Method for coating metal surface
Assignee: NITTON ELECTRIC INDUSTRIAL Co Ltd
•
Filing: 1983-12-28
•
Granted: 1985-04-09
•
Expires: 2003-12-28
Abstract
Abstract A method for coating a metal surface by forming a corrosion-protective layer on the metal surface or a defective area of a corrosion-protective layer formed on the metal surface, which comprises using a coating material selected from the group consisting of a tape-like, sheet-like and chip-like polymerizable coating material comprising a vinyl monomer and/or a vinyl group-containing oligomer and a liquid material comprising a vinyl monomer and/or a vinyl group-containing oligomer, wherein either the coating material or the liquid material contains a polymerization initiator and the material not containing the polymerization initiator contains a polymerization accelerator, and polymerizing the vinyl monomer and/or the vinyl monomer-containing oligomer in the state such that the metal surface or the defective area is covered with the coating material by interposing the liquid material therebetween, to form the corrosion-protective layer.
Inventors
- 👤 Toshimitsu Okuno
- 👤 Yutaka Hori
- 👤 Makoto Sunakawa
- 👤 Sadayuki Inagaki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 22:53
CPC Classifications
F; F16; F16L; F16L58/00; F16L58/02; F16L58/04; F16L58/10
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
176 words
A method for coating a metal surface by forming a corrosion-protective layer on the metal surface or on defective areas of a corrosion-protective layer on a metal surface comprising: (a) coating the metal surface, defective areas, or a coating material with a liquid material comprising a vinyl monomer and/or a vinyl group-containing oligomer; (b) wrapping or bonding the coating material which is selected from the group consisting of a tape-like, sheet-like and chip-like polymerizable coating comprising a vinyl monomer and/or a vinyl group-containing oligomer, to the metal surface or defective area such that the liquid material is interposed between the coating material and the metal surface or defective area; and (c) polymerizing the vinyl monomer and/or the vinyl group-containing oligomer to form the corrosion-protective layer; wherein the vinyl monomer and/or vinyl group-containing oligomer is selected from the group consisting of monofunctional monomer or oligomer and a polyfunctional monomer or oligomer; and wherein either the coating material or the liquid material contains a polymerization initiator and the material not containing the polymerization initiator contains a polymerization accelerator.
Claim 2
Independent Claim
176 words
A method for coating a metal surface by forming a corrosion-protective layer on the metal surface or on defective areas of a corrosion-protective layer on a metal surface comprising: (a) coating the metal surface, defective areas, or a coating material with a liquid material comprising a vinyl monomer and/or a vinyl group-containing oligomer; (b) wrapping or bonding the coating material which is selected from the group consisting of a tape-like, sheet-like and chip-like polymerizable coating comprising a vinyl monomer and/or a vinyl group-containing oligomer, to the metal surface or defective area such that the liquid material is interposed between the coating material and the metal surface or defective area; and (c) polymerizing the vinyl monomer and/or the vinyl group-containing oligomer to form the corrosion-protective layer; wherein the vinyl monomer and/or vinyl group-containing oligomer is selected from the group consisting of monofunctional monomer or oligomer and a polyfunctional monomer or oligomer; and wherein either the coating material or the liquid material contains a polymerization initiator and the material not containing the polymerization initiator contains a polymerization accelerator.
Claim 3
Dependent Claim
21 words
The method as claimed in claim 1, wherein one side of the polymerizable coating material is backed with a self-supporting material.
Claim 4
Dependent Claim
44 words
The method as claimed in claim 1, wherein said monofunctional monomer is selected from the group consisting of alkyl acrylate, cycloalkyl acrylate, alkyl methacrylate, cycloalkyl methacrylate, vinyl acetate; vinyl propionate; (meth)acrylonitrile; styrene; vinyltoluene; (meth)acrylic acid; hydroxy ester of (meth)acrylic acid; glycidyl (meth)acrylate; and diethylaminoethyl(meth)acrylate.
Claim 5
Dependent Claim
30 words
The method as claimed in claim 3, wherein said alkyl acrylate or alkyl methacrylate is selected from the group consisting of methyl(meth)acrylate, ethyl(meth)acrylate, n-butyl(meth)acrylate, isobutyl(meth)acrylate, cyclohexyl(meth)acrylate, 2-ethylhexyl(meth)acrylate, decyl(meth)acrylate and lauryl(meth)acrylate.
Claim 6
Dependent Claim
24 words
The method as claimed in claim 3, wherein said hydroxy ester of (meth)acrylic acid is selected from the group consisting of 2-hydroxyethyl(meth)acrylate and 2-hydroxypropyl(meth)acrylate.
