Polymethyl methacrylate compatible silicon dioxide complexing agent
Assignee: HP Inc
•
Filing: 1984-03-08
•
Granted: 1985-04-02
•
Expires: 2004-03-08
Abstract
Abstract An etching solution for the dissolution of silicon dioxide through a portable conformable mask, with PMMA as the etch stop layer, has been developed which eliminates resist lifting and non-uniform lateral etching, thereby providing the improved oxide edge definitions required for 1 micron line geometries in VLSI chips.
Inventors
- 👤 Keith G. Bartlett
- 👤 Mary A. Caolo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 22:40
CPC Classifications
H; H10; H10P; H10P50/00; H10P50/20; H10P50/28; H10P50/282; H10P50/283; C; C03; C03C; C03C15/00; Y; Y10; Y10S; Y10S438/00; Y10S438/942; Y10S438/948
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
39 words
An etchant solution for the dissolution of silicon dioxide, comprising: an aqueous solution of ammonium fluoride from about 1% to about 20% by volume; and citric acid from about 10 to about 200 grams per liter of aqueous solution.
Claim 2
Dependent Claim
39 words
An etchant solution for the dissolution of silicon dioxide, comprising: an aqueous solution of ammonium fluoride from about 1% to about 20% by volume; and citric acid from about 10 to about 200 grams per liter of aqueous solution.
Claim 3
Independent Claim
49 words
A method of dissolving silicon dioxide, which comprises the step of exposing the silicon dioxide to an etchant solution comprising: an aqueous solution of ammonium fluoride from about 1% to about 20% by volume; and citric acid from about 10 to about 200 grams per liter of aqueous solution.
Claim 4
Independent Claim
49 words
A method of dissolving silicon dioxide, which comprises the step of exposing the silicon dioxide to an etchant solution comprising: an aqueous solution of ammonium fluoride from about 1% to about 20% by volume; and citric acid from about 10 to about 200 grams per liter of aqueous solution.
Claim 5
Independent Claim
63 words
A method of dissolving silicon dioxide through a portable conformable resist mask, with a PMMA as the etch stop layer which comprises the step of exposing the silicon dioxide to an etchant solution comprising: an aqueous solution of ammonium fluoride from about 1% to about 20% by volume; and citric acid from about 10 to about 200 grams per liter of aqueous solution.
Claim 6
Independent Claim
63 words
A method of dissolving silicon dioxide through a portable conformable resist mask, with a PMMA as the etch stop layer which comprises the step of exposing the silicon dioxide to an etchant solution comprising: an aqueous solution of ammonium fluoride from about 1% to about 20% by volume; and citric acid from about 10 to about 200 grams per liter of aqueous solution.
Claim 7
Dependent Claim
215 words
An improved method of photoetching a silicon dioxide or doped silicon dioxide using a photosensitive mask of the portable conformal mask type wherein a first resist is deposited on the substrate to produce a bottom resist layer having a substantially planar top surface, a second resist is deposited as a top resist layer producing a multilayer substrate coating having the bottom resist layer, producing a multilayer substrate coating having the bottom resist layer sandwiched between the silicon dioxide and the top resist layer, the top resist layer is exposed to light in a range in which the second resist is insensitive, said light having been passed through a mask to expose only selected portions of the top resist layer, the top layer is developed to produce a portable conformable mask, and the layers of the substrate coating other than the top resist layer are processed to replicate the pattern of this portable conformable mask into such layers and placing the silicon dioxide in an etchant bath to dissolve the silicon dioxide where it is left exposed by the mask, the improvement comprising: the etchant bath comprising: an aqueous solution of ammonium fluoride from about 1% to about 20% by volume; and citric acid from about 10 to about 200 grams per liter of aqueous solution.
Claim 8
Dependent Claim
215 words
An improved method of photoetching a silicon dioxide or doped silicon dioxide using a photosensitive mask of the portable conformal mask type wherein a first resist is deposited on the substrate to produce a bottom resist layer having a substantially planar top surface, a second resist is deposited as a top resist layer producing a multilayer substrate coating having the bottom resist layer, producing a multilayer substrate coating having the bottom resist layer sandwiched between the silicon dioxide and the top resist layer, the top resist layer is exposed to light in a range in which the second resist is insensitive, said light having been passed through a mask to expose only selected portions of the top resist layer, the top layer is developed to produce a portable conformable mask, and the layers of the substrate coating other than the top resist layer are processed to replicate the pattern of this portable conformable mask into such layers and placing the silicon dioxide in an etchant bath to dissolve the silicon dioxide where it is left exposed by the mask, the improvement comprising: the etchant bath comprising: an aqueous solution of ammonium fluoride from about 1% to about 20% by volume; and citric acid from about 10 to about 200 grams per liter of aqueous solution.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-04-01 | 1988-10-01 | 1989-04-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-04-01 | 1992-10-01 | 1993-04-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-04-01 | 1996-10-01 | 1997-04-02 | $7700.00 | Window Closed / Lapsed |