US4501875A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Polycarbonate from carbonyl halide, bischloroformate and dihydric phenol
Assignee: General Electric Co
•
Filing: 1982-08-23
•
Granted: 1985-02-26
•
Expires: 2002-08-23
Abstract
Abstract Novel carbonate polymers exhibiting improved processability comprised of the polymerized reaction products of (i) at least one dihydric phenol, (ii) a carbonyl halide carbonate precursor, and (iii) at least one specific bishaloformate. The bishaloformate is selected from bishaloformates represented by the general formulae ##STR1## wherein: X is independently selected from chlorine and bromine radicals; R is selected from alkylene radicals, cycloalkylene radicals, and divalent hydrocarbon radicals; R 3 and R 4 are independently selected from alkylene radicals; and Z is selected from the following divalent radicals ##STR2## the --(R 6 ) d --Ar--(R 7 ) e --radical wherein Ar represents a divalent mono-, di- or polynuclear aromatic residue, R 6 and R 7 are independently selected from alkylene radicals, and d and e are independently selected from zero and one, and a divalent organic aliphatic hetero non-cyclic radical containing at least one carbon atom and at least one hetero group selected from ##STR3## The instant polycarbonates are useful in making films, glazing sheets, fibers, and molded articles.
Inventors
- 👤 Victor Mark
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 13:05
CPC Classifications
C; C08; C08G; C08G64/00; C08G64/16; C08G64/1608
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
339 words
High molecular weight thermoplastic aromatic polycarbonate exhibiting improved processability consisting essentially of at least one recurring structural unit represented by the general formula ##STR51## and at least one recurring structural unit represented by the general formula ##STR52## or at least one recurring structural unit represented by the general formula ##STR53## and at least one recurring structural unit represented by the general formula ##STR54## derived from (i) a carbonyl halide carbonate precursor; (ii) at least one dihydric phenol; and (iii) at least one bishaloformate selected from bishaloformates represented by the general formulae ##STR55## wherein: Y is independently selected from halogen, monovalent hydrocarbon or monovalent hydrocarbonoxy radicals, Y' is independently selected from halogen, monovalent hydrocarbon or monovalent hydrocarbonoxy radicals, W is selected from divalent hydrocarbon radicals, ##STR56## n and n' are independently selected from whole numbers having a value of from 0 to 4 inclusive, m is either zero or one, X is independently selected from chlorine or bromine radicals, R is selected from alkylene radicals, cycloalkylene radicals, or divalent radicals represented by the general formula ##STR57## wherein R 1 and R 2 are independently selected from alkylene radicals, R 5 is independently selected from alkyl radicals, A represents a cycloalkylene radical, the letters b and c are independently selected from zero or one, with the proviso that the sum of b and c is at least one, and p represents a whole number having a value of from zero up to the number of replaceable hydrogen atoms present on A, R 3 and R 4 are independently selected from alkylene radicals, and Z is selected from the following divalent radicals ##STR58## the --(R 6 ) d --Ar--(R 7 ) e -- radical wherein Ar represents a divalent mono, di- or polynuclear aromatic residue, R 6 and R 7 are independently selected from alkylene radicals, and the letters d and e are independently selected from zero or one, or a divalent organic aliphatic hetero noncyclic radical containing at least one carbon atom and at least one hetero group selected from ##STR59##
Claim 2
Dependent Claim
339 words
High molecular weight thermoplastic aromatic polycarbonate exhibiting improved processability consisting essentially of at least one recurring structural unit represented by the general formula ##STR51## and at least one recurring structural unit represented by the general formula ##STR52## or at least one recurring structural unit represented by the general formula ##STR53## and at least one recurring structural unit represented by the general formula ##STR54## derived from (i) a carbonyl halide carbonate precursor; (ii) at least one dihydric phenol; and (iii) at least one bishaloformate selected from bishaloformates represented by the general formulae ##STR55## wherein: Y is independently selected from halogen, monovalent hydrocarbon or monovalent hydrocarbonoxy radicals, Y' is independently selected from halogen, monovalent hydrocarbon or monovalent hydrocarbonoxy radicals, W is selected from divalent hydrocarbon radicals, ##STR56## n and n' are independently selected from whole numbers