Foam rubber backings for composite materials having glass fiber substrates coated with PVC
Assignee: BASF SE
•
Filing: 1983-06-21
•
Granted: 1985-02-19
•
Expires: 2003-06-21
Abstract
Abstract Composite materials having glass fiber substrates and attached foam backings are useful in surface covering applications especially as resilient floor coverings. The glass fiber substrates are usually coated with a plastisol of polyvinyl chloride. Conventional foam rubber backings made from high solids SBR latex have poor adhesion to such coated substrates. However this problem may be overcome by using foam rubber backings made from a blend of SBR and NBR latices, which backings have excellent adhesion to these coated substrates.
Inventors
- 👤 Gerard Peltier
- 👤 Michel Longuet
- 👤 Charles A. Midgley
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 22:16
CPC Classifications
D; D06; D06N; D06N7/00; D06N7/0005; D06N7/006; Y; Y10; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249953; Y10T428/249982; Y10T428/249983; Y10T428/25; Y10T442/00; Y10T442/30; Y10T442/3325; Y10T442/3366; Y10T442/60; Y10T442/647; Y10T442/652
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
154 words
A composite material comprising a woven or non-woven glass fiber substrate which is coated with a gelled plastisol of a co- or homo-polymer of vinyl chloride having formed on one surface of said glass substrate and integrally bonded thereto during the process of its formation a foam formed from a compound comprising a latex having a bulk polymer composition comprising (a) from about 0 to about 30 percent by weight of a vinyl or vinylidene monoaromatic monomer which may be unsubstituted or substituted by a C 1-4 aliphatic radical or a bromine or chlorine radical; (b) from about 60 to about 85 percent by weight of a C 4-6 aliphatic conjugated diene monomer; and (c) from about 3 to about 40 percent by weight of a polar monomer selected from the group consisting of C 2-9 ethylenically unsaturated amide, aldehyde, carboxylic acid, and nitrile monomers, and C 1-6 esters of said carboxylic acid monomers.
Claim 2
Dependent Claim
154 words
A composite material comprising a woven or non-woven glass fiber substrate which is coated with a gelled plastisol of a co- or homo-polymer of vinyl chloride having formed on one surface of said glass substrate and integrally bonded thereto during the process of its formation a foam formed from a compound comprising a latex having a bulk polymer composition comprising (a) from about 0 to about 30 percent by weight of a vinyl or vinylidene monoaromatic monomer which may be unsubstituted or substituted by a C 1-4 aliphatic radical or a bromine or chlorine radical; (b) from about 60 to about 85 percent by weight of a C 4-6 aliphatic conjugated diene monomer; and (c) from about 3 to about 40 percent by weight of a polar monomer selected from the group consisting of C 2-9 ethylenically unsaturated amide, aldehyde, carboxylic acid, and nitrile monomers, and C 1-6 esters of said carboxylic acid monomers.
Claim 3
Dependent Claim
100 words
The composite according to claim 1 characterized in that the latex is a blend of a styrene-butadiene rubber latex with an acrylonitrile-butadiene rubber latex wherein the styrene-butadiene rubber latex has a polymer solids content of about 65 percent by weight and a styrene:butadiene weight ratio of from about 25:75 to about 35:65 and the acrylonitrile-butadiene rubber latex has a polymer solids content of about 56 percent by weight and an acrylonitrile:butadiene weight ratio of from about 30:70 to about 40:60, the weight ratio of the styrene-butadiene rubber latex to the acrylonitrile-butadiene rubber latex being from about 80:20 to about 50:50.
Claim 4
Dependent Claim
49 words
The composite according to claim 2 characterized in that the latex blend has a bulk polymer composition comprising (a) from about 15 to about 25 weight percent styrene; (b) from about 65 to about 75 weight percent butadiene; and (c) from about 5 to about 20 weight percent acrylonitrile.
Claim 5
Dependent Claim
37 words
The composite according to claim 3 characterized in that the latex blend has a bulk polymer composition comprising (a) about 18 weight percent styrene; (b) about 68 weight percent butadiene; and (c) about 14 weight percent acrylonitrile.
