Cured elastomers with improved high temperature tear strength
Assignee: EIDP Inc
•
Filing: 1984-01-06
•
Granted: 1985-03-05
•
Expires: 2004-01-06
Abstract
Abstract Blends of elastomers of chlorinated or chlorosulfonated polyethylene and ultra high molecular weight, i.e. at least one million, when cured with conventional curing systems for the chlorinated or chlorosulfonated polyethylene have higher tear strengths at temperatures of about 150° C. than do the unblended elastomers. The amount of polyethylene in the blend is 5 to 50 parts by weight per 100 parts by weight of elastomer. The blend, thus produced has a modulus (M 100 ) of greater than 1000 psi prior to curing.
Inventors
- 👤 Herbert F. McShane, Jr.
- 👤 Peter N. Plimmer
- 👤 Charles W. Stewart
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 17:50
CPC Classifications
C; C08; C08L; C08L23/00; C08L23/26; C08L23/28; C08L23/286; C08L23/32; C08L23/34; C08L23/02; C08L23/04; C08L23/06
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
118 words
A thermoset cured blend of (a) an elastomeric material selected from the class consisting of chlorinated polyethylene, and chlorosulfonated polyethylene and (b) polyethylene, and (c) a conventional curing system for elastomeric chlorinated polyethylene or elastomeric chlorosulfonated polyethylene said blend when cured having a tear strength at 150° C. greater than the tear strength of the unblended cured chlorinated polyethylene or chlorosulfonated polyethylene, said blend containing between 5 and 50 parts by weight of polyethylene per 100 parts by weight of chlorinated polyethylene or chlorosulfonated polyethylene, said polyethylene being a linear polymer of ethylene, having a molecular weight of at least one million, said blend having a room temperature 100 percent modulus of greater than 1000 psi (6.9 MPa).
Claim 2
Dependent Claim
118 words
A thermoset cured blend of (a) an elastomeric material selected from the class consisting of chlorinated polyethylene, and chlorosulfonated polyethylene and (b) polyethylene, and (c) a conventional curing system for elastomeric chlorinated polyethylene or elastomeric chlorosulfonated polyethylene said blend when cured having a tear strength at 150° C. greater than the tear strength of the unblended cured chlorinated polyethylene or chlorosulfonated polyethylene, said blend containing between 5 and 50 parts by weight of polyethylene per 100 parts by weight of chlorinated polyethylene or chlorosulfonated polyethylene, said polyethylene being a linear polymer of ethylene, having a molecular weight of at least one million, said blend having a room temperature 100 percent modulus of greater than 1000 psi (6.9 MPa).
Claim 3
Dependent Claim
13 words
The blend of claim 1 in which the elastomeric material is chlorosulfonated polyethylene.
Claim 4
Dependent Claim
88 words
A process for improving the high temperature tear strength of a cured elastomeric material selected from the class consisting of chlorinated polyethylene and chlorosulfonated polyethylene, which comprises blending between 5 to 50 parts by weight of linear polyethylene per 100 parts by weight of the elastomeric material, said polyethylene having a molecular weight of at least one million thus forming a blend having room temperature 100% modulus of at least 1000 psi (6.9 MPa), and then curing said blend with a conventional curing system for the elastomeric material.
Claim 5
Dependent Claim
88 words
A process for improving the high temperature tear strength of a cured elastomeric material selected from the class consisting of chlorinated polyethylene and chlorosulfonated polyethylene, which comprises blending between 5 to 50 parts by weight of linear polyethylene per 100 parts by weight of the elastomeric material, said polyethylene having a molecular weight of at least one million thus forming a blend having room temperature 100% modulus of at least 1000 psi (6.9 MPa), and then curing said blend with a conventional curing system for the elastomeric material.
Claim 6
Dependent Claim
13 words
The process of claim 3 in which the elastomeric material is chlorosulfonated polyethylene.
References Cited (Backward Citations)
US3641216A
Cited
US4141878A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-03-04 | 1988-09-03 | 1989-03-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-03-04 | 1992-09-03 | 1993-03-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-03-04 | 1996-09-03 | 1997-03-05 | $7700.00 | Window Closed / Lapsed |