having a value of from 0 to 4 inclusive, m is either zero or one, X is independently selected from chlorine or bromine radicals, R is selected from alkylene radicals, cycloalkylene radicals, or divalent radicals represented by the general formula ##STR57## wherein R 1 and R 2 are independently selected from alkylene radicals, R 5 is independently selected from alkyl radicals, A represents a cycloalkylene radical, the letters b and c are independently selected from zero or one, with the proviso that the sum of b and c is at least one, and p represents a whole number having a value of from zero up to the number of replaceable hydrogen atoms present on A, R 3 and R 4 are independently selected from alkylene radicals, and Z is selected from the following divalent radicals ##STR58## the --(R 6 ) d --Ar--(R 7 ) e -- radical wherein Ar represents a divalent mono, di- or polynuclear aromatic residue, R 6 and R 7 are independently selected from alkylene radicals, and the letters d and e are independently selected from zero or one, or a divalent organic aliphatic hetero noncyclic radical containing at least one carbon atom and at least one hetero group selected from ##STR59##
Claim 3
Dependent Claim
47 words
The polycarbonate of claim 1 consisting essentially of at least one recurring structural unit represented by the general formula ##STR60## and at least one recurring structural unit represented by the general formula ##STR61## and wherein said bishaloformate is selected from bishaloformates represented by the general formula ##STR62##
Claim 4
Dependent Claim
19 words
The polycarbonate of claim 2 wherein R represents an alkylene radical containing from 1 to about 30 carbon atoms.
Claim 5
Dependent Claim
19 words
The polycarbonate of claim 2 wherein R represents a cycloalkylene radical containing from 4 to about 30 carbon atoms.
Claim 6
Dependent Claim
64 words
The polycarbonate of claim 2 wherein R represents a divalent radical represented by the general formula ##STR63## wherein A represents a cycloalkylene residue containing from 4 to 16 carbon atoms, R 1 and R 2 are independently selected from alkylene radical containing from 1 to about 20 carbon atoms, and p is a whole number having a value of from 0 to 4 inclusive.
Claim 7
Dependent Claim
47 words
The polycarbonate of claim 1 consisting essentially of at least one recurring structural unit represented by the general formula ##STR64## and at least one recurring structural unit represented by the general formula ##STR65## and wherein said bishaloformate is selected from bishaloformates represented by the general formula ##STR66##
Claim 8
Dependent Claim
25 words
The polycarbonate of claim 6 wherein R 3 and R 4 are independently selected from alkylene radicals containing from 1 to about 30 carbon atoms.
Claim 9
Dependent Claim
45 words
The polycarbonate of claim 7 wherein R 6 and R 7 are independently selected from alkylene radicals containing from 1 to about 30 carbon atoms and Ar is selected from phenylene radicals, lower alkyl substituted phenylene radicals, biphenylene radicals, or lower alkyl substituted biphenylene radicals.
Claim 10
Dependent Claim
46 words
The polycarbonate of claim 7 wherein said divalent organic aliphatic hetero non-cyclic radical is selected from polyether residues represented by the general formula (--R.sup.8 --O--).sub.y wherein R 8 represents an alkylene radical and y is a number having a value of from 2 to about 350.
Claim 11
Dependent Claim
22 words
The polycarbonate of claim 9 wherein R 8 is selected from lower alkylene radicals containing from 1 to about 5 carbon atoms.
Claim 12
Dependent Claim
36 words
The polycarbonate of claim 1 wherein said bishaloformate reactant is present in an amount effective to improve the processability of the carbonate polymer but insufficient to substantially deleteriously affect the advantageous properties of said carbonate polymer.
Claim 13
Dependent Claim
32 words
The polycarbonate of claim 11 wherein said bishaloformate reactant is present in an amount of from about 0.1 to about 15 mole percent, based on the amount of dihydric phenol reactant present.
Claim 14
Dependent Claim
32 words
The polycarbonate of claim 12 wherein said bishaloformate reactant is present in an amount of from about 1 to about 10 mole percent, based on the amount of dihydric phenol reactant present.
Claim 15
Dependent Claim
20 words
The polycarbonate of claim 13 which contain admixed therewith a flame retardant amount of at least one flame retardant compound.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-02-26 | 1988-08-27 | 1989-02-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-02-26 | 1992-08-27 | 1993-02-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-02-26 | 1996-08-27 | 1997-02-26 | $7700.00 | Window Closed / Lapsed |