US4509984A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for preparing tire curing bladder lubricant
Assignee: Goodyear Tire and Rubber Co
•
Filing: 1983-02-07
•
Granted: 1985-04-09
•
Expires: 2003-02-07
Abstract
Abstract Method for preparing a lubricant composition comprised of clay, polydimethylsiloxane of required viscosity range, poly(ethylene glycol and/or propylene glycol) of required molecular weight range and surfactant.
Inventors
- 👤 Robert F. Scheiderich
- 👤 Louis F. Comper
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 15:49
CPC Classifications
B; B29; B29D; B29D30/00; B29D30/06; B29D30/0601; B29D30/0654; B29C; B29C33/00; B29C33/56; B29C33/60; B29C33/62; B29D2030/0655; C; C10; C10M; C10M2201/00; C10M2201/02; C10M2201/10; C10M2201/102; C10M2201/103; C10M2207/00; C10M2207/10; C10M2207/14; C10M2207/141; C10M2209/00; C10M2209/10; C10M2209/103; C10M2209/104; C10M2209/105; C10M2229/00; C10M2229/04; C10M2229/041; C10N; C10N2020/00; C10N2020/01
Claims Analysis
Total Claims: 2
Claim 1
Independent Claim
213 words
A method of preparing an aqueous-based lubricant composition which consists essentially of: (A) mixing under high shear mixing conditions about 10 to about 40 parts by weight bentonite clay having a mesh size in the range of about 100 to about 500 U.S. standard sieve size with about 500 to about 1500 parts by weight water until the mixture thickens where said water is preheated to a temperature in the range of 50° C. to about 85° C. prior to mixing said clay therewith (B) mixing therewith while maintaining the mixture temperature in the range of about 20° C. to about 95° C., about 15 to about 45 parts by weight polydimethylsiloxane characterized by having a viscosity in the range of about 40,000 to about 120,000 centistokes at 25° C., about 12 to about 36 parts by weight of at least one of polyethylene glycol and polypropylene glycol having a molecular weight in the range of about 1500 to about 2500, and a surfactant for said polydimethylsiloxane and polyglycol and (C) optionally mixing therewith about 2 to about 10 parts by weight additional surfactant; about 2 to about 8 parts by weight corrosion inhibitor; about 0.2 to about 1 part by weight defoamer; and about 2 to about 10 parts by weight stabilizer.
Claim 2
Independent Claim
213 words
A method of preparing an aqueous-based lubricant composition which consists essentially of: (A) mixing under high shear mixing conditions about 10 to about 40 parts by weight bentonite clay having a mesh size in the range of about 100 to about 500 U.S. standard sieve size with about 500 to about 1500 parts by weight water until the mixture thickens where said water is preheated to a temperature in the range of 50° C. to about 85° C. prior to mixing said clay therewith (B) mixing therewith while maintaining the mixture temperature in the range of about 20° C. to about 95° C., about 15 to about 45 parts by weight polydimethylsiloxane characterized by having a viscosity in the range of about 40,000 to about 120,000 centistokes at 25° C., about 12 to about 36 parts by weight of at least one of polyethylene glycol and polypropylene glycol having a molecular weight in the range of about 1500 to about 2500, and a surfactant for said polydimethylsiloxane and polyglycol and (C) optionally mixing therewith about 2 to about 10 parts by weight additional surfactant; about 2 to about 8 parts by weight corrosion inhibitor; about 0.2 to about 1 part by weight defoamer; and about 2 to about 10 parts by weight stabilizer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-04-08 | 1988-10-08 | 1989-04-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-04-08 | 1992-10-08 | 1993-04-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-04-08 | 1996-10-08 | 1997-04-09 | $7700.00 | Window Closed / Lapsed |