US4495375A
Expired / Lapsed
US
⏱️ 0.0 years remaining
MIS or SIS Solar cells
Assignee: Battelle-Institut
•
Filing: 1983-09-13
•
Granted: 1985-01-22
•
Expires: 2003-09-13
Abstract
Abstract The function of the insulating film in MIS and SIS solar cells can also be fulfilled by a semiconductor with a sufficiently large energy gap. The doping of the quasi insulating layer guarantees good fill factors and short-circuit current densities also at a relatively high film thickness. For cadmium selenide solar cells with a quasi insulating film made of zinc selenide, copper is preferably used as a doping material.
Inventors
- 👤 Edmund Rickus
- 👤 Karlheinz Jager
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 15:43
CPC Classifications
H; H10; H10F; H10F77/00; H10F77/10; H10F77/12; H10F77/123; H10F77/1233; H10F10/00; H10F10/10; H10F10/12; Y; Y02; Y02E; Y02E10/00; Y02E10/50
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
58 words
A solar cell with metal layer-quasi insulator-semiconductor (MIS) or semiconductor-quasi insulator-semiconductor (SIS) layer arrangement where the quasi insulating layer consists of a high-resistance semiconductor material, characterized in that the quasi insulating layer is doped with a material which makes it easier for the appropriate minority carrier to overcome the additional potential barrier caused by the quasi insulating layer.
Claim 2
Dependent Claim
58 words
A solar cell with metal layer-quasi insulator-semiconductor (MIS) or semiconductor-quasi insulator-semiconductor (SIS) layer arrangement where the quasi insulating layer consists of a high-resistance semiconductor material, characterized in that the quasi insulating layer is doped with a material which makes it easier for the appropriate minority carrier to overcome the additional potential barrier caused by the quasi insulating layer.
Claim 3
Dependent Claim
47 words
The solar cell as claimed in claim 1 wherein said solar cell comprises a cadmium selenide MIS solar cell containing a quasi insulating layer of zinc selenide doped with a material which forms acceptor levels in the zinc selenide or which prevents the recombination of minority carriers.
Claim 4
Dependent Claim
30 words
The solar cell as claimed in claim 2, wherein the quasi insulating layer is doped with a material selected from the group consisting of silver, antimony, gold, arsenic, and copper.
Claim 5
Dependent Claim
15 words
The solar cell as claimed in claim 3, wherein the metal layer consists of gold.
Claim 6
Dependent Claim
15 words
The solar cell as claimed in claim 2, wherein the metal layer consists of gold.
Claim 7
Dependent Claim
56 words
The solar cell as claimed in claim 1 wherein the doping materials are present in a higher concentration in the case of MIS solar cells, on the surface area adjacent to the metal layer, and in the case of SIS solar cells, on the surface area adjacent to the semiconductor