Method for hydrogenation of polymer
Assignee: Asahi Kasei Corp
•
Filing: 1984-01-06
•
Granted: 1985-02-26
•
Expires: 2004-01-06
Abstract
Abstract Selective hydrogenation of unsaturated double bonds in conjugated diene units of a conjugated diene polymer resulting from polymerization of copolymerization of a conjugated diene is effected by a method which comprises hydrogenating the conjugated diene polymer in an inert solvent in the presence of: (A) at least one bis-(cyclopentadienyl) titanium compound or (B) at least one hydrocarbon lithium compound containing at least one lithium atom in addition to (A) the aforementioned at least one bis-(cyclopentadienyl) titanium compound as a catalyst (providing that the presence of both the two components, (A) and (B), is essential where the conjugated diene polymer under treatment is other than a living polymer containing a lithium atom in the polymer chain thereof).
Inventors
- 👤 Yasushi Kishimoto
- 👤 Hideo Morita
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 04:50
CPC Classifications
C; C08; C08C; C08C19/00; C08C19/02
Claims Analysis
Total Claims: 32
Claim 1
Independent Claim
132 words
A method for the hydrogenation of a conjugated diene polymer in an inert organic solvent, said polymer being obtained by polymerization or copolymerization of a conjugated diene, which comprises effecting selective hydrogenation of unsaturated double bonds in the conjugated diene units of said conjugated diene polymer in the presense of: (A) at least one bis-(cyclopentadienyl)titanium compound represented by the formula: ##STR4## wherein R and R' denote the same or different moieties selected from the group consisting of C 1 -C 8 alkyl and alkoxy groups, C 6 -C 8 aryl, aryloxy, aralkyl and cycloalkyl groups, halogen groups, and carbonyl groups, and (B) at least one hydrocarbon lithium compound having at least one lithium atom ion as catalysts, with the molar ratio of lithium atoms to titanium atoms being from 0.1 to 100.
Claim 2
Independent Claim
132 words
A method for the hydrogenation of a conjugated diene polymer in an inert organic solvent, said polymer being obtained by polymerization or copolymerization of a conjugated diene, which comprises effecting selective hydrogenation of unsaturated double bonds in the conjugated diene units of said conjugated diene polymer in the presense of: (A) at least one bis-(cyclopentadienyl)titanium compound represented by the formula: ##STR4## wherein R and R' denote the same or different moieties selected from the group consisting of C 1 -C 8 alkyl and alkoxy groups, C 6 -C 8 aryl, aryloxy, aralkyl and cycloalkyl groups, halogen groups, and carbonyl groups, and (B) at least one hydrocarbon lithium compound having at least one lithium atom ion as catalysts, with the molar ratio of lithium atoms to titanium atoms being from 0.1 to 100.
Claim 3
Dependent Claim
18 words
A method according to claim 1, wherein said conjugated diene polymer is a polymer of 1,3-butadiene and/or isoprene.
Claim 4
Dependent Claim
28 words
A method according to claim 2, wherein a 1,2-vinyl bond is contained in a concentration of not less than 30% in the microstructure in said conjugated diene polymer.
Claim 5
Dependent Claim
23 words
A method according to claim 1, wherein said conjugated diene polymer is a copolymer of a conjugated diene and a vinyl-substituted aromatic hydrocarbon.
Claim 6
Dependent Claim
30 words
A method according to claim 4, wherein said copolymer is a block copolymer having at least one conjugated diene polymer block and at least one vinyl-substituted aromatic hydrocarbon polymer block.
Claim 7
Dependent Claim
32 words
A method according to claim 5, wherein the vinyl-substituted aromatic hydrocarbon polymer block content (a) in said block copolymer is 10 to 90% by weight based on the total amount of polymers.
Claim 8
Dependent Claim
36 words
A method according to claim 5, wherein the 1,2-vinyl bond content (b) of conjugated diene units in said block copolymer is 30 to 70% by weight based on the total amount of said conjugated diene units.
Claim 9
Dependent Claim
22 words
A method according to claim 1, wherein the number-average molecular weight of said conjugated diene polymer is about 1,000 to about 1,000,000.
Claim 10
Dependent Claim
28 words
A method according to claim 1, wherein said catalyst consists of at least one of the compounds of (A) and at least one of the compounds of (B).
Claim 11
Dependent Claim
31 words
A method according to claim 9, wherein said component (A) of said catalyst is at least one member selected from the group consisting of bis-(cyclopendadienyl)titanium dichloride, bis-(cyclopentadienyl)titanium dimethyl, and bis-(cyclopentadienyl)titanium dicarbonyl.
Claim 12
Dependent Claim
16 words
A method according to claim 9, wherein said component (B) of said catalyst is n-butyl lithium.
Claim 13
Dependent Claim
25 words
A method according to claim 9, wherein the molar ratio of said component (B) to said component (A) in said catalyst is 0.5 to 20.