Claim 7
Dependent Claim
33 words
The method as claimed in claim 1, wherein said polyfunctional vinyl monomer is selected from the group consisting of ethylene glycol, propylene glycol, diesters of (meth)acrylic acid, trimethylolpropane tri(meth)acrylate and tetramethylol propane tetra(meth)acrylate.
Claim 8
Dependent Claim
31 words
The method as claimed in claim 6, wherein said diester of (meth)acrylic acid is selected from the group consisting of ethylene glycol di(meth)acrylate and diethylene glycol di(meth)acrylate and triethylene glycol tri(meth)acrylate.
Claim 9
Dependent Claim
24 words
The method as claimed in claim 1, wherein said monofunctional oligomer is polyester mono(meth)acrylate obtained by the reaction of polyester resin and (meth)acrylic acid.
Claim 10
Dependent Claim
67 words
The method as claimed in claim 1, wherein said polyfunctional oligomer is selected from the group consisting of polyethylene glycol di(meth)acrylate; epoxy(meth)acrylate obtained by the reaction of epoxy resin and (meth)acrylic acid; urethane (meth)acrylate obtained by the reaction of polyisocyanate and hydroxyacryl(meth)acrylate; polyester di(meth)acrylate obtained by the reaction of polyester resin and (meth)acrylic acid; and polyether di(meth)acrylate obtained by the reaction of polyester resin and (meth)acrylic acid.
Claim 11
Dependent Claim
29 words
The method as claimed in claim 1 or claim 2, wherein viscosity increasing materials or additives are added to either the coating material, the liquid material, or to both.
Claim 12
Dependent Claim
38 words
The method as claimed in claim 10, wherein said viscosity increasing materials are selected from the group consisting of polymers of said vinyl monomer, copolymers of said vinyl monomer and a monomer copolymerizable therewith; synthetic resins; and rubbers.
Claim 13
Dependent Claim
33 words
The method as claimed in claim 10, wherein said additives are selected from the group consisting of fillers, plasticizers; anti-aging agents, antimicrobial agents, antioxidants, UV light absorbers, antiozonants, thixotropic agents and rust inhibitors.
Claim 14
Dependent Claim
15 words
The method as claimed in claim 1, wherein said polymerization initiator is an organic peroxide.
Claim 15
Dependent Claim
24 words
The method as claimed in claim 13, wherein said organic peroxide is selected from the group consisting of ketone peroxide, hydroperoxide; and diacyl peroxide.
Claim 16
Dependent Claim
45 words
The method as claimed in claim 1, wherein said polymerization initiator is employed in an amount of from 0.01 to 10 parts by weight based on 100 parts by weight of the vinyl monomer and/or vinyl group-containing oligomer in the coating material or liquid material.
Claim 17
Dependent Claim
45 words
The metod as claimed in claim 1, wherein said polymerization initiator is employed in an amount of from 0.1 to 5 parts by weight based on 100 parts by weight of the vinyl monomer and/or vinyl group-containing oligomer in the coating material or liquid material.
Claim 18
Dependent Claim
16 words
The method as claimed in claim 1, wherein the polymerization initiator additionally contains a polymerization inhibitor.
Claim 19
Dependent Claim
33 words
The method as claimed in claim 17, wherein said polymerization inhibitor is selected from the group consisting of hydroquinone, hydroquinone monomethyl ether, methyl hydroquinone, p-benzoquinone, catechol, phenoazine picrate, A-butyl catechol, 2-butyl-4-hydroxyanisole and 2,6-di-t-butyl-p-cresol.
Claim 20
Dependent Claim
47 words
The method as claimed in claim 1, wherein said polymerization accelerator is selected from at least one member of the group consisting of dimethyl aniline, dimethyl-p-toluidine, diethyl-p-toluidine, diisopropyl-p-toluidine, cobalt naphthenate, copper napthenate, zinc napthenate, thiourea, acetylthiourea, sodium ascorbate, a condensate of n-butyl aldehyde and aniline, vanadium pentoxide.
Claim 21
Dependent Claim
35 words
The method as claimed in claim 2, wherein said self-supporting material is selected from the group consisting of a plastic film, a plastic sheet, a rubber sheet, a foamed sheet, and a composite material thereof.
Claim 22
Dependent Claim
28 words
The method as claimed in claim 1, wherein said liquid material is applied to at least one of the covering material and the metal surface or defective area.
References Cited (Backward Citations)
US4439291A
Cited
US4373077A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-04-08 | 1988-10-08 | 1989-04-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-04-08 | 1992-10-08 | 1993-04-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-04-08 | 1996-10-08 | 1997-04-09 | $7700.00 | Window Closed / Lapsed |