Valve metal powder doped with boron
Assignee: H.C. Starck GmbH
•
Filing: 1984-06-13
•
Granted: 1985-04-23
•
Expires: 2004-06-13
Abstract
Abstract A process for the production of valve metal powder, which is doped with boron or boron compounds, for electrolytic capacitors having a low relative leakage current and a high specific charge. The doping with boron or boron compounds in amounts of up to 0.5 percent by weight, relative to the metal content, can take place either during the production of the metal powder or the green valve metal anodes.
Inventors
- 👤 Wolf-Wigand Albrecht
- 👤 Uwe Papp
- 👤 Dieter Behrens
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 09:23
CPC Classifications
H; H01; H01G; H01G9/00; H01G9/004; H01G9/04; H01G9/048; H01G9/052; H01G9/0525; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12028; Y10T428/12042
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
84 words
In a process for producing an agglomerated valve metal powder for use in electrolytic capacitors having a low relative leakage current and a high specific charge, wherein the valve metal powder is heated under vacuum or under inert gas until an agglomerated state of said valve metal powder is achieved, the improvement which comprises admixing boron or a boron compound in amount up to 0.5 percent by weight, relative to the metal content, with the valve metal powder before thus thermally agglomerating said powder.
Claim 2
Dependent Claim
84 words
In a process for producing an agglomerated valve metal powder for use in electrolytic capacitors having a low relative leakage current and a high specific charge, wherein the valve metal powder is heated under vacuum or under inert gas until an agglomerated state of said valve metal powder is achieved, the improvement which comprises admixing boron or a boron compound in amount up to 0.5 percent by weight, relative to the metal content, with the valve metal powder before thus thermally agglomerating said powder.
Claim 3
Dependent Claim
11 words
Valve metal powder produced by the process according to claim 1.
Claim 4
Dependent Claim
79 words
In a process for producing a sintered valve metal anode which comprises forming a green valve metal anode with valve metal powder and sintering said green valve metal anode, the improvement which comprises adding a boron compound in liquid or gaseous phase to the green valve metal anode prior to or during sintering so that in the sintered final product boron of up to 0.5 percent by weight, relative to the metal content, is present in the metallic phase.
Claim 5
Dependent Claim
79 words
In a process for producing a sintered valve metal anode which comprises forming a green valve metal anode with valve metal powder and sintering said green valve metal anode, the improvement which comprises adding a boron compound in liquid or gaseous phase to the green valve metal anode prior to or during sintering so that in the sintered final product boron of up to 0.5 percent by weight, relative to the metal content, is present in the metallic phase.
Claim 6
Dependent Claim
12 words
A sintered valve metal anode produced by the process of claim 3.
Claim 7
Dependent Claim
109 words
In a process for producing a doped valve metal powder for use in electrolytic capacitors having a low relative leakage current and a high specific charge, wherein a doping agent is added to raw material for producing the valve metal and said raw material is then processed to produce the valve metal in elemental and powdered form, the improvement which comprises during the production of said valve metal powder admixing boron or a boron compound as the doping agent with the raw material for producing said valve metal powder in an amount of up to 0.5 percent by weight relative to the total metal content of the resulting powder.
Claim 8
Dependent Claim
109 words
In a process for producing a doped valve metal powder for use in electrolytic capacitors having a low relative leakage current and a high specific charge, wherein a doping agent is added to raw material for producing the valve metal and said raw material is then processed to produce the valve metal in elemental and powdered form, the improvement which comprises during the production of said valve metal powder admixing boron or a boron compound as the doping agent with the raw material for producing said valve metal powder in an amount of up to 0.5 percent by weight relative to the total metal content of the resulting powder.
Claim 9
Dependent Claim
42 words
Process according to claim 5, in which the boron or compound of boron is used in an amount so as to be present in an amount of at least 0.0005 percent by weight of the total metal content of the resulting powder.
Claim 10
Dependent Claim
11 words
Valve metal powder produced by the process according to claim 5.
Claim 11
Dependent Claim
13 words
A sintered anode produced from the valve metal powder according to claim 7.
Claim 12
Dependent Claim
55 words
A process according to claim 5, wherein during the production of the boron-doped valve metal, the boron or boron compound is added in an amount of up to 0.5 percent by weight, relative to the metal content, to one of one or more auxiliary agents participating in a reduction process for producing said valve metal.
Claim 13
Dependent Claim
14 words
Process according to claim 9, in which the boron compound is KBF 4 .
Claim 14
Dependent Claim
12 words
A valve metal powder produced by the processing according to claim 10.
Claim 15
Dependent Claim
21 words
A process according to claim 5, wherein tantalum and/or niobium or alloys thereof are produced and is used as valve metals.
Claim 16
Dependent Claim
26 words
A process according to claim 12, wherein boron-doped K 2 TaF 7 is employed as the raw material for the production of B-doped tantalum metal powder.
Claim 17
Dependent Claim
11 words
Valve metal powder produced by the process according to claim 13.
Claim 18
Dependent Claim
39 words
A process according to claim 13, wherein boron is added as a doping agent in the form of soluble compounds thereof to a solution from which K 2 TaF 7 is recovered prior to the crystallization and precipitation thereof.
Claim 19
Dependent Claim
12 words
Valve metal powder produced and by the process according to claim 15.
Claim 20
Dependent Claim
13 words
Process according to claim 15, in which the boron compound is boric acid.
Claim 21
Dependent Claim
12 words
A valve metal powder produced by the process according to claim 17.
References Cited (Backward Citations)
US2769114A
Cited
US3470030A
Cited
US3723838A
Cited
US4231790A
Cited
US4009007A
Cited
US4229217A
Cited
US4084965A
Cited
US4141719A
Cited
US4141720A
Cited
US4356028A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-04-22 | 1988-10-22 | 1989-04-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-04-22 | 1992-10-22 | 1993-04-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-04-22 | 1996-10-22 | 1997-04-23 | $7700.00 | Window Closed / Lapsed |