Continuous inorganic fibers and process for production thereof
Assignee: Ube Corp
•
Filing: 1981-12-15
•
Granted: 1985-05-07
•
Expires: 2001-12-15
Abstract
Abstract Continuous inorganic fibers consisting substantially of Si, Zr and C and optionally of O, said fibers being composed of (1) an amorphous material consisting substantially of Si, Zr and C and optionally of O, or (2) an aggregate consisting substantially of ultrafine crystalline particles of β-SiC, ZrC, a solid solution of β-SiC and ZrC and ZrC 1-x wherein 0<x<1 and having a particle diameter of not more than 500Å, in which amorphous SiO 2 and ZrO 2 sometimes exist in the neighborhood of these ultrafine crystalline particles, or (3) a mixture of said amorphous material (1) and said aggregate (2) of ultrafine crystalline particles. The aforesaid continuous inorganic fibers can be produced by the following steps: a first step of preparing a semi-inorganic block copolymer comprising polycarbosilane blocks having a main chain skeleton composed mainly of carbosilane units of the formula --Si--CH 2 --, each silicon atom of said carbosilane units having bonded thereto a side-chain group selected from the class consisting of hydrogen, lower alkyl and phenyl, and zirconoxane units of the formula --Zr--O--; a second step of preparing a spinning dope of said semi-inorganic block copolymer and spinning the dope; a third step of subjecting the resulting ribers to a treatment of rendering them infusible under tension or under no tension; and a fourth step of firing the infusible fibers at a temperature of 800° to 1800° C. in vacuum or in an atmosphere of an inert gas or a reducing gas.
Inventors
- 👤 Seishi Yajima, deceased
- 👤 heir Akiko Noda
- 👤 Kiyohito Okamura
- 👤 Yoshio Hasegawa
- 👤 Takemi Yamaura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 17:19
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/622; C04B35/62227; C04B35/62272; C04B35/515; C04B35/56; C04B35/565; C04B35/571; C08; C08G; C08G77/00; C08G77/60; Y; Y10; Y10S; Y10S264/00; Y10S264/19; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/294
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
149 words
A process for producing continuous inorganic fibers consisting substantially of Si, Zr and C and optionally of O, which comprises a first step of preparing a semi-inorganic block copolymer comprising polycarbosilane blocks having a main chain skeleton composed mainly of carbosilane units of the formula --Si--CH 2 --, each silicon atom of said carbosilane units having bonded thereto a side-chain group selected from the group consisting of hydrogen, lower alkyl and phenyl, and zirconoxane units of the formula --Zr--O--; a second step of preparing a spinning dope of said semi-inorganic block copolymer and spinning the dope; a third step of subjecting the resulting fibers to a treatment of rendering them infusible under tension or under no tension; and a fourth step of firing the infusible fibers at a temperature of 800° to 1800° C. in a vacuum or in an atmosphere of an inert gas or a reducing gas.
Claim 2
Dependent Claim
149 words
A process for producing continuous inorganic fibers consisting substantially of Si, Zr and C and optionally of O, which comprises a first step of preparing a semi-inorganic block copolymer comprising polycarbosilane blocks having a main chain skeleton composed mainly of carbosilane units of the formula --Si--CH 2 --, each silicon atom of said carbosilane units having bonded thereto a side-chain group selected from the group consisting of hydrogen, lower alkyl and phenyl, and zirconoxane units of the formula --Zr--O--; a second step of preparing a spinning dope of said semi-inorganic block copolymer and spinning the dope; a third step of subjecting the resulting fibers to a treatment of rendering them infusible under tension or under no tension; and a fourth step of firing the infusible fibers at a temperature of 800° to 1800° C. in a vacuum or in an atmosphere of an inert gas or a reducing gas.
