Sintered apatite bodies and composites thereof
Assignee: Inax Corp
•
Filing: 1983-04-28
•
Granted: 1985-03-05
•
Expires: 2003-04-28
Abstract
Abstract There are provided a novel sintered apatite body and a novel sintered apatite-mineral fiber material composite. The crystals of the sintered apatite have fine dense crystalline structures comprising needle-like fine crystals and are entangled together, whereby the mechanical properties of the sintered apatite body or composite are markedly enhanced. The sintered body and composite wherein the apatite is hydroxyapatite are useful for bioceramic uses. The sintered apatite body or composite is produced by baking an apatite material alone or in contact with a reinforcing mineral fiber material in the presence of water under pressure at a temperature lower than 1000° C., and further at a temperature lower than the temperature causing deterioration of the fiber material in the case of the composite.
Inventors
- 👤 Seiichi Hatahira
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 08:27
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/447; C04B35/71; C04B35/78; C04B35/80; A; A61; A61F; A61F2/00; A61F2/02; A61F2/28; A61L; A61L27/00; A61L27/02; A61L27/12; A61L27/40; A61L27/42; A61L27/425; C04B35/622; C04B35/64; C08; C08K; C08K7/00; C08K7/02; C08K7/04; A61F2310/00; A61F2310/00005; A61F2310/00179; A61F2310/00293; Y; Y10; Y10S; Y10S428/00; Y10S428/902
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
100 words
A process for producing a sintered apatite body, which comprises baking an apatite powder material selected from the group consisting of hydroxyapatite, carbonate apatite, fluoroapatite, chloroapatite, precursor materials thereof, the mixtures thereof, in the presence of co-existing water in an amount of not more than about 25% by weight of the apatite material in addition to crystal water, under pressure of at least about 5 kg/cm 2 at a temperature of not higher than about 800° C. to substantially sinter the apatite material, the crystals of the sintered apatite having fine dense crystalline structures comprising needle-like fine crystals entangled together.
Claim 2
Dependent Claim
100 words
A process for producing a sintered apatite body, which comprises baking an apatite powder material selected from the group consisting of hydroxyapatite, carbonate apatite, fluoroapatite, chloroapatite, precursor materials thereof, the mixtures thereof, in the presence of co-existing water in an amount of not more than about 25% by weight of the apatite material in addition to crystal water, under pressure of at least about 5 kg/cm 2 at a temperature of not higher than about 800° C. to substantially sinter the apatite material, the crystals of the sintered apatite having fine dense crystalline structures comprising needle-like fine crystals entangled together.
Claim 3
Dependent Claim
65 words
The process according to claim 1, in which the apatite has the fundamental structure represented by the following formula and the atomic ratio of calcium to phosphorus in the apatite is in the range of about 4/3 to about 11/6; Ca.sub.10 (PO.sub.4).sub.6 Z.sub.m wherein, Z is selected from OH, CO 3 , F, Cl and mixtures thereof and m is a number satisfying atomic valences.
Claim 4
Dependent Claim
20 words
The process according to claim 1, in which the apatite material to be baked is sealed in a pressure-deformable vessel.
Claim 5
Dependent Claim
44 words
The process according to claim 2, in which a small amount of an inorganic non-phosphorus calcium compound is intimately mixed with an apatite material having the calcium/phosphorus ratio of less than 5/3 to adjust the Ca/P ratio of the apatite material to about 5/3.
Claim 6
Dependent Claim
38 words
The process according to claim 2, in which the apatite is hydroxyapatite wherein all or not less than about 90% of the substituent Z is OH group and the balance of Z if any is CO 3 group.
Claim 7
Dependent Claim
24 words
The process according to claim 5, in which the sintered apatite has open pore voids of about 3% to about 40% for bioceramic uses.
Claim 8
Dependent Claim
128 words
A process for producing a sintered apatite composite, which comprises baking a matrix amount of an apatite powder material selected from the group consisting of hydroxyapatite, carbonate apatite, fluoroapatite chloroapatite, precursor materials thereof, and mixtures thereof in contact with a reinforcing effective amount of reinforcing mineral fiber material under pressure of at least about 5 kg/cm 2 , in the presence of coexisting water in an amount of not more than about 25% by weight of the apatite material in addition to crystal water, at a temperature not higher than about 800° C. to substantially sinter the apatite material and lower than the temperature causing substantial deterioration of the fiber material, the crystals of the sintered apatite having fine dense crystalline structures comprising needle-like fine crystals entangled together.
Claim 9
Dependent Claim
128 words
A process for producing a sintered apatite composite, which comprises baking a matrix amount of an apatite powder material selected from the group consisting of hydroxyapatite, carbonate apatite, fluoroapatite chloroapatite, precursor materials thereof, and mixtures thereof in contact with a reinforcing effective amount of reinforcing mineral fiber material under pressure of at least about 5 kg/cm 2 , in the presence of coexisting water in an amount of not more than about 25% by weight of the apatite material in addition to crystal water, at a temperature not higher than about 800° C. to substantially sinter the apatite material and lower than the temperature causing substantial deterioration of the fiber material, the crystals of the sintered apatite having fine dense crystalline structures comprising needle-like fine crystals entangled together.
