Catalyst for reforming of methanol and process of preparing same
Assignee: Nissan Motor Co Ltd
•
Filing: 1983-12-30
•
Granted: 1985-02-26
•
Expires: 2003-12-30
Abstract
Abstract A catalyst for reforming of methanol to hydrogen and carbon monoxide, which is high in activity, selectivity and durability. The catalyst utilizes a granular or monolithic carrier of which the principal material is active alumina. First the carrier is coated with a mixture of cerium oxide and zirconium oxide, preferably by pyrolysis of a cerium salt and a zirconium salt applied to the carrier as a mixed solution. Then either Pt or Pd, or both, is deposited on the coated carrier preferably by pyrolysis of a platinum or palladium compound applied to the carrier as a solution. After that the nearly finished catalyst is treated with a solution of a reducing agent such as sodium boron hydride or hydrazine to render the deposited Pt and/or Pd substantially completely reduced.
Inventors
- 👤 Koji Masuda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 19:24
CPC Classifications
C; C01; C01B; C01B3/00; C01B3/02; C01B3/22; B; B01; B01J; B01J23/00; B01J23/38; B01J23/54; B01J23/56; B01J23/63; B01J37/00; B01J37/02; B01J37/024
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
61 words
A catalyst for the reforming of methanol to hydrogen and carbon monoxide, consisting essentially of: a carrier which comprises active alumina as a principal material thereof and is coated with a mixture consisting esssentially of cerium oxide and zirconium oxide; and at least one catalytic metal selected from the group consisting of platinum and palladium, which is deposited on said carrier.
Claim 2
Dependent Claim
61 words
A catalyst for the reforming of methanol to hydrogen and carbon monoxide, consisting essentially of: a carrier which comprises active alumina as a principal material thereof and is coated with a mixture consisting esssentially of cerium oxide and zirconium oxide; and at least one catalytic metal selected from the group consisting of platinum and palladium, which is deposited on said carrier.
Claim 3
Dependent Claim
38 words
A catalyst according to claim 1, wherein Ce in said cerium oxide amounts to 0.1 to 15% by weight of said carrier and Zr in said zirconium oxide amounts to 0.1 to 10% by weight of said carrier.
Claim 4
Dependent Claim
30 words
A catalyst according to claim 2, wherein the total content of said at least one catalytic metal in the catalyst is in the range from 0.1 to 1.0% by weight.
Claim 5
Dependent Claim
11 words
A catalyst according to claim 1, wherein said carrier is granular.
Claim 6
Dependent Claim
11 words
A catalyst according to claim 1, wherein said carrier is monolithic.
Claim 7
Dependent Claim
189 words
A process of preparing a catalyst for the reforming of methanol to hydrogen and carbon monoxide, the process consisting essentially of the steps of: (a) coating a carrier which comprises active alumina as a principal material thereof with a mixture consisting essentially of cerium oxide and zirconium oxide; (b) impregnating the coated carrier with an aqueous solution consisting essentially of at least one thermally decomposable compound of a catalytic metal selected from the group consisting of platinum compounds and palladium compounds; (c) after step (b), drying the carrier so as to reduce moisture content therein to a predetermined level; (d) baking the carrier impregnated with said solution in a steam atmosphere at a temperature between about 500° C. and 600° C. such that said compound adhering to the carrier is decomposed, thereby depositing at least one catalytic metal selected from the group consisting of platinum and palladium on the carrier; and (e) subjecting the carrier treated in step (d) to a reduction treatment which comprises immersing the carrier in a solution of a reducing agent, such that said catalytic metal deposited on the carrier is rendered substantially completely reduced.
Claim 8
Dependent Claim
189 words
A process of preparing a catalyst for the reforming of methanol to hydrogen and carbon monoxide, the process consisting essentially of the steps of: (a) coating a carrier which comprises active alumina as a principal material thereof with a mixture consisting essentially of cerium oxide and zirconium oxide; (b) impregnating the coated carrier with an aqueous solution consisting essentially of at least one thermally decomposable compound of a catalytic metal selected from the group consisting of platinum compounds and palladium compounds; (c) after step (b), drying the carrier so as to reduce moisture content therein to a predetermined level; (d) baking the carrier impregnated with said solution in a steam atmosphere at a temperature between about 500° C. and 600° C. such that said compound adhering to the carrier is decomposed, thereby depositing at least one catalytic metal selected from the group consisting of platinum and palladium on the carrier; and (e) subjecting the carrier treated in step (d) to a reduction treatment which comprises immersing the carrier in a solution of a reducing agent, such that said catalytic metal deposited on the carrier is rendered substantially completely reduced.
Claim 9
Dependent Claim
48 words
A process according to claim 6, wherein step (a) is performed such that Ce in said cerium oxide amounts to about 0.1 to about 15% by weight of the carrier and Zr in said zirconium oxide amounts to about 0.1 to about 10% by weight of the carrier.
Claim 10
Dependent Claim
37 words
A process according to claim 7, wherein the step (a) comprises the impregnating said carrier with an aqueous mixed solution of a cerium salt and a zirconium salt and baking the carrier impregnated with said mixed solution.
Claim 11
Dependent Claim
32 words
A process according to claim 8, wherein said baking in step (a) is performed in an oxidizing atmosphere at a temperature in the range from about 450° C. to about 600° C.
Claim 12
Dependent Claim
20 words
A process according to claim 8, wherein said cerium salt is cerium nitrate and said zirconium salt is zirconium oxynitrate.
Claim 13
Dependent Claim
33 words
A process according to claim 8, wherein step (b) is performed such that the total content of said catalytic metal in the catalyst is in the range from 0.1 to 1.0% by weight.
Claim 14
Dependent Claim
42 words
A process according to claim 11, wherein said solution in step (b) is selected from the group consisting of an aqueous solution of chloroplatinic acid, an aqueous solution of palladium chloride and an aqueous mixed solution of chloroplatinic acid and palladium chloride.
Claim 15
Dependent Claim
21 words
A process according to claim 11, wherein said solution of said reducing agent is an aqueous solution of sodium boron hydride.
Claim 16
Dependent Claim
27 words
A process according to claim 13, wherein the concentration of said sodium boron hydride in the solution is in the range from 0.5 to 5% by weight.
Claim 17
Dependent Claim
19 words
A process according to claim 11, wherein said solution of said reducing agent is an aqueous solution of hydrazine.
Claim 18
Dependent Claim
25 words
A process according to claim 15, wherein the concentration of said hydrazine in the solution is in the range from 1.0 to 5% by weight.
Claim 19
Dependent Claim
13 words
A process according to claim 11, wherein said carrier is grains of γ-alumina.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-02-26 | 1988-08-27 | 1989-02-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-02-26 | 1992-08-27 | 1993-02-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-02-26 | 1996-08-27 | 1997-02-26 | $7700.00 | Window Closed / Lapsed |