US4503010A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process of producing a compound material of chromium and copper
Assignee: Siemens AG
•
Filing: 1983-07-13
•
Granted: 1985-03-05
•
Expires: 2003-07-13
Abstract
Abstract In the method according to the invention, Cr powder is poured into a degased mold, which can be made of graphite. On this Cr powder a piece of low-oxygen copper is placed. Subsequently, the mold is closed with a porous cover, which can also be made of graphite. Then the mold is degased in a high-vacuum furnace at room temperature until a pressure of better than 10 -4 mb is reached. Thereafter, the furnace temperature is increased to as high as possible a temperature below the melting point of copper. This furnace temperature is maintained constant until an internal pressure in the furnace of better than 10 -4 mb is reached. Subsequently, without intermediate cooling, the furnace temperature is further increased slowly to a final value of 100 degrees K. to 200 degrees K. above the melting temperature of the copper. This temperature is then maintained until the porosity contained in the Cr powder is completely filled up by the liquid copper.
Inventors
- 👤 Horst Kippenberg
- 👤 Heinrich Haessler
- 👤 Manfred Huehnlein
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 08:01
CPC Classifications
B; B22; B22F; B22F3/00; B22F3/24; B22F3/26; H; H01; H01H; H01H1/00; H01H1/02; H01H1/0203; H01H1/0206
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
162 words
A method for producing a compound material of chromium and copper as contact material for medium voltage vacuum power swtiches, comprising the steps: (a) pouring Cr powder into a degased mold; (b) placing a piece of low-oxygen copper on the Cr powder; (c) closing the mold with a porous cover; (d) degasing the mold in a high-vacuum furnace at room temperature until a pressure of better than 10 -4 mb is reached; (e) increasing the furnace temperature to as high as possible a temperature below the melting point of copper; (f) maintaining the furnace temperature at a constant level until a constant internal pressure in the furnace of better than 10 -4 mb is reached; and (g) increasing further the furnace temperature, without intermediate cooling, to a final value of 100 degree K. to 200 degree K. above the melting point of copper and maintaining this temperature until the porosity contained in the Cr powder is completely filled up by liquid copper.
Claim 2
Independent Claim
162 words
A method for producing a compound material of chromium and copper as contact material for medium voltage vacuum power swtiches, comprising the steps: (a) pouring Cr powder into a degased mold; (b) placing a piece of low-oxygen copper on the Cr powder; (c) closing the mold with a porous cover; (d) degasing the mold in a high-vacuum furnace at room temperature until a pressure of better than 10 -4 mb is reached; (e) increasing the furnace temperature to as high as possible a temperature below the melting point of copper; (f) maintaining the furnace temperature at a constant level until a constant internal pressure in the furnace of better than 10 -4 mb is reached; and (g) increasing further the furnace temperature, without intermediate cooling, to a final value of 100 degree K. to 200 degree K. above the melting point of copper and maintaining this temperature until the porosity contained in the Cr powder is completely filled up by liquid copper.
Claim 3
Dependent Claim
17 words
The method according to claim 1, characterized in that the furnace temperature in step (e) is ##EQU3##
Claim 4
Dependent Claim
24 words
The method according to claim 1, characterized in that the pressure in steps (d) and (f) is in the range of 10 -5 mb.
Claim 5
Dependent Claim
21 words
The method according to claim 1, characterized in that the furnace temperature in step (f) is maintained for about one hour.
Claim 6
Dependent Claim
21 words
The method according to claim 1, characterized in that the temperature in step (g) is maintained for 20 to 30 minutes.
Claim 7
Dependent Claim
30 words
The method according to claim 1, characterized in that, when using alumino-thermally produced chromium, the Cr powder produced therefrom has a particle size distribution between 50 micron and 200 micron.
Claim 8
Dependent Claim
24 words
The method according to claim 6, characterized in that Cr powder having a particle size with fractions of at least 150 micron is used.
Claim 9
Dependent Claim
30 words
The method according to claim 1, characterized in that, when using electrolytically produced chromium, the Cr powder produced therefrom has a particle size distribution between 25 micron and 200 micron.
Claim 10
Independent Claim
17 words
The method according to one of claims 1 to 8, characterized in that a graphite-mold is used.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-03-04 | 1988-09-03 | 1989-03-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-03-04 | 1992-09-03 | 1993-03-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-03-04 | 1996-09-03 | 1997-03-05 | $7700.00 | Window Closed / Lapsed |