Thermoplastic PVC molding compositions
Assignee: Albemarle Corp
•
Filing: 1980-11-24
•
Granted: 1985-04-09
•
Expires: 2000-11-24
Abstract
Abstract Blends of (a) a vinyl chloride polymer having a relative viscosity as measured at a concentration of 1 gram per 100 grams of cyclohexanone at 25° C. falling within the range of about 1.50 to about 1.85; (b) a copolymer of a vinyl aromatic compound and an α,β-unsaturated cyclic anhydride in which the relative proportions of said compound and said anhydride fall within the range of about 91 to about 70 weight percent of said compound and about 9 to about 30 weight percent of said anhydride; and (c) a tin-containing stabilizer and an impact modifier for vinyl chloride polymers. These blends contain 60 to 40 weight percent of (a) and 40 to 60 weight percent of (b) and have an Izod impact strength (ASTM D 256, Method A) of at least 0.5 foot pound per inch; a heat deflection temperature (ASTM D 648) at 66 psi of at least 75° C.; and a dynamic thermal stability of at least 10 minutes.
Inventors
- 👤 Jesse D. Jones
- 👤 Edwin D. Hornbaker
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 21:05
CPC Classifications
C; C08; C08L; C08L27/00; C08L27/02; C08L27/04; C08L27/06; C08L51/00; C08L51/04
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
211 words
A thermoplastic composition which comprises in intimate admixture: (a) a vinyl chloride polymer having a relative viscosity as measured at a concentration of 1 gram per 100 grams of cyclohexanone at 25° C. falling within the range of about 1.50 to about 1.85; and (b) a rubber-modified graft copolymer of a vinyl aromatic compound and an α,β-unsaturated cyclic anhydride in which the relative proportions of said compound and said anhydride fall within the range of about 91 to about 70 weight percent of said compound and about 9 to about 30 weight percent of said anhydride, and in which the graft copolymer contains up to 33 parts by weight of the rubber per 100 parts by weight of the copolymer; and (c) a tin-containing stabilizer and an impact modifier for vinyl chloride polymers; with the proviso that said admixture contains 60 to 35 weight percent of (a) and 40 to 65 weight percent of (b) and the further proviso that the blend has the following properties: (d) an Izod impact strength (ASTM D 256, Method A) of at least 0.5 foot pound per inch; (e) a heat deflection temperature (ASTM D 648) at 66 psi of at least 75° C.; and (f) a dynamic thermal stability of at least 10 minutes.
Claim 2
Dependent Claim
211 words
A thermoplastic composition which comprises in intimate admixture: (a) a vinyl chloride polymer having a relative viscosity as measured at a concentration of 1 gram per 100 grams of cyclohexanone at 25° C. falling within the range of about 1.50 to about 1.85; and (b) a rubber-modified graft copolymer of a vinyl aromatic compound and an α,β-unsaturated cyclic anhydride in which the relative proportions of said compound and said anhydride fall within the range of about 91 to about 70 weight percent of said compound and about 9 to about 30 weight percent of said anhydride, and in which the graft copolymer contains up to 33 parts by weight of the rubber per 100 parts by weight of the copolymer; and (c) a tin-containing stabilizer and an impact modifier for vinyl chloride polymers; with the proviso that said admixture contains 60 to 35 weight percent of (a) and 40 to 65 weight percent of (b) and the further proviso that the blend has the following properties: (d) an Izod impact strength (ASTM D 256, Method A) of at least 0.5 foot pound per inch; (e) a heat deflection temperature (ASTM D 648) at 66 psi of at least 75° C.; and (f) a dynamic thermal stability of at least 10 minutes.
Claim 3
Dependent Claim
17 words
A composition of claim 1 wherein (b) is a graft copolymer of a styrene and maleic anhydride.
Claim 4
Dependent Claim
49 words
A composition of claim 1 wherein (b) is a graft copolymer of a styrene and a maleic anhydride in which the relative proportions thereof fall within the range of about 86 to about 80 weight percent of styrene and about 14 to about 20 weight percent of maleic anhydride.
