US4497943A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Organocyclopolysiloxane and a room temperature curable composition containing same
Assignee: Shin-Etsu Chemical Co Ltd
•
Filing: 1983-04-21
•
Granted: 1985-02-05
•
Expires: 2003-04-21
Abstract
Abstract The room temperature curable organopolysiloxane composition of the invention comprises a dimethylpolysiloxane terminated at both molecular chain ends with silanolic hydroxy groups, an organocyclopolysiloxane, typically a cyclotetrasiloxane, having 2 or more alkenyloxy groups such as isopropenyloxy groups in a molecule as a crosslinking agent for the dimethylpolysiloxane and a guanidyl-containing organosilane or polysiloxane compound as a curing catalyst. The composition is capable of giving a cured rubbery elastomer when kept in a moisture-containing atmosphere at room temperature without the problems in the prior art compositions such as noxious condensation products or poor adhesion to the surface of the substrate on which the composition has been cured. The above mentioned organocyclopolysiloxane having alkenyloxy groups along with one or more of trihydrocarbylsiloxy groups or, typically, trimethylsiloxy groups bonded to the silicon atoms in the ring structure is a novel compound not described in any prior art literatures.
Inventors
- 👤 Toshio Takago
- 👤 Osamu Sodeyama
- 👤 Masami Terashima
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 22:55
CPC Classifications
C; C08; C08G; C08G77/00; C08G77/04; C08G77/045; C07; C07F; C07F7/00; C07F7/02; C07F7/08; C07F7/0803; C07F7/081; C07F7/0896; C07F7/18; C07F7/1804; C07F7/21; C08L; C08L83/00; C08L83/04; C08G77/14; C08G77/16; C08G77/18; C08G77/20
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
95 words
An organocyclopolysiloxane represented by the general formula ##STR9## in which X is an alkenyloxy group of the formula --OCR 3 ═CH--R 2 , Y is a trimethylsiloxy group of the formula --O--Si(CH 3 ) 3 , R 1 is monovalent hydrocarbon group having from 1 to 8 carbon atoms, R 2 and R 3 are each independently a hydrogen atom or a substituted or unsubstituted monovalent hydrocarbon group having from 1 to 6 carbon atoms, m is 2 or 3, and n is a positive integer with the proviso that m+n is equal to 4.
Claim 2
Dependent Claim
95 words
An organocyclopolysiloxane represented by the general formula ##STR9## in which X is an alkenyloxy group of the formula --OCR 3 ═CH--R 2 , Y is a trimethylsiloxy group of the formula --O--Si(CH 3 ) 3 , R 1 is monovalent hydrocarbon group having from 1 to 8 carbon atoms, R 2 and R 3 are each independently a hydrogen atom or a substituted or unsubstituted monovalent hydrocarbon group having from 1 to 6 carbon atoms, m is 2 or 3, and n is a positive integer with the proviso that m+n is equal to 4.
Claim 3
Dependent Claim
25 words
The organocyclopolysiloxane as claimed in claim 1 wherein the group denoted by X is an isopropenyloxy group of the formula --O--C(CH 3 )═CH 2 .
Claim 4
Dependent Claim
206 words
A room temperature curable organopolysiloxane composition which comprises: (a) 100 parts by weight of a diorganopolysiloxane terminated at both molecular chain ends with silanolic hydroxy groups; (b) from 0.01 to 25 parts by weight of an organocyclopolysiloxane represented by the general formula ##STR10## in which X is an alkenyloxy group of the formula --OCR 3 ═CH--R 2 , Y is a trihydrocarbylsiloxy group of the formula --O--SiR 1 3 or a monovalent hydrocarbon group having from 1 to 5 carbon atoms, R 1 is a monovalent hydrocarbon group having from 1 to 8 carbon atoms, R 2 and R 3 are each independently a hydrogen atom or a substituted or unsubstituted monovalent hydrocarbon group having from 1 to 6 carbon atoms, m is a positive interger of 2, 3 or 4 and n is zero or a positive integer with the proviso that m+n is equal to 4, 5 or 6; and (c) from 0.01 to 5 parts by weight of a guanidyl-containing organosilicon compound having, in a molecule, at least one substituted or unsubstituted guanidyl group represented by the general formula (R 4 2 N--) 2 C═N--, in which each R 4 is a hydrogen atom or a monovalent hydrocarbon group independently from the others.
