Photographic material with a temporary barrier layer comprising a chill-gelable polymer

Claim 2

A photographic element having thereon at least one dye imaging layer, a neutralizing layer, and a chill-gelable temporary barrier layer separating said dye imaging reactant layer from said neutralizing layer, said chill-gelable barrier layer comprising a chill-gelable polymer comprising about 30 to 97 weight percent of polymerized N-alkyl-substituted acrylamide, about 3 to about 25 weight percent of polymerized crosslinking monomer having at least two addition-polymerizable groups per molecule and about 0 to about 60 weight percent of one or more other polymerized addition-polymerizable monomers, said polymer having a solubility parameter δ from about 13 to 16 at 25° C. with the proviso that said monomers comprise less than 5 weight percent of cationic monomers, less than 15 weight percent of free acid monomers, and less than 3 weight percent of metal or ammonium salts of acid monomers.

Claim 3

The photographic element of claim 1 wherein said polymer has recurring units having the structure: ##STR10## wherein Z is a linking group; R and R 4 are individually hydrogen or methyl; R 1 represents recurring units in the polymer of one or more addition polymerizable comonomers; R 2 is alkyl of about 1 to 6 carbon atoms or aryl; R 3 is hydrogen, aryl, or alkyl of about 1 to 6 carbon atoms; R 5 is H or CH 3 ; n is 1 or 2; x represents about 30 to 97 weight percent; y represents about 3 to 25 weight percent; and z represents about 0 to 30 weight percent with the proviso that said monomers comprise less than 5 weight percent of polymer that is derived from cationic monomers, less than 15 weight percent of said polymer that is derived from free acid monomers, and less than 3 weight percent of said polymer that is derived from monomers that contain metal or ammonium salts of acid monomers.

Claim 4

In a photographic element comprising a support, at least one silver halide layer, at least one dye imaging layer, at least one neutralizing layer, and a temporary barrier layer separating said dye imaging layer from said neutralizing layer, the improvement wherein said barrier layer is chill-gelable and comprises a chill-gelable polymer comprising about 30 to 97 weightpercent of polymerized N-alkyl-substituted acrylamide, about 3 to about 25 weight percent of polymerized crosslinking monomer having at least two addition-polymerizable groups per molecule and about 0 to about 60 weight percent of one or more other polymerized addition-polymerizable monomers, said polymer having a solubility parameter δ from about 13 to 16 at 25° C. with the proviso that said monomers comprise less than 5 weight percent of cationic monomers less than 15 weight percent of free acid monomers, and less than 3 weight percent of metal or ammonium salts of acid monomers.

Claim 5

In a photographic element comprising a support, at least one silver halide layer, at least one dye imaging layer, at least one neutralizing layer, and a temporary barrier layer separating said dye imaging layer from said neutralizing layer, the improvement wherein said barrier layer is chill-gelable and comprises a chill-gelable polymer comprising about 30 to 97 weightpercent of polymerized N-alkyl-substituted acrylamide, about 3 to about 25 weight percent of polymerized crosslinking monomer having at least two addition-polymerizable groups per molecule and about 0 to about 60 weight percent of one or more other polymerized addition-polymerizable monomers, said polymer having a solubility parameter δ from about 13 to 16 at 25° C. with the proviso that said monomers comprise less than 5 weight percent of cationic monomers less than 15 weight percent of free acid monomers, and less than 3 weight percent of metal or ammonium salts of acid monomers.

Claim 6

The photographic element of claim 3 wherein said polymer has recurring units having the structure: ##STR11## wherein Z is a linking group; R and R 4 are individually hydrogen or methyl; R 1 represents recurring units in the polymer of one or more addition polymerizable comonomers; R 2 is alkyl of about 1 to 6 carbon atoms or aryl; R 3 is hydrogen, aryl, or alkyl of about 1 to 6 carbon atoms; R 5 is H or CH 3 ; n is 1 or 2; x represents about 30 to 97 weight percent; y represents about 3 to 25 weight percent; and z represents about 0 to 30 weight percent with the proviso that said monomers comprise less than 5 weight percent of polymer that is derived from cationic monomers, less than 15 weight percent of said polymer that is derived from free acid monomers, and less than 3 weight percent of said polymer that is derived from monomers that contain metal or ammonium salts of acid monomers.