Claim 5
Dependent Claim
22 words
A composition of claim 1 wherein said admixture contains about 50 weight percent of (a) and about 50 weight percent of (b).
Claim 6
Dependent Claim
10 words
A composition of claim 1 wherein (a) is polyvinyl chloride.
Claim 7
Dependent Claim
40 words
A composition of claim 1 wherein (a) is polyvinyl chloride having a relative viscosity as measured at a concentration of 1 gram per 100 grams of cyclohexanone at 25° C. falling within the range of about 1.50 to about 1.65.
Claim 8
Dependent Claim
22 words
A composition of claim 1 wherein (a) is polyvinyl chloride and (b) is a graft copolymer of a styrene and maleic anhydride.
Claim 9
Dependent Claim
81 words
A composition of claim 1 wherein (a) is polyvinyl chloride having a relative viscosity as measured at a concentration of 1 gram per 100 grams of cyclohexanone at 25° C. falling within the range of about 1.50 to about 1.65, and (b) is a graft copolymer of styrene and maleic anhydride in which the relative proportions thereof fall within the range of about 86 to 80 weight percent of styrene and about 14 to about 20 weight percent of maleic anhydride.
Claim 10
Dependent Claim
27 words
A composition of claim 1 wherein said graft copolymer contains up to 25 parts by weight of the rubber per 100 parts by weight of the copolymer.
Claim 11
Dependent Claim
134 words
A polyblend composition comprising: A. from 35 to 60% by weight of polyvinylchloride B. from 65 to 40% by weight of a rubber-modified copolymer of a vinylaromatic monomer, and unsaturated dicarboxylic acid anhydride and copolymerizable termonomer, wherein the relative weight proportions of the monomers are about 70 to about 91% of the vinylaromatic monomer, about 9 to 30% of the anhydride and 0 to 20% of the termonomer; and wherein the monomers are polymerized in the presence of 5 to 25% of a rubber having a glass transition temperature below 0° C.; and C. from about 5 to about 20% by weight of a composition comprising a graft copolymer of a monomer selected from the group comprising methyl methacrylate and acrylonitrile and a vinyl aromatic monomer said copolymer being grafted onto a substrate rubber.
Claim 12
Dependent Claim
134 words
A polyblend composition comprising: A. from 35 to 60% by weight of polyvinylchloride B. from 65 to 40% by weight of a rubber-modified copolymer of a vinylaromatic monomer, and unsaturated dicarboxylic acid anhydride and copolymerizable termonomer, wherein the relative weight proportions of the monomers are about 70 to about 91% of the vinylaromatic monomer, about 9 to 30% of the anhydride and 0 to 20% of the termonomer; and wherein the monomers are polymerized in the presence of 5 to 25% of a rubber having a glass transition temperature below 0° C.; and C. from about 5 to about 20% by weight of a composition comprising a graft copolymer of a monomer selected from the group comprising methyl methacrylate and acrylonitrile and a vinyl aromatic monomer said copolymer being grafted onto a substrate rubber.
Claim 13
Dependent Claim
32 words
A composition according to claim 10 in which the termonomer in Component B is selected from the group consisting of C 1 to C 2 alkyl acrylates and methacrylates and unsaturated nitriles.
Claim 14
Dependent Claim
17 words
A composition according to claim 11 in which Component B is a rubber-modified styrene/maleic anhydride/methyl methacrylate terpolymer.
Claim 15
Dependent Claim
15 words
A composition according to claim 10 that incorporates about 10% by weight of Component C.
Claim 16
Dependent Claim
16 words
A composition according to claim 10 in which Component C is a rubber-modified styrene/methyl methacrylate copolymer.
Claim 17
Dependent Claim
15 words
A composition according to claim 10 in which Component C is a rubber-modified styrene/acrylonitrile copolymer.
Claim 18
Dependent Claim
24 words
A composition according to any one of claims 10 to 15 in which Component A represents from 40 to 55% of the composition weight.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-04-08 | 1988-10-08 | 1989-04-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-04-08 | 1992-10-08 | 1993-04-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-04-08 | 1996-10-08 | 1997-04-09 | $7700.00 | Window Closed / Lapsed |