weight percent, wherein the aqueous chemical treating composition is essentially free of glass fiber lubricants which are water insoluble, hydrogenated or saturated fatty acid esters of glycerol or vegetable oils, B. chopping the glass fiber strands, C. applying the chopped glass fiber strands to a matrix resin, wherein the glass fibers wet-out within the resin within 5 to 10 minutes, and D. curing the glass fiber containing polymeric matrix to produce the fiber reinforced polymeric material.

Claim 25

Method of forming fiber reinforced polymeric materials having good clarity and weatherability, comprising: A. preparing chemically treated glass fibers, wherein the glass fibers have applied to them an aqueous chemical treating composition so that at least a portion of the surface of each glass fiber is covered with the treating composition where the composition has: a. a film forming polymer system, comprising: 1. an aqueous soluble, emulsifiable or dispersible epoxy-containing polymer or copolymer having an epoxy equivalent weight in the range of about 180 to about 230 grams of polymer per one gram of equivalent epoxide and present in the aqueous chemical treating composition in an amount of about 50 to about 70 weight percent of the solids of the aqueous chemical treating composition, 2. an aqueous soluble, emulsifiable or dispersible non-tacky film forming polymer which is compatible in the epoxy-containing polymer, 3. polyvinyl pyrrolidone in an amount of not greater than 25 weight percent of the solids of the aqueous chemical treating composition, b. methacryloxy alkyltrialkoxy silane coupling agent, c. cationic glass fiber lubricant in an effective lubricating amount, d. water in an amount to give a total solids in the range of about 1 to about 30 weight percent, wherein the aqueous chemical treating composition is essentially free of glass fiber lubricants which are water insoluble, hydrogenated or saturated fatty acid esters of glycerol or vegetable oils, B. chopping the glass fiber strands, C. applying the chopped glass fiber strands to a matrix resin, wherein the glass fibers wet-out within the resin within 5 to 10 minutes, and D. curing the glass fiber containing polymeric matrix to produce the fiber reinforced polymeric material.