Claim 7

The photographic element of claim 4 wherein Z is selected from the group consisting of alkylenebis(iminocarbonyl), alkylenebis(oxycarbonyl), and arylene.

Claim 8

The photographic element of claim 3 wherein the N-alkyl-substituted acrylamide is isopropylacrylamide.

Claim 9

The photographic element of claim 3 wherein said polymer has a molecular weight of from about 100,000 to 1,000,000.

Claim 10

The photographic element of claim 3 wherein said polymer is poly(N-isopropyl)acrylamide(co-2-hydroxyethyl acrylate-co-N,N'-methylenebisacrylamide) (70:20:10 by weight).

Claim 11

The photographic element of claim 8 wherein the weight ratio is 80:10:10.

Claim 12

In a photographic element comprising a support, at least one silver halide emulsion layer, a dye image-providing layer, a dye image-receiving layer, and a neutralizing layer, said element containing a temporary barrier layer having a negative activation energy and being located between said neutralizing layer and said silver halide emulsion layer, said neutralizing layer providing a pH of 11 or less to the silver halide emulsion layer, the improvement wherein said barrier layer is chill-gelable and comprises a chill-gelable polymer comprising about 30 to 97 weight percent of polymerized N-alkyl-substituted acrylamide, about 3 to about 25 weight percent of polymerized crosslinking monomer having at least two addition-polymerizable groups per molecule and about 0 to about 60 weight percent of one or more other polymerized addition-polymerizable monomers, said polymer having a solubility parameter δ from about 13 to 16 at 25° C. with the proviso that said monomers comprise less than 5 weight percent of cationic monomers, less than 15 weight percent of free acid monomers, and less than 3 weight percent of metal or ammonium salts of acid monomers.

Claim 13

In a photographic element comprising a support, at least one silver halide emulsion layer, a dye image-providing layer, a dye image-receiving layer, and a neutralizing layer, said element containing a temporary barrier layer having a negative activation energy and being located between said neutralizing layer and said silver halide emulsion layer, said neutralizing layer providing a pH of 11 or less to the silver halide emulsion layer, the improvement wherein said barrier layer is chill-gelable and comprises a chill-gelable polymer comprising about 30 to 97 weight percent of polymerized N-alkyl-substituted acrylamide, about 3 to about 25 weight percent of polymerized crosslinking monomer having at least two addition-polymerizable groups per molecule and about 0 to about 60 weight percent of one or more other polymerized addition-polymerizable monomers, said polymer having a solubility parameter δ from about 13 to 16 at 25° C. with the proviso that said monomers comprise less than 5 weight percent of cationic monomers, less than 15 weight percent of free acid monomers, and less than 3 weight percent of metal or ammonium salts of acid monomers.

Claim 14

The photographic element of claim 10 wherein said polymer has recurring units having the structure: ##STR12## wherein Z is a linking group; R and R 4 are individually hydrogen or methyl; R 1 represents recurring units in the polymer of one or more addition polymerizable comonomers; R 2 is alkyl of about 1 to 6 carbon atoms or aryl; R 3 is hydrogen, aryl, or alkyl of about 1 to 6 carbon atoms; R 5 is H or CH 3 ; n is 1 or 2; x represents about 30 to 97 weight percent; y represents about 3 to 25 weight percent; and z represents about 0 to 30 weight percent with the proviso that said monomers comprise less than 5 weight percent of polymer that is derived from cationic monomers, less than 15 weight percent of said polymer that is derived from free acid monomers, and less than 3 weight percent of said polymer that is derived from monomers that contain metal or ammonium salts of acid monomers.

Claim 15

The photographic element of claim 11 wherein Z is selected from the group consisting of alkylenebis(iminocarbonyl), alkylenebis(oxycarbonyl), and arylene.

Claim 16

The photographic element of claim 10 wherein the N-alkyl-substituted acrylamide is isopropylacrylamide.

Claim 17

The photographic element of claim 10 wherein said polymer has a molecular weight of from about 100,000 to 1,000,000.

Claim 18

The photographic element of claim 10 wherein said polymer is poly(N-isopropyl)acrylamide(co-2-hydroxyethyl acrylate-co-N,N'-methylenebisacrylamide) (70:20:10 by weight).

Claim 19

The photographic element of claim 15 wherein the weight ratio is 80:10:10.