Claim 10
Dependent Claim
65 words
The process according to claim 7, in which the apatite has the fundamental structure represented by the following formula and the atomic ratio of calcium to phosphorus in the apatite is in the range of about 4/3 to about 11/6; Ca.sub.10 (PO.sub.4).sub.6 Z.sub.m wherein, Z is selected from OH, CO 3 , F, Cl and mixtures thereof and m is a number satisfying atomic valences.
Claim 11
Dependent Claim
19 words
The process according to claim 7, in which the material to be baked is sealed in a pressure-deformable vessel.
Claim 12
Dependent Claim
44 words
The process according to claim 8, in which a small amount of an inorganic non-phosphorus calcium compound is intimately mixed with an apatite material having the calcium/phosphorus ratio of less than 5/3 to adjust the Ca/P ratio of the apatite material to about 5/3.
Claim 13
Dependent Claim
38 words
The process according to claim 8, in which the apatite is hydroxyapatite wherein all or not less than about 90% of the substituent Z is OH group and the balance of Z if any is CO 3 group.
Claim 14
Dependent Claim
24 words
The process according to claim 11, in which the sintered apatite has open pore voids of about 3% to about 40% for bioceramic uses.
Claim 15
Dependent Claim
37 words
The process according to claim 12, in which the fiber material is selected from carbon fiber, silicon carbide fiber, mullite fiber, silica fiber, alumina fiber, apatite glass fiber, silicon nitride fiber, and mixtures thereof for bioceramic uses.
Claim 16
Dependent Claim
79 words
A sintered apatite-mineral fiber material composite which consists essentially of an effective amount of a reinforcing mineral fiber material and a matrix amount of sintered apatite in contact with the fiber material, said apatite being selected from hydroxyapatite, carbonate apatite, fluoroapatite, chloroapatite and mixtures thereof, wherein the crystals of the sintered apatite have fine dense crystalline structures comprising at least about 30% of needle-like fine crystals and are entangled together and wherein the fiber material is not substantially deteriorated.
Claim 17
Dependent Claim
79 words
A sintered apatite-mineral fiber material composite which consists essentially of an effective amount of a reinforcing mineral fiber material and a matrix amount of sintered apatite in contact with the fiber material, said apatite being selected from hydroxyapatite, carbonate apatite, fluoroapatite, chloroapatite and mixtures thereof, wherein the crystals of the sintered apatite have fine dense crystalline structures comprising at least about 30% of needle-like fine crystals and are entangled together and wherein the fiber material is not substantially deteriorated.
Claim 18
Dependent Claim
65 words
The composite according to claim 14, in which the apatite has the fundamental structure represented by the following formula and the atomic ratio of calcium to phosphorus in the apatite is in the range of about 4/3 to about 11/6; Ca.sub.10 (PO.sub.4).sub.6 Z.sub.m wherein, Z is selected from OH, CO 3 , F, Cl and mixtures thereof and m is a number satisfying atomic valences.
Claim 19
Dependent Claim
45 words
The composite according to claim 14, in which the amount of the fiber material is in the range of about 1% to about 50% by weight and the amount of the apatite material is in the range of about 99% to about 50% by weight.
Claim 20
Dependent Claim
34 words
The composite according to claim 14, in which the fiber material is in the form of short fibers, long fibers, fiber yarns, fiber strands, wooly fibers, whiskers, nonwoven or woven fabrics, and/or mixtures thereof.
Claim 21
Dependent Claim
41 words
The composite according to claim 14, in which the fiber material is selected from carbon fiber, mullite fiber, silicon carbide fiber, apatite glass fiber, glass fiber, silicon nitride fiber, silica fiber, alumina fiber, chemically inert metallic fiber materials, and mixtures thereof.
Claim 22
Dependent Claim
38 words
The composite according to claim 15, in which the apatite is hydroxyapatite wherein all or not less than about 90% of the substituent Z is OH group and the balance of Z if any is CO 3 group.
Claim 23
Dependent Claim
21 words
The composite according to claim 19, in which the sintered apatite has open pore voids of about 3% to about 40%.
Claim 24
Dependent Claim
12 words
The composite according to claim 20, in which the composite is biocompatible.
Claim 25
Dependent Claim
34 words
The composite according to claim 20, in which the fiber material is selected from carbon fiber, silicon carbide fiber, mullite fiber, silica fiber, alumina fiber, apatite glass fiber, silicon nitride fiber, and mixtures thereof.
Claim 26
Dependent Claim
12 words
The composite according to claim 22, in which the composite is biocompatible.
Claim 27
Dependent Claim
29 words
The composite according to claim 14, produced by baking an apatite powder material in contact with the fiber material under pressure of at least about 5 kg/cm 2 .
Claim 28
Dependent Claim
46 words
The composite according to claim 24, in which the baking was conducted in the presence of co-existing water of not more than about 25% by weight of the apatite material in addition to crystal water and at a temperature of not higher than about 800° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-03-04 | 1988-09-03 | 1989-03-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-03-04 | 1992-09-03 | 1993-03-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-03-04 | 1996-09-03 | 1997-03-05 | $7700.00 | Window Closed / Lapsed |