Claim 5
Dependent Claim
206 words
A room temperature curable organopolysiloxane composition which comprises: (a) 100 parts by weight of a diorganopolysiloxane terminated at both molecular chain ends with silanolic hydroxy groups; (b) from 0.01 to 25 parts by weight of an organocyclopolysiloxane represented by the general formula ##STR10## in which X is an alkenyloxy group of the formula --OCR 3 ═CH--R 2 , Y is a trihydrocarbylsiloxy group of the formula --O--SiR 1 3 or a monovalent hydrocarbon group having from 1 to 5 carbon atoms, R 1 is a monovalent hydrocarbon group having from 1 to 8 carbon atoms, R 2 and R 3 are each independently a hydrogen atom or a substituted or unsubstituted monovalent hydrocarbon group having from 1 to 6 carbon atoms, m is a positive interger of 2, 3 or 4 and n is zero or a positive integer with the proviso that m+n is equal to 4, 5 or 6; and (c) from 0.01 to 5 parts by weight of a guanidyl-containing organosilicon compound having, in a molecule, at least one substituted or unsubstituted guanidyl group represented by the general formula (R 4 2 N--) 2 C═N--, in which each R 4 is a hydrogen atom or a monovalent hydrocarbon group independently from the others.
Claim 6
Dependent Claim
21 words
The room temperature curable organopolysiloxane composition as claimed in claim 3 wherein the diorganopolysiloxane as the component (a) is a dimethylpolysiloxane.
Claim 7
Dependent Claim
25 words
The room temperature curable organopolysiloxane composition as claimed in claim 4 wherein the dimethylpolysiloxane has a viscosity of at least 25 centistokes at 25° C.
Claim 8
Dependent Claim
37 words
The room temperature curable organopolysiloxane composition as claimed in claim 3 wherein the group denoted by X in the general formula of the component (b) is an isopropenyloxy group of the formula --O--C(CH 3 )═CH 2 .
Claim 9
Dependent Claim
23 words
The room temperature curable organopolysiloxane composition as claimed in claim 3 wherein m is 2 or 3 and m+n is equal to 4.
Claim 10
Dependent Claim
30 words
The room temperature curable organopolysiloxane composition as claimed in claim 3 wherein the trihydrocarbylsiloxy group denoted by Y is a trimethylsiloxy group of the formula --O--Si(CH 3 ) 3 .
Claim 11
Dependent Claim
27 words
The room temperature curable organopolysiloxane composition as claimed in claim 3 wherein the monovalent hydrocarbon group denoted by Y is a methyl group or a propyl group.
Claim 12
Dependent Claim
52 words
The room temperature curable organopolysiloxane composition as claimed in claim 3 wherein the component (b) is a mixture of a first organocyclopolysiloxane of the general formula in which m is 2 and n is 2 or 3 and a second organocyclopolysiloxane of the general formula in which m is 3 or 4.
Claim 13
Dependent Claim
31 words
The room temperature curable organopolysiloxane composition as claimed in claim 10 wherein the molar ratio of the first organocyclopolysiloxane to the second organocyclopolysiloxane is in the range from 99.5:0.5 to 70:30.
Claim 14
Dependent Claim
27 words
The room temperature curable organopolysiloxane composition as claimed in claim 3 wherein the guanidyl group in the component (c) is a tetramethylguanidyl group of the formula ##STR11##
Claim 15
Dependent Claim
19 words
The room temperature curable organopolysiloxane composition as claimed in claim 3 wherein the component (c) is 1-tetramethylguanidyl 3-trimethylsilyl propane.
Claim 16
Dependent Claim
19 words
The room temperature curable organopolysiloxane composition as claimed in claim 3 wherein the component (c) is 3-tetramethylguanidylpropyl tris(trimethylsiloxy) silane.
Claim 17
Dependent Claim
38 words
The room temperature curable organopolysiloxane composition as claimed in claim 3 wherein the amount of the component (b) is in the range from 0.1 to 20 parts by weight per 100 parts by weight of the component (a).
Claim 18
Dependent Claim
38 words
The room temperature curable organopolysiloxane composition as claimed in claim 3 wherein the amount of the component (c) is in the range from 0.1 to 2 parts by weight per 100 parts by weight of the component (a).
Claim 19
Dependent Claim
35 words
The room temperature curable organopolysiloxane composition as claimed in claim 3 which further comprises a filler in an amount of 400 parts by weight or smaller per 100 parts by weight of the component (a).
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-02-05 | 1988-08-06 | 1989-02-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-02-05 | 1992-08-06 | 1993-02-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-02-05 | 1996-08-06 | 1997-02-05 | $7700.00 | Window Closed / Lapsed |