Claim 6
Independent Claim
195 words
A method of manufacturing a composite material comprising a woven or non-woven glass fiber substrate encapsulated with a gelled plastisol of a co- or homo-polymer of vinyl chloride coated on at least one surface with a rubber foam which comprises: (a) forming a compound comprising a latex having a polymeric content of at least about 60 percent by weight and having a bulk composition (i) from about 0 to 30 percent by weight of a vinyl or vinylidene monoaromatic monomer which may be unsubstituted or substituted by a C 1-4 aliphatic radical or a chlorine or bromine atom; (ii) from about 60 to about 85 percent by weight of a C 4-6 aliphatic conjugated diene monomer; (iii) from about 3 to about 40 percent by weight of a polar monomer selected from the group consisting of C 2-9 ethylenically unsaturated amide, aldehyde, carboxylic acid and nitrile monomers and C 1-6 esters of said carboxylic acid monomers; (b) foaming said compound; (c) applying said wet foam compound to at least one surface of glass fiber substrate; (d) subjecting said wet foam compound to heating conditions for a time sufficient to set and dry said wet foam.
Claim 7
Independent Claim
195 words
A method of manufacturing a composite material comprising a woven or non-woven glass fiber substrate encapsulated with a gelled plastisol of a co- or homo-polymer of vinyl chloride coated on at least one surface with a rubber foam which comprises: (a) forming a compound comprising a latex having a polymeric content of at least about 60 percent by weight and having a bulk composition (i) from about 0 to 30 percent by weight of a vinyl or vinylidene monoaromatic monomer which may be unsubstituted or substituted by a C 1-4 aliphatic radical or a chlorine or bromine atom; (ii) from about 60 to about 85 percent by weight of a C 4-6 aliphatic conjugated diene monomer; (iii) from about 3 to about 40 percent by weight of a polar monomer selected from the group consisting of C 2-9 ethylenically unsaturated amide, aldehyde, carboxylic acid and nitrile monomers and C 1-6 esters of said carboxylic acid monomers; (b) foaming said compound; (c) applying said wet foam compound to at least one surface of glass fiber substrate; (d) subjecting said wet foam compound to heating conditions for a time sufficient to set and dry said wet foam.
Claim 8
Dependent Claim
57 words
A method according to claim 5 wherein said compound further includes (i) up to about 150 parts by weight of a filler per 100 parts by weight of polymeric solids in said latex; and (ii) up to about 5 parts by weight of soap or surfactant per 100 parts by weight of polymeric solids in said latex.
Claim 9
Dependent Claim
20 words
The method according to claim 6 characterized in that the polar monomer is a C 2-9 ethylenically unsaturated nitrile monomer.
Claim 10
Dependent Claim
18 words
The method according to claim 7 characterized in that the substrate is coated with a polyvinyl chloride plastisol.
Claim 11
Dependent Claim
25 words
The method according to claim 8 characterized in that the monoaromatic monomer is styrene, the diene monomer is butadiene, and the nitrile monomer is acrylonitrile.
Claim 12
Dependent Claim
100 words
The method according to claim 5 characterized in that the latex is a blend of a styrene-butadiene rubber latex with an acrylonitrile-butadiene rubber latex wherein the styrene-butadiene rubber latex has a polymer solids content of about 65 percent by weight and a styrene:butadiene weight ratio of from about 25:75 to about 35:65 and the acrylonitrile-butadiene rubber latex has a polymer solids content of about 56 percent by weight and an acrylonitrile:butadiene weight ratio of from about 30:70 to about 40:60, the weight ratio of the styrene-butadiene rubber latex to the acrylonitrile-butadiene rubber latex being from about 80:20 to about 50:50.
Claim 13
Dependent Claim
49 words
The method according to claim 10 characterized in that the latex blend has a bulk polymer composition comprising (a) from about 15 to about 25 weight percent styrene; (b) from about 65 to about 75 weight percent butadiene; and (c) from about 5 to about 20 weight percent acrylonitrile.
Claim 14
Dependent Claim
37 words
The method according to claim 10 characterized in that the latex blend has a bulk polymer composition comprising (a) about 18 weight percent styrene; (b) about 68 weight percent butadiene; and (c) about 14 weight percent acrylonitrile.
Claim 15
Dependent Claim
30 words
A method according to claim 10 wherein said compound further includes from about 3 to 7 percent by weight on a wet basis of said latex of a gelling agent.
Claim 16
Dependent Claim
33 words
A process according to claim 13 wherein said compound is foamed to a density of from 500 to 800 g/l and is applied at a coat weight of about 500 g/m 2 .
References Cited (Backward Citations)
GB867746A
Cited
US3553047A
Cited
US3336180A
Cited
US3813462A
Cited
US3360422A
Cited
US3649433A
Cited
US4259384A
Cited
US4390585A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-02-19 | 1988-08-20 | 1989-02-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-02-19 | 1992-08-20 | 1993-02-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-02-19 | 1996-08-20 | 1997-02-19 | $7700.00 | Window Closed / Lapsed |