Process for vitrifying liquid radioactive waste
Assignee: National Institute of Advanced Industrial Science and Technology
•
Filing: 1982-07-06
•
Granted: 1985-04-30
•
Expires: 2002-07-06
Abstract
Abstract A process for vitrifying liquid radioactive waste is provided. In this process, a solution of a water-soluble vitrifying-facilitating inorganic compound in liquid radioactive waste is mixed with a solution obtained by hydrolyzing an alkyl silicate and then the solution mixture is left to gel. Thereafter, the resulting gel is irradiated with microwave to calcine the gel, and the calcined gel is further heated to melt and then cooled to obtain a vitrified product.
Inventors
- 👤 Hajimu Wakabayashi
- 👤 Ryohei Terai
- 👤 Hiroshi Yamanaka
- 👤 Shigeo Hara
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 12:50
CPC Classifications
C; C03; C03C; C03C1/00; C03C1/002; C03B; C03B1/00; C03B5/00; C03B5/005; C03B5/02; C03B5/023; C03C1/006; G; G21; G21F; G21F9/00; G21F9/28; G21F9/30; G21F9/301; G21F9/302; G21F9/305; Y; Y02; Y02P; Y02P40/00; Y02P40/50
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
154 words
A process for vitrifying liquid radioactive waste, comprising the steps of: dissolving at least one water-soluble vitrifying-facilitating inorganic compound selected from the group consisting of boric acid, aluminum hydroxide, lithium nitrate, lithium carbonate, lithium sulfate, magnesium nitrate, magnesium carbonate, magnesium sulfate, calcium nitrate, calcium carbonate, barium nitrate, aluminum nitrate, zinc nitrate, zinc sulfate, zirconium oxynitrate and a hydrate thereof, into a liquid radioactive waste acidified with nitric acid adding to the resulting solution an alcoholic silica sol obtainable through hydrolysis with an acid of at least about 1 part by weight of alkyl silicate to 1 part by weight of the at least one inorganic compound, based on the weight of the oxide, and allowing the resulting solution mixture to gel at a temperature of from room temperature to 50? C., calcining the resulting gel by microwave radiation, and heating the resulting calcined product to melt, followed by cooling to obtain a vitrified product.
Claim 2
Dependent Claim
154 words
A process for vitrifying liquid radioactive waste, comprising the steps of: dissolving at least one water-soluble vitrifying-facilitating inorganic compound selected from the group consisting of boric acid, aluminum hydroxide, lithium nitrate, lithium carbonate, lithium sulfate, magnesium nitrate, magnesium carbonate, magnesium sulfate, calcium nitrate, calcium carbonate, barium nitrate, aluminum nitrate, zinc nitrate, zinc sulfate, zirconium oxynitrate and a hydrate thereof, into a liquid radioactive waste acidified with nitric acid adding to the resulting solution an alcoholic silica sol obtainable through hydrolysis with an acid of at least about 1 part by weight of alkyl silicate to 1 part by weight of the at least one inorganic compound, based on the weight of the oxide, and allowing the resulting solution mixture to gel at a temperature of from room temperature to 50? C., calcining the resulting gel by microwave radiation, and heating the resulting calcined product to melt, followed by cooling to obtain a vitrified product.
Claim 3
Dependent Claim
21 words
A process for vitrifying liquid radioactive waste according to claim 1, wherein the calcined product is heated by the microwave irradiation.
Claim 4
Dependent Claim
28 words
A process for vitrifying liquid radioactive waste according to claim 1, wherein the calcined product is heated by high frequency heating, electric Joule heating or external heating means.
References Cited (Backward Citations)
US3298960A
Cited
US3791808A
Cited
US3959172A
Cited
US4221680A
Cited
US4242220A
Cited
US4312774A
Cited
US4382026A
Cited
US4333847A
Cited
US4376070A
Cited
US4377507A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-04-29 | 1988-10-29 | 1989-04-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-04-29 | 1992-10-29 | 1993-04-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-04-29 | 1996-10-29 | 1997-04-30 | $7700.00 | Window Closed / Lapsed |