Chlorosulfonated polyethylene coating composition

Claim 2

A coating composition comprising 10-80% by weight of binder and 20-90% by weight of an organic solvent; wherein the binder consists essentially of about (1) 40-85% by weight, based on the weight of the binder, of a chlorosulfonated polyethylene having a weight average molecular weight of about 75,000 to 300,000 determined by gel permeation chromatography and having a chlorine content of 20 to 50% by weight and a sulfur content of 0.7 to 2.0% by weight; (2) 9-44% by weight, based on the weight of the binder, of an epoxy resin; (3) 3-20% by weight, based on the weight of the binder, of a polyamine curing agent of the formula ##STR8## where R is R 1 NH 2 and R 1 is an aliphatic or cycloaliphatic radical; and (4) 0.1-3% by weight, based on the weight of the binder, of a bicyclic amidine.

Claim 3

The coating composition of claim 1 containing pigment in a pigment-to-binder weight ratio of about 20:100 to 200:100.

Claim 4

The coating composition of claim 2 in which the chlorosulfonated polyethylene has the formula ##STR9## where m and n are positive integers of about 5-25 and has a weight average molecular weight of about 100,000 to 150,000.

Claim 5

The coating composition of claim 3 in which the epoxy resin has the formula ##STR10## where R 2 is an aromatic radical and b is a positive integer of about 0.5 to 4.

Claim 6

The coating composition of claim 4 in which R 2 is ##STR11##

Claim 7

The coating composition of claim 3 in which the epoxy resin is an epoxy novolac resin of the formula ##STR12## where d is a positive integer of about 0.2-2.

Claim 8

The coating composition of claim 3 in which R is ##STR13##

Claim 9

The coating composition of claim 3 in which the bicyclic amidine is 1,8-diaza-bicyclo(5,4,0)-undecene-7.

Claim 10

The coating composition of claim 3 containing about 0.1-3% by weight, based on the weight of the binder, of a fluorochemical surfactant.

Claim 11

The coating composition of claim 2 in which the binder consists essentially of about (1) 40-85% by weight, based on the weight of the binder, of a chlorosulfonated polyethylene having the formula ##STR14## where m and n are positive integers of about 5-25 and has a weight average molecular weight of about 100,000 to 150,000. (2) 9-44% by weight, based on the weight of the binder, of an epoxy resin of the formula ##STR15## where b is a positive integer of about 0.5 to 4; (3) 3-20% by weight, based on the weight of the binder, of a polyamine curing agent of the formula ##STR16## where R is ##STR17## and (4) 0.01-3% by weight of 1,8-diaza-bicyclo(5,4,0)-undecene-7.

Claim 12

A two-component composition wherein the two components are mixed together to form a composition comprising about 10-80% by weight binder and 20-90% by weight organic solvent and wherein the binder consists essentially of about 40-85% by weight, of chlorosulfonated polyethylene, 9-44% by weight of epoxy resin, 3-20% by weight of polyamine curing agent, and 0.1-3% by weight of bicyclic amidine and wherein the the components comprise component (1) a solution of a chlorosulfonated polyethylene having a weight average molecular weight of about 75,000 to 300,000 determined by gel permeation chromatography and having a chlorine content of 20 to 50% by weight and a sulfur content of 0.7 to 2% by weight and an epoxy resin. component (2) a polyamine curing agent of the formula ##STR18## where R is R 1 NH 2 and R 1 is an aliphatic or cycloaliphatic radical and a bicyclic amidine.

Claim 13

A two-component composition wherein the two components are mixed together to form a composition comprising about 10-80% by weight binder and 20-90% by weight organic solvent and wherein the binder consists essentially of about 40-85% by weight, of chlorosulfonated polyethylene, 9-44% by weight of epoxy resin, 3-20% by weight of polyamine curing agent, and 0.1-3% by weight of bicyclic amidine and wherein the the components comprise component (1) a solution of a chlorosulfonated polyethylene having a weight average molecular weight of about 75,000 to 300,000 determined by gel permeation chromatography and having a chlorine content of 20 to 50% by weight and a sulfur content of 0.7 to 2% by weight and an epoxy resin. component (2) a polyamine curing agent of the formula ##STR18## where R is R 1 NH 2 and R 1 is an aliphatic or cycloaliphatic radical and a bicyclic amidine.

Claim 14

A substrate coated with a cured layer of the composition of claim 1.

Claim 15

A metal substrate coated with a cured primer layer of the composition of claim 2 and having in superimposed adherence to the primer layer a cured layer of a fluorocarbon polymer comprising vinylidene fluoride and hexafluoropropylene.