Claim 3
Dependent Claim
298 words
The process of claim 1 wherein said semi-inorganic block copolymer is an organometallic copolymer having a number average molecular weight of about 1000 to about 50000 and composed of crosslinked polycarbosilane blocks and polyzirconosiloxane blocks, which is obtained by mixing (1) polycarbosilane with a number average molecular weight of about 500 to about 10000 having a main chain skeleton composed mainly of carbosilane units of the formula --Si--CH 2 --, each silicon atom of the carbosilane units substantially having bonded thereto a side-chain group selected from the class consisting of hydrogen, lower alkyl and phenyl, with (2) polyzirconosiloxane with a number average molecular weight of about 500 to 10000 having a main chain skeleton composed mainly of zirconoxane units of the formula --Zr--O-- and siloxane units of the formula --Si--O--, most of the zirconium atoms of said zirconoxane units having bonded thereto a side-chain group selected from the group consisting of lower alkoxy, phenoxy and acetylacetoxy, most of the silicon atoms of said siloxane units having bonded thereto a side-chain group selected from the class consisting of lower alkyl and phenyl, and the ratio of the total number of said zirconoxane units to that of said siloxane units being in the range of about 30:1 to about 1:30, in such mixing proportions that the ratio of the total number of said carbosilane units to the sum of the total number of said zirconoxane units and the total number of said siloxane units is in the range of about 100:1 to about 1:100; and heating the resulting mixture in an organic solvent in an atmosphere inert to the reaction to bond at least some of the silicon atoms of said polycarbosilane with at least some of the zirconium atoms and/or silicon atoms of said polyzirconosiloxane through an oxygen atom.
Claim 4
Dependent Claim
25 words
The process of claim 2 wherein at least some of the side-chain groups bonded to the silicon atoms of the carbosilane units are hydrogen atoms.
Claim 5
Dependent Claim
170 words
The process of claim 1 wherein said semi-inorganic block polymer is polyzirconocarbosilane having a number average molecular weight of 700 to 100,000 which is obtained by mixing polycarbosilane with a number average molecular weight of 200 to 10000 mainly having a main chain skeleton expressed by the general formula ##STR6## wherein R represents a hydrogen atom, a lower alkyl group or a phenyl group, with an organo zirconium compound of the general formula ZrX.sub.4 wherein X represents an alkoxy group having 1 to 20 carbon atoms, a phenoxy group or an acetylacetoxy group, in such proportions that the ratio of the total number of the structural units --Si--CH 2 -- of the polycarbosilane to that of the structural units --Zr--O-- of the zirconium compound is in the range of from 2:1 to 200-1; and heating the resulting mixture in an atmosphere inert to the reaction, thereby to bond at least some of the silicon atoms of the polycarbosilane to the zirconium atoms of the zirconium compound through an oxygen atom.
Claim 6
Dependent Claim
20 words
The process of claim 4 wherein at least some of the side-chain groups R of the polycarbosilane are hydrogen atoms.
Claim 7
Dependent Claim
24 words
The process of claim 1 wherein said spinning dope in the second step is obtained by heat-melting the copolymer obtained in the first step.
Claim 8
Dependent Claim
23 words
The process of claim 1 wherein said spinning dope is prepared by dissolving the copolymer obtained in the first step in a solvent.
Claim 9
Dependent Claim
29 words
The process of claim 1 wherein said third step is carried out by heating the spun fibers obtained in the second step, at low temperatures in an oxidizing atmosphere.
Claim 10
Dependent Claim
36 words
The process of claim 1 wherein said third step is carried out by exposing the fibers obtained in the second step to irradiation of γ-rays or electron beams in an oxidizing atmosphere or a non-oxidizing atmosphere.
Claim 11
Dependent Claim
42 words
The process of claim 1 wherein after the first step but before the second step, low-molecular-weight compounds in the copolymer obtained in the first step are extracted by a solvent thereby to reduce the content of the low-molecular-weight compounds in the copolymer.
Claim 12
Dependent Claim
56 words
The process of claim 1 wherein after the first step but before the second step, the copolymer formed by the first step is heated under reduced pressure or in an inert gaseous atmosphere to remove a part of the low-molecular-weight compounds in the copolymer thereby to reduce the content of the low-molecular-weight compounds in the copolymer.
Claim 13
Dependent Claim
42 words
The process of claim 1 wherein after the fourth step, the fired fibers are treated with an acid or alkali, and/or heated at a temperature of 800° to 1600° C. in an oxidizing atmosphere, thereby to remove impurities in the fired fibers.
References Cited (Backward Citations)
US4010233A
Cited
US4205032A
Cited
US4289720A
Cited
US4283376A
Cited
US4222977A
Cited
US4342712A
Cited
US4336215A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-05-06 | 1988-11-05 | 1989-05-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-05-06 | 1992-11-05 | 1993-05-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-05-06 | 1996-11-05 | 1997-05-07 | $7700.00 | Window Closed / Lapsed |