US4507447A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Polyurethane adhesive compositions containing oxyacid of phosphorus and silane coupling agent
Assignee: Takeda Pharmaceutical Co Ltd
•
Filing: 1983-09-07
•
Granted: 1985-03-26
•
Expires: 2003-09-07
Abstract
Abstract A polyurethane adhesive composition, which comprises an organic polyisocyanate, a polyol, an oxyacid of phosphorus or a derivative thereof, an epoxy resinand a silane coupling agent. The polyurethane adhesive composition, when used as an adhesive for packaging materials for food, provides the bond showing outstandingly excellent adhesion strength, heat resistance and hot-water resistance between metal foil such as aluminum foil and films of plastics such as polyethylene, polypropylene, nylon and polyethylene terephthalate etc.
Inventors
- 👤 Kyuya Yamazaki
- 👤 Sachio Igarashi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 13:12
CPC Classifications
C; C09; C09J; C09J175/00; C09J175/04; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/30; C08G18/38; C08G18/3878; C08G18/3882; C08G18/40; C08G18/4009; C08G18/4045; C08K; C08K5/00; C08K5/49; C08K5/51; C08K5/52; C08K5/54; C08L; C08L2666/00; C08L2666/28; C08L2666/40; C08L2666/44
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
112 words
A polyurethane adhesive composition, which comprises an organic polyisocyanate, a polyol, about 0.01 to 10 weight percent based on the total adhesive composition of an oxyacid of phosphorus or a derivative thereof, about 1 to 50 weight percent based on the total adhesive composition of an epoxy resin and about 0.05 to 20 weight percent based on the total adhesive composition of a silane coupling agent and wherein the ratio of the number of the NCO groups of the organic polyisocyanate to the number of active hydrogen groups of the polyol, the oxyacid of phosphorus or the derivative thereof and the epoxy resin is in the range of about 0.4 to 20.
Claim 2
Dependent Claim
112 words
A polyurethane adhesive composition, which comprises an organic polyisocyanate, a polyol, about 0.01 to 10 weight percent based on the total adhesive composition of an oxyacid of phosphorus or a derivative thereof, about 1 to 50 weight percent based on the total adhesive composition of an epoxy resin and about 0.05 to 20 weight percent based on the total adhesive composition of a silane coupling agent and wherein the ratio of the number of the NCO groups of the organic polyisocyanate to the number of active hydrogen groups of the polyol, the oxyacid of phosphorus or the derivative thereof and the epoxy resin is in the range of about 0.4 to 20.
Claim 3
Dependent Claim
67 words
A polyurethane adhesive composition claimed in claim 1, which is obtained by reacting a mixed solution of the polyol, the oxyacid of phosphorus or the derivative thereof, the epoxy resin and the silane coupling agent with the organic polyisocyanate, wherein the NCO/(the active hydrogen group (H) of the polyol, the oxyacid of phosphorus or the derivative thereof and the epoxy resin) ratio is about 1.5 to 20.
Claim 4
Dependent Claim
69 words
A polyurethane adhesive composition claimed in claim 1, wherein a mixture of the polyol, the oxyacid of phosphorus or the derivative thereof, the epoxy resin and the silane coupling agent constitutes the principal component and the organic polyisocyanate is a curing agent, the NCO/(the active hydrogen group (H) of the polyol, the oxyacid of phosphorus or the derivative thereof and the epoxy resin) ratio being about 0.4 to 10.
Claim 5
Dependent Claim
50 words
A polyurethane adhesive composition claimed in claim 1, wherein the silane coupling agent is a compound having the structural formula: R--Si.tbd.(X).sub.3 or R--Si.tbd.(R')(X).sub.2 wherein R is an organic group having a vinyl, epoxy, amino, imino or mercapto group; R' is a C1-8 alkyl group; X is methoxy, ethoxy or chlorine.
Claim 6
Dependent Claim
15 words
A polyurethane adhesive composition claimed in claim 4, wherein the silane coupling agent is N-(diethoxymethylsilylpropyl)ethylenediamine.
Claim 7
Dependent Claim
15 words
A polyurethane adhesive composition claimed in claim 4, wherein the silane coupling agent is γ-glycidoxypropyltrimethoxysilane.
Claim 8
Dependent Claim
15 words
A polyurethane adhesive composition claimed in claim 4, wherein the silane coupling agent is vinyltriethoxysilane.
Claim 9
Dependent Claim
15 words
A polyurethane adhesive composition claimed in claim 4, wherein the silane coupling agent is vinyltrichlorosilane.
Claim 10
Dependent Claim
15 words
A polyurethane adhesive composition claimed in claim 4, wherein the silane coupling agent is γ-mercaptopropyltrimethoxysilane.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-03-25 | 1988-09-24 | 1989-03-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-03-25 | 1992-09-24 | 1993-03-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-03-25 | 1996-09-24 | 1997-03-26 | $7700.00 | Window Closed / Lapsed |