Phenolic blast tube insulators for rocket motors
Assignee: Hercules LLC
•
Filing: 1983-02-03
•
Granted: 1985-03-12
•
Expires: 2003-02-03
Abstract
Abstract Phenolic insulators for blast tubes of rocket motors are disclosed. The insulators are rigid, low density bodies comprising 100 parts by weight crosslinked phenolic resin in which are dispersed finely divided inorganic particulate and fibrous reinforcement selected from carbon fiber, polyaramide pulp and combinations thereof. Compounding these rigid bodies is also disclosed, the compounding including forming a molding crumb containing the aforesaid ingredients.
Inventors
- 👤 Liles G. Herring
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 21:12
CPC Classifications
F; F02; F02K; F02K9/00; F02K9/08; F02K9/32; F02K9/34; F02K9/346; Y; Y10; Y10S; Y10S428/00; Y10S428/902; Y10S428/903; Y10T; Y10T428/00; Y10T428/13; Y10T428/1352; Y10T428/1372; Y10T428/25; Y10T428/254; Y10T428/259; Y10T428/29; Y10T428/2982; Y10T428/2991; Y10T428/30; Y10T442/00; Y10T442/60; Y10T442/699
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
89 words
A blast tube insulator for tactical rocket motor, said insulator having a density between about 0.050 and 0.57 pounds per cubic inch and being a rigid, molded body which consists essentially of: 100 parts by weight of a cured phenolic resin in which are dispersed particulates consisting of between about 10 and 60 parts by weight finely divided silica particulate and between about 40 and 120 parts by weight of fibrous reinforcement selected from the group consisting of polyaramide pulps, carbon fibers and combination of said fibers and pulps.
Claim 2
Dependent Claim
89 words
A blast tube insulator for tactical rocket motor, said insulator having a density between about 0.050 and 0.57 pounds per cubic inch and being a rigid, molded body which consists essentially of: 100 parts by weight of a cured phenolic resin in which are dispersed particulates consisting of between about 10 and 60 parts by weight finely divided silica particulate and between about 40 and 120 parts by weight of fibrous reinforcement selected from the group consisting of polyaramide pulps, carbon fibers and combination of said fibers and pulps.
Claim 3
Dependent Claim
17 words
The blast tube insulator in accordance with claim 1, wherein said fibrous reinforcement comprises said carbon fibers.
Claim 4
Dependent Claim
17 words
The blast tube insulator in accordance with claim 1, wherein said fibrous reinforcement comprises said polyaramide pulps.
Claim 5
Dependent Claim
89 words
A blast tube insulator for tactical rocket motors, said insulator having a density between about 0.053 and 0.054 pounds per cubic inch, and being a rigid molded body which consists essentially of; 100 parts by weight of a cured phenolic resin in which are dispersed particulates consisting of between about 10 and 30 parts by weight of finely divided silica particulate and between about 40 and 80 parts by weight of fibrous reinforcement selected from carbon fibers having a length in a range between about 4 and 8 millimeters.
Claim 6
Dependent Claim
89 words
A blast tube insulator for tactical rocket motors, said insulator having a density between about 0.053 and 0.054 pounds per cubic inch, and being a rigid molded body which consists essentially of; 100 parts by weight of a cured phenolic resin in which are dispersed particulates consisting of between about 10 and 30 parts by weight of finely divided silica particulate and between about 40 and 80 parts by weight of fibrous reinforcement selected from carbon fibers having a length in a range between about 4 and 8 millimeters.
Claim 7
Dependent Claim
72 words
A blast tube insulator for tactical rocket motors, said insulator having a density between about 0.052 and 0.053 pounds per cubic inch being a rigid molded body which consists essentially of: 100 parts by weight of a cured phenolic resin in which are dispersed particulates consisting of between about 30 and 50 parts by weight of finely divided silica particulate and between about 80 and 120 parts by weight of polyaramide pulp.
Claim 8
Dependent Claim
72 words
A blast tube insulator for tactical rocket motors, said insulator having a density between about 0.052 and 0.053 pounds per cubic inch being a rigid molded body which consists essentially of: 100 parts by weight of a cured phenolic resin in which are dispersed particulates consisting of between about 30 and 50 parts by weight of finely divided silica particulate and between about 80 and 120 parts by weight of polyaramide pulp.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-03-11 | 1988-09-10 | 1989-03-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-03-11 | 1992-09-10 | 1993-03-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-03-11 | 1996-09-10 | 1997-03-12 | $7700.00 | Window Closed / Lapsed |