US4497948A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Chemical approach for controlling nadimide cure temperature and rate with maleimide
Assignee: National Aeronautics and Space Administration
•
Filing: 1983-12-14
•
Granted: 1985-02-05
•
Expires: 2003-12-14
Abstract
Abstract Polyimide resins suitable for use as composite matrix materials are formed by copolymerization of maleic and norbornenyl endcapped monomers and oligomers. The copolymers can be cured at temperatures under about 300 DEG C. by controlling the available concentration of the maleic end-capped reactant. This control can be achieved by adding sufficient amounts of said maleic reactant, or by chemical modification of either copolymer, so as to either increase Diels-Alder retrogression of the norbornenyl capped reactant and/or holding initiation and polymerization to a rate compatible with the availability of the maleic-capped reactant.
Inventors
- 👤 Richard W. Lauver
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 04:29
CPC Classifications
C; C08; C08F; C08F8/00
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
213 words
A process for the production of a polyimide of the general formula: ##STR11## wherein R 1 is a tetravalent arene radical and R 3 is a divalent arene radical, comprising the steps of: copolymerizing a maleic end capped prepolymer reactant with a stoichiometric amount of norborneny end-capped prepolymer reactant at temperatures under 300° C. and wherein the prepolymer reactants are generated by heating a solution of solvent and from about 30 percent to about 70 percent by weight of a mixture of compounds of the formulae: ##STR12## wherein R 1 is a tetravalent arene radical and at least two of R 2 are alkyl with the remainder being hydrogen: and (b) H.sub.2 N--R.sub.3 --NH.sub.2 wherein R 3 is a divalent arene radical: and ##STR13## wherein R 2 is defined as in (a) and at least one R 2 in (c) being alkyl, and R 4 is ##STR14## wherein R 5 is hydrogen or lower alkyl of 1-4 carbons, and wherein the ratio of (a):(b):(c) is n:(n+1):2, wherein n has a value from 1-20, to obtain curable polyimide prepolymers and including the step of promoting Diels-Alder retrogression of the norbornenyl end-capped prepolymer reactant by adding to the norbornenyl reactant a chemical modifier having at least one aromatic ring containing at least one electronegative substituent.
Claim 2
Dependent Claim
213 words
A process for the production of a polyimide of the general formula: ##STR11## wherein R 1 is a tetravalent arene radical and R 3 is a divalent arene radical, comprising the steps of: copolymerizing a maleic end capped prepolymer reactant with a stoichiometric amount of norborneny end-capped prepolymer reactant at temperatures under 300° C. and wherein the prepolymer reactants are generated by heating a solution of solvent and from about 30 percent to about 70 percent by weight of a mixture of compounds of the formulae: ##STR12## wherein R 1 is a tetravalent arene radical and at least two of R 2 are alkyl with the remainder being hydrogen: and (b) H.sub.2 N--R.sub.3 --NH.sub.2 wherein R 3 is a divalent arene radical: and ##STR13## wherein R 2 is defined as in (a) and at least one R 2 in (c) being alkyl, and R 4 is ##STR14## wherein R 5 is hydrogen or lower alkyl of 1-4 carbons, and wherein the ratio of (a):(b):(c) is n:(n+1):2, wherein n has a value from 1-20, to obtain curable polyimide prepolymers and including the step of promoting Diels-Alder retrogression of the norbornenyl end-capped prepolymer reactant by adding to the norbornenyl reactant a chemical modifier having at least one aromatic ring containing at least one electronegative substituent.
Claim 3
Dependent Claim
20 words
The process as defined by claim 1 in which said separate chemical modifier contains at least one NO 2 substituent.
Claim 4
Dependent Claim
24 words
The process as defined by claim 1 in which the chemical modifier is selected from the group consisting of nitrobenzene, dinitrobenzene, and mixtures thereof.
Claim 5
Dependent Claim
19 words
The process as defined by claim 1 in which said separate chemical modifier contains at least one CN substituent.
Claim 6
Dependent Claim
19 words
The process as defined by claim 1 in which said separate chemical modifier contains at least one halogen substituent.
Claim 7
Dependent Claim
43 words
The process as defined by claim 1 comprising retarding polymerization by adding a separate chemical modifier to a mixture of norbornenyl end-capped prepolymer reactant and maleic end-capped prepolymer reactant, said modifier comprising at least one aromatic ring containing at least one electronegative substituent.
Claim 8
Dependent Claim
19 words
The process as defined by claim 6 in which said chemical modifier has at least one NO 2 substituent.
Claim 9
Dependent Claim
24 words
The process as defined by claim 6 in which said chemical modifier is selected from the group consisting of nitrobenzene, dinitrobenzene, and mixtures thereof.
Claim 10
Dependent Claim
18 words
The process as defined by claim 6 in which said chemical modifier contains at least one CN substituent.
Claim 11
Dependent Claim
17 words
The process as defined by claim 6 wherein the chemical modifier contains at least one halogen substituent.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-02-05 | 1988-08-06 | 1989-02-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-02-05 | 1992-08-06 | 1993-02-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-02-05 | 1996-08-06 | 1997-02-05 | $7700.00 | Window Closed / Lapsed |