Method for ablating a coded marking into a glass workpiece and product thereof
Assignee: RCA Licensing Corp
•
Filing: 1982-09-20
•
Granted: 1985-05-07
•
Expires: 2002-09-20
Abstract
Abstract A dark-colored undercoating is deposited on a desired surface area of a glass workpiece, and a light-colored overcoating is applied upon the undercoating, each coating being dried in less than about 60 seconds. Then a plurality of related marks is recessed through the overcoating by ablation, as with a laser beam. Each of the undercoating and the overcoating is comprised of pigment particles and an alkali silicate binder. Unlike the prior practice, the undercoating contains an operative proportion of mica particles, and the overcoating is essentially free from mica.
Inventors
- 👤 John N. Bleacher
- 👤 Barry M. Cushman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 15:31
CPC Classifications
H; H01; H01J; H01J9/00; B; B41; B41M; B41M5/00; B41M5/24; B44; B44B; B44B7/00; B44B7/002; B44B7/005; C; C03; C03C; C03C17/00; C03C17/34; C03C17/3411; G; G09; G09F; G09F3/00; C03C2217/00; C03C2217/40; C03C2217/43; C03C2217/44; C03C2217/45; C03C2217/46; C03C2217/47; C03C2217/475; C03C2217/48; C03C2217/485; H01J2209/00; H01J2209/46; H01J2209/463; H01J2209/466; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24479; Y10T428/24612; Y10T428/24802; Y10T428/24851; Y10T428/24868; Y10T428/24876; Y10T428/24893; Y10T428/24909; Y10T428/24926; Y10T428/24942; Y10T428/25; Y10T428/251
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
141 words
In a method for producing a machine-readable coded marking in a surface of a glass workpiece, said method including (a) coating a selected surface area of said glass workpiece with an undercoating comprising a first aqueous suspension of first pigment particles and a first alkali silicate binder, (b) drying said undercoating, (c) coating said dry undercoating with an overcoating comprising a second aqueous suspension of second pigment particles and a second alkali silicate binder, (d) drying said overcoating, and (e) recessing a plurality of related marks through said overcoating by selectively ablating said overcoating with a laser beam, the improvement wherein said first suspension includes an operative proportion of mica particles, said proportion of mica being operative to reduce the tendency to spalling of said glass workpiece by said laser beam, and said second suspension is essentially free from mica particles.
Claim 2
Dependent Claim
141 words
In a method for producing a machine-readable coded marking in a surface of a glass workpiece, said method including (a) coating a selected surface area of said glass workpiece with an undercoating comprising a first aqueous suspension of first pigment particles and a first alkali silicate binder, (b) drying said undercoating, (c) coating said dry undercoating with an overcoating comprising a second aqueous suspension of second pigment particles and a second alkali silicate binder, (d) drying said overcoating, and (e) recessing a plurality of related marks through said overcoating by selectively ablating said overcoating with a laser beam, the improvement wherein said first suspension includes an operative proportion of mica particles, said proportion of mica being operative to reduce the tendency to spalling of said glass workpiece by said laser beam, and said second suspension is essentially free from mica particles.
Claim 3
Dependent Claim
16 words
The method defined in claim 1 wherein said mica particles are substantially entirely particles of muscovite.
Claim 4
Dependent Claim
22 words
The method defined in claim 1 wherein said mica particles constitute about 6 to 28 weight percent of said first aqueous suspension.
Claim 5
Dependent Claim
19 words
The method defined in claim 1 wherein said mica particles constitute about 16 weight percent of said aqueous solution.
Claim 6
Dependent Claim
25 words
The method defined in claim 1 wherein said first alkali silicate binder consists essentially of dissolved sodium silicate, dissolved potassium silicate and lithium-stabilized silica sol.
Claim 7
Dependent Claim
106 words
In a workpiece comprising a glass main body, a thin undercoating on a portion of said body and an overcoating on said undercoating, said overcoating having a plurality of related marks recessed through said overcoating, said undercoating comprising first pigment particles and a first alkali silicate binder and said overcoating comprising second pigment particles and a second alkali silicate binder, the improvement wherein said undercoating contains an operative proportion of mica particles therein and said overcoating is essentially free of mica, said proportion of mica being operative to reduce the tendency to spalling of the glass workpiece while said marks are being recessed through said overcoating.
Claim 8
Dependent Claim
106 words
In a workpiece comprising a glass main body, a thin undercoating on a portion of said body and an overcoating on said undercoating, said overcoating having a plurality of related marks recessed through said overcoating, said undercoating comprising first pigment particles and a first alkali silicate binder and said overcoating comprising second pigment particles and a second alkali silicate binder, the improvement wherein said undercoating contains an operative proportion of mica particles therein and said overcoating is essentially free of mica, said proportion of mica being operative to reduce the tendency to spalling of the glass workpiece while said marks are being recessed through said overcoating.
Claim 9
Dependent Claim
16 words
The workpiece defined in claim 6 wherein said mica particles are substantially entirely particles of muscovite.
Claim 10
Dependent Claim
20 words
The workpiece defined in claim 6 wherein said mica particles constitute about 24 to 70 weight percent of said undercoating.
Claim 11
Dependent Claim
18 words
The workpiece defined in claim 6 wherein said mica particles constitute about 37 weight percent of said undercoating.
Claim 12
Dependent Claim
23 words
The workpiece defined in claim 6 wherein said first alkali silicate binder consists essentially of a mixture of sodium, potassium and lithium silicates.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-05-06 | 1988-11-05 | 1989-05-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-05-06 | 1992-11-05 | 1993-05-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-05-06 | 1996-11-05 | 1997-05-07 | $7700.00 | Window Closed / Lapsed |