Claim 20

In a photographic film unit comprising: (a) a support having thereon at least one photosensitive silver halide emulsion layer having associated herewith a dye-image-providing layer; (b) a dye image-receiving layer; (c) alkaline processing composition and means for discharging same within said film unit in contact with said photosensitive layer; (d) a neutralizing layerfo rneutralizing said alkaline processing composition; and (e) a barrier layer having a negative activation energy of penetration by an aqueous alkaline solution, and which is permeable by said alkaline processing composition after a predetermined time located between said neutralizing layer and said photosensitive silver halide emulsion, said film unit containing a silver halide developing agent, said neutralizing layer providing a pH of 11 or less to the silver halide emulsion layer upon breakdown of said barrier layer, the improvement wherein said barrier layer is chill-gelable and comprises a chill gelable polymer comprising about 30 to 97 weight percent of polymerized N-alkyl-substituted acrylamide, about 3 to about 25 weight percent of polymerized crosslinking monomer having at least two addition-polymerizable groups per molecule and about 0 to about 60weight percent of one or more other polymerized addition-polymerizable monomers, said polymer having a solubility parameter δ from about 13 to 16 at 25° C. with the proviso that said monomers comprise less than 5 weight percent of cationic monomers, less than 15 weight percent of free acid monomers, and less than 3 weight percent of metal or ammonium salts of acid monomers.

Claim 21

In a photographic film unit comprising: (a) a support having thereon at least one photosensitive silver halide emulsion layer having associated herewith a dye-image-providing layer; (b) a dye image-receiving layer; (c) alkaline processing composition and means for discharging same within said film unit in contact with said photosensitive layer; (d) a neutralizing layerfo rneutralizing said alkaline processing composition; and (e) a barrier layer having a negative activation energy of penetration by an aqueous alkaline solution, and which is permeable by said alkaline processing composition after a predetermined time located between said neutralizing layer and said photosensitive silver halide emulsion, said film unit containing a silver halide developing agent, said neutralizing layer providing a pH of 11 or less to the silver halide emulsion layer upon breakdown of said barrier layer, the improvement wherein said barrier layer is chill-gelable and comprises a chill gelable polymer comprising about 30 to 97 weight percent of polymerized N-alkyl-substituted acrylamide, about 3 to about 25 weight percent of polymerized crosslinking monomer having at least two addition-polymerizable groups per molecule and about 0 to about 60weight percent of one or more other polymerized addition-polymerizable monomers, said polymer having a solubility parameter δ from about 13 to 16 at 25° C. with the proviso that said monomers comprise less than 5 weight percent of cationic monomers, less than 15 weight percent of free acid monomers, and less than 3 weight percent of metal or ammonium salts of acid monomers.

Claim 22

The photographic film unit of claim 17 wherein: (a) said dye-image receiving layer is located between said support and said silver halide emulsion layer; and (b) said film unit also includes a transparent cover sheet over the layer outermost from said support.

Claim 23

The film unit of claim 18 wherein said transparent cover sheet contains in order, said neutralizing layer and said barrier layer.

Claim 24

The film unit of claim 18 wherein said discharging means is a rupturable container containing said alkaline agent, said container being so positioned during processing of said film unit that a compressive force applied to said container will effect a discharge of the container's contents between said cover sheet and the outermost layer of said photosensitive element.

Claim 25

The film unit of claim 17 comprising: (a) a photosensitive element comprising a transparent support having thereon the following layers in sequence: an image-receiving layer; an alkaline solution-permeable, light-reflective layer; an alkaline solution-permeable opaque layer; a red-sensitive silver halide emulsion layer having a ballasted redox cyan dye-releaser associated therewith; a green-sensitive silver halide emulsion having a ballasted redox magenta dye-releaser associated therewith; and a blue-sensitive silver halide emulsion layer having a ballasted redox yellow dye-releaser associated therewith; (b) a cover sheet superposed over said blue-sensitive silver halide emulsion layer and comprising a transparent support coated with said neutralizing layer and said barrier layer; and (c) a rupturable container containing an alkaline processing composition and an opacifying agent, said container being so positioned during processing of said film unit that a compressive force supplied to said container will effect a discharge of the container's contents between said cover sheet and said blue-sensitive silver halide emulsion layer.

Claim 26

The film unit of claim 17 wherein said dye image-receiving layer is located on one support and said photosensitive silver halide emulsion layer is located on another support.