Single-batch process to prepare noble metal vanadium alloy catalyst on a carbon based support
Assignee: RTX Corp
•
Filing: 1983-06-20
•
Granted: 1985-04-23
•
Expires: 2003-06-20
Abstract
Abstract A novel single-batch method for preparing carbon supported alloy catalysts, wherein one of the metals is a noble metal, preferably platinum and the other metals selected from the transition Groups IV, V, VI or VII. The process comprises sequentially adsorbing the metallic components onto the carbon support. The adsorption takes place in an aqueous medium and the metal components are introduced in the ionic form. The catalyst is finally formed by heating to an elevated temperature.
Inventors
- 👤 Francis J. Luczak
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 18:04
CPC Classifications
B; B01; B01J; B01J23/00; B01J23/38; B01J23/54; B01J23/56; B01J23/64
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
179 words
A method for making a finely divided platinum alloy catalyst supported on carbon for use in a fuel cell comprising: (a) preparing an aqueous dispersion of platinum ions and electrically conductive carbon support particles, heating the dispersion to about 45° C., (b) preparing a sulfur ion containing aqueous solution, (c) adding the sulfur ion solution to the platinum dispersion and agitating while maintaining the dispersion at about 45° C., (d) adsorbing the platinum onto the carbon support by intimately contacting the platinum with the support particles by agitating and maintaining the dispersion at about 45° C., (e) preparing a second aqueous dispersion containing a salt of an element from transition Groups IV, V, VI or VII, (f) adding the second aqueous dispersion to the platinum dispersion while maintaining the dispersion at about 45° C. and adjusting the pH to about 5.5, (g) adsorbing the transition element onto the support particles by agitating while maintaining the dispersion at about 45° C.; (h) removing the treated support particles from the dispersion, drying, sifting and heating the particles to form the catalyst.
Claim 2
Independent Claim
179 words
A method for making a finely divided platinum alloy catalyst supported on carbon for use in a fuel cell comprising: (a) preparing an aqueous dispersion of platinum ions and electrically conductive carbon support particles, heating the dispersion to about 45° C., (b) preparing a sulfur ion containing aqueous solution, (c) adding the sulfur ion solution to the platinum dispersion and agitating while maintaining the dispersion at about 45° C., (d) adsorbing the platinum onto the carbon support by intimately contacting the platinum with the support particles by agitating and maintaining the dispersion at about 45° C., (e) preparing a second aqueous dispersion containing a salt of an element from transition Groups IV, V, VI or VII, (f) adding the second aqueous dispersion to the platinum dispersion while maintaining the dispersion at about 45° C. and adjusting the pH to about 5.5, (g) adsorbing the transition element onto the support particles by agitating while maintaining the dispersion at about 45° C.; (h) removing the treated support particles from the dispersion, drying, sifting and heating the particles to form the catalyst.
Claim 3
Dependent Claim
17 words
The method of claim 1 wherein the platinum ions are provided in the form of chloroplatinic acid.
Claim 4
Dependent Claim
17 words
The method of claim 1 wherein the sulfur ions are provided in the form of sodium dithionite.
Claim 5
Dependent Claim
11 words
The method of claim 1 wherein the transition element is vanadium.
Claim 6
Dependent Claim
15 words
The method of claim 4 wherein vanadium is provided in the form of ammonium meta-vanadate.
Claim 7
Dependent Claim
13 words
A platinum alloy carbon supported catalyst prepared by the process of claim 1.
Claim 8
Dependent Claim
21 words
The catalyst of claim 6 wherein the finely divided platinum alloy has an average particle size less than about 45 Å.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-04-22 | 1988-10-22 | 1989-04-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-04-22 | 1992-10-22 | 1993-04-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-04-22 | 1996-10-22 | 1997-04-23 | $7700.00 | Window Closed / Lapsed |