Claim 14
Dependent Claim
32 words
A method according to claim 9, wherein the amount of said catalyst in terms of the amount of said component (A) is 0.05 to 20 millimoles per 100 g of said polymer.
Claim 15
Dependent Claim
27 words
A method according to claim 1, wherein said hydrogenation is carried out at 20° to 80° C. under hydrogen pressure of 2 to 30 kg/cm 2 .
Claim 16
Dependent Claim
28 words
A method according to claim 1, wherein said hydrogenation is effected on at least 50% of the unsaturated double bonds in said conjugated diene units of said polymer.
Claim 17
Dependent Claim
28 words
A method according to claim 15, wherein said hydrogenation is effected on at least 90% of the unsaturated double bonds in said conjugated diene units of said polymer.
Claim 18
Dependent Claim
46 words
A method according to any of claim 4, wherein said hydrogenation is effected selectively on at least 50% of the unsaturated double bonds in said conjugated diene units of said polymer and on not more than 10% of the vinyl-substituted aromatic hydrocarbon units of said polymer.
Claim 19
Dependent Claim
44 words
A method according to claim 17, wherein said hydrogenation is effected selectively on at least 90% of the unsaturated double bonds in said conjugated diene units of said polymer and on not more than 5% of the vinyl-substituted aromatic hydrocarbon units of said polymer.
Claim 20
Dependent Claim
36 words
A method according to claim 6, wherein the 1,2-vinyl bond content (b) of conjugated diene units in said block copolymer is 30 to 70% by weight based on the total amount of said conjugated diene units.
Claim 21
Dependent Claim
44 words
A method according to claim 5, wherein said hydrogenation is effected selectively on at least 50% of the unsaturated double bonds in said conjugated diene units of said polymer and on not more than 10% of the vinyl-substituted aromatic hydrocarbon units of said polymer.
Claim 22
Dependent Claim
44 words
A method according to claim 6, wherein said hydrogenation is effected selectively on at least 50% of the unsaturated double bonds in said conjugated diene units of said polymer and on not more than 10% of the vinyl-substituted aromatic hydrocarbon units of said polymer.
Claim 23
Dependent Claim
44 words
A method according to claim 7, wherein said hydrogenation is effected selectively on at least 50% of the unsaturated double bonds in said conjugated diene units of said polymer and on not more than 10% of the vinyl-substituted aromatic hydrocarbon units of said polymer.
Claim 24
Dependent Claim
44 words
A method according to claim 8, wherein said hydrogenation is effected selectively on at least 50% of the unsaturated double bonds in said conjugated diene units of said polymer and on not more than 10% of the vinyl-substituted aromatic hydrocarbon units of said polymer.
Claim 25
Dependent Claim
44 words
A method according to claim 9, wherein said hydrogenation is effected selectively on at least 50% of the unsaturated double bonds in said conjugated diene units of said polymer and on not more than 10% of the vinyl-substituted aromatic hydrocarbon units of said polymer.
Claim 26
Dependent Claim
62 words
A method according to claim 1, wherein said catalyst (B) is a conjugated diene living polymer or a living copolymer containing conjugated diene and vinyl-substituted aromatic hydrocarbon prepared by using an organic lithium compound as a polymerization catalyst and containing a lithium atom in the polymer chain thereof and having a number-average molecular weight in the range of from 1,000 to 1,000,000.
Claim 27
Dependent Claim
13 words
A method according to claim 25, wherein said catalyst (A) is bis-(cyclopentadienyl)titanium dichloride.
Claim 28
Dependent Claim
36 words
A method according to claim 26, wherein the amount of the catalyst is in the range of 0.005 to 10 millimoles/100 g of the amount of the polymer, computed as the amount of the catalyst (A).
Claim 29
Dependent Claim
20 words
A method according to claim 25, wherein the conjugated diene living polymer is a living polymer of 1,3-butadiene and/or isoprene.
Claim 30
Dependent Claim
22 words
A methd according to claim 25, wherein the conjugated diene living polymer is a living copolymer of 1,3-butadiene and/or isoprene and styrene.
Claim 31
Dependent Claim
63 words
A method according to claim 29, wherein the conjugated diene living copolymer has at least one 1,3-butadiene and/or isoprene block and at least one styrene block in which the styrene block content is in the range of 10 to 90% by weight, and the 1,2-vinyl bond content is in the range of 30 to 70% by weight in the 1,3-butadiene and/or isoprene units.
Claim 32
Dependent Claim
36 words
A method according to claim 30, wherein hydrogenation is effected selectively on at least 90% of the unsaturated double bonds in said 1,3-butadiene and/or isoprene units and on not more than 5% of the styrene units.
References Cited (Backward Citations)
US3700748A
Cited
US3696088A
Cited
US3700633A
Cited
US3993855A
Cited
US4057601A
Cited
US4049753A
Cited
US4174360A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-02-26 | 1988-08-27 | 1989-02-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-02-26 | 1992-08-27 | 1993-02-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-02-26 | 1996-08-27 | 1997-02-26 | $7700.00 | Window Closed / Lapsed |