Diffusion membrane and process for separating hydrogen from gas mixture
Assignee: Forschungszentrum Jülich
•
Filing: 1984-06-06
•
Granted: 1985-01-29
•
Expires: 2004-06-06
Abstract
Abstract For separation of hydrogen and its isotopes by diffusion through a membraneirtually impermeable to other gases, a non-porous hydrogen-permeable metallic membrane is provided on the gas access side with a coating of an alloy of palladium with at least 45 atomic % Cu or at least 50 atomic percent Ag or at least 7 atomic % Y, the membrane itself containing Cu, Ag or Y respectively in a concentration at least equilibrated with the coating at operation temperature. Preferably the membrane consists of a metal of niobium and/or tantalum bases especially of an alloy containing from 10 to 30 % Ti, 3 to 10 % V, 0 to 25 % Nb and at least 30 % Ta, all by weight, and preferably it is of a composition of 20 to 25 % Ti, 5 to 7,5 % V, 0 to 25 Nb, and at least 50 % Ta, being saturated with copper and or silver, while a copper and/or silver palladium alloy coating is used. Such inherently oxidation sensitive membranes can be stabilized by provision of an internal intermediate layer in the form of a melt forming or containing an alkaline metal hydride and/or an alkaline earth metal hydride. A melt containing alkaline metal and/or alkaline earth metal which forms a hydride, brought into contact on the secondary side of a membrane in accordance with the invention, provides a hydrogen sink on the secondary side and inhibits internal hydride formation and secondary side oxidation of the membrane.
Inventors
- 👤 Friedrich Behr
- 👤 Rudolf Schulten
- 👤 Walter Weirich
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 11:11
CPC Classifications
B; B01; B01D; B01D59/00; B01D59/10; B01D59/12; B01D59/14; B01D53/00; B01D53/22; B01D71/00; B01D71/02; B01D71/022; B01D71/0221; B01D71/0223; B01D71/02231; B01D71/02232; C; C01; C01B; C01B3/00; C01B3/50; C01B3/501; C01B3/503; C01B3/505
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
139 words
Hydrogen diffusion membrane consisting essentially of a metallic material selected from the group consisting of tantalum, niobium, titanium, vanadium, nickel and alloys and mixtures of two or more of the foregoing, which material is non-porous but selectively permeable for hydrogen, having a palladium alloy coating on the hydrogen entry side and having the improvement wherein: said palladium alloy coating is of an alloy of palladium and an alloy partner metal selected from the group consisting of copper, silver and yttrium with a content of at least 45 atomic % copper or at least 50 atomic % silver or at least 7 atomic % yttrium, and said material of said membrane itself has a content of the same alloy partner metal as in said palladium alloy which is in a concentration at least sufficient for equilibrium with the palladium alloy.
Claim 2
Dependent Claim
139 words
Hydrogen diffusion membrane consisting essentially of a metallic material selected from the group consisting of tantalum, niobium, titanium, vanadium, nickel and alloys and mixtures of two or more of the foregoing, which material is non-porous but selectively permeable for hydrogen, having a palladium alloy coating on the hydrogen entry side and having the improvement wherein: said palladium alloy coating is of an alloy of palladium and an alloy partner metal selected from the group consisting of copper, silver and yttrium with a content of at least 45 atomic % copper or at least 50 atomic % silver or at least 7 atomic % yttrium, and said material of said membrane itself has a content of the same alloy partner metal as in said palladium alloy which is in a concentration at least sufficient for equilibrium with the palladium alloy.
Claim 3
Dependent Claim
29 words
A membrane according to claim 1 in which said metallic material of said membrane is saturated with said metal selected from the group consisting of copper, silver and yttrium.
Claim 4
Dependent Claim
34 words
Membrane according to claim 2 in which said metallic material of said membrane consists predominantly of a substance selected from the group consisting of tantalum, niobium and alloys and mixtures of tantalum and niobium.
Claim 5
Dependent Claim
34 words
Membrane according to claim 1 in which said metallic material of said membrane consists predominantly of a substance selected from the group consisting of tantalum, niobium and alloys and mixtures of tantalum and niobium.
Claim 6
Dependent Claim
106 words
Membrane according to claim 4 in which said palladium alloy is an alloy of palladium and an alloy partner metal selected from the group consisting of copper and silver and in which said metallic material of said membrane consists of an alloy composed of not less than 10% nor more than 30% by weight of titanium, not less than 3% and not more than 10% by weight of vanadium, not more than 25% by weight of niobium and at least 30% by weight of tantalum, said alloy constituting said membrane being saturated with said alloy partner metal selected from the group consisting of copper and silver.
Claim 7
Dependent Claim
80 words
Membrane according to claim 5 in which said palladium alloy is an alloy of palladium and copper and in which said metallic material of said membrane consists of an alloy of at least 20% and not more than 25% by weight of titanium, at least 5% and not more than 7.5% by weight of vanadium, not more than 25% by weight of niobium and at least 50% by weight of tantalum, which alloy constituting said membrane is saturated with copper.
Claim 8
Dependent Claim
79 words
Membrane according to claim 1 in which an intermediate layer in the form of a melt, forming or containing a metal hydride substance, is interposed between outer layers of said metallic material of said membrane, thereby providing a three-layer structure, on the hydrogen entry side of which said palladium alloy coating is provided, said metal hydride being selected from the group of alkali metal hydrides, alkaline earth metal hydrides and mixtures of alkali metal and alkaline earth metal hydrides.
Claim 9
Dependent Claim
30 words
Membrane according to claim 7 in which said interposed layer in said membrane is formed by a melt containing a eutectic mixture of lithium hydride with a halogenide of lithium.
Claim 10
Dependent Claim
62 words
Membrane according to claim 7 in which said membrane is coated on the hydrogen exit side with an additional coating of an alloy of palladium with said metal selected from the group consisting of copper, silver and yttrium having a content of at least 45 atomic % copper or at least 50 atomic % silver or at least 7 atomic % yttrium.
Claim 11
Dependent Claim
62 words
Membrane according to claim 7 in which said membrane is coated on the hydrogen exit side with an additional coating of an alloy of palladium with said metal selected from the group consisting of copper, silver and yttrium having a content of at least 45 atomic % copper or at least 50 atomic % silver or at least 7 atomic % yttrium.
Claim 12
Dependent Claim
62 words
Membrane according to claim 1 in which said membrane is coated on the hydrogen exit side with an additional coating of an alloy of palladium with said metal selected from the group consisting of copper, silver and yttrium having a content of at least 45 atomic % copper or at least 50 atomic % silver or at least 7 atomic % yttrium.
Claim 13
Dependent Claim
19 words
Membrane according to claim 1, in which said palladium alloy coating is of an alloy of palladium and copper.
Claim 14
Dependent Claim
19 words
Membrane according to claim 1, in which said palladium alloy coating is of an alloy of palladium and silver.
Claim 15
Dependent Claim
219 words
Method for the separation of hydrogen from gas mixtures by diffusion at elevated temperature through a membrane of a metallic material having a coating of a palladium alloy on the hydrogen entry side, said method comprising the steps of: utilizing a membrane in which said palladium alloy coating is an alloy of palladium and an alloy partner metal selected from the group consisting of copper, silver and yttrium with a content of at least 45 atomic % copper, or at least 50 atomic % silver, or at least 7 atomic % yttrium, while the metallic material of the membrane itself has a content of the same alloy partner metal as in said palladium alloy which is in a concentration at least sufficient for equilibrium with the palladium alloy; causing the hydrogen, after passing through a layer of the metallic material of said membrane, to come into contact with a melt containing a substance selected from the group consisting of alkali metals, alkaline earth metals and mixtures of alkali and alkaline earth metals having an affinity for hydrogen which is higher than that of the metallic material of said membrane and of that of the hydrogen bonding in said gas mixture and which is capable of forming a hydride either in solution in said melt or as a suspension therein.
Claim 16
Dependent Claim
219 words
Method for the separation of hydrogen from gas mixtures by diffusion at elevated temperature through a membrane of a metallic material having a coating of a palladium alloy on the hydrogen entry side, said method comprising the steps of: utilizing a membrane in which said palladium alloy coating is an alloy of palladium and an alloy partner metal selected from the group consisting of copper, silver and yttrium with a content of at least 45 atomic % copper, or at least 50 atomic % silver, or at least 7 atomic % yttrium, while the metallic material of the membrane itself has a content of the same alloy partner metal as in said palladium alloy which is in a concentration at least sufficient for equilibrium with the palladium alloy; causing the hydrogen, after passing through a layer of the metallic material of said membrane, to come into contact with a melt containing a substance selected from the group consisting of alkali metals, alkaline earth metals and mixtures of alkali and alkaline earth metals having an affinity for hydrogen which is higher than that of the metallic material of said membrane and of that of the hydrogen bonding in said gas mixture and which is capable of forming a hydride either in solution in said melt or as a suspension therein.
Claim 17
Dependent Claim
31 words
Method according to claim 14 in which said melt is an alkali metal melt in which the alkali metal is selected from the group consisting of sodium-potassium mixtures and molten lithium.
Claim 18
Dependent Claim
40 words
Method according to claim 14 in which said melt is a melt containing alkaline earth metal in the form of a eutectic mixture of barium and magnesium in which calcium is dissolved to an extent not exceeding 40 atomic %.
Claim 19
Dependent Claim
33 words
Method according to claim 14 in which a subsequent step is produced of filtering out the metal hydride formed in the melt and then decomposing it to recover hydrogen and regenerate the metal.
Claim 20
Dependent Claim
33 words
Method according to claim 14 in which a further step is performed of heating said melt in order to decompose hydrides formed therein, for recovery of the hydrogen and regeneration of the metal.
Claim 21
Dependent Claim
28 words
Method according to claim 14 in which the further step is performed of separating the hydrogen compound produced in said melt by dissolving it in a halogenide melt.
Claim 22
Dependent Claim
25 words
Method according to claim 19 in which the solution of said hydride in halogenide melt is subjected to fluid melt electrolysis for recovery of hydrogen.
References Cited (Backward Citations)
US2958391A
Cited
US3148031A
Cited
US3128178A
Cited
US3350846A
Cited
US3413777A
Cited
DE1558409A1
Cited
US3407571A
Cited
US3371468A
Cited
US3497390A
Cited
US3447286A
Cited
US3439474A
Cited
GB1292025A
Cited
GB1346422A
Cited
US4235863A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-01-29 | 1988-07-30 | 1989-01-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-01-29 | 1992-07-30 | 1993-01-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-01-29 | 1996-07-30 | 1997-01-29 | $7700.00 | Window Closed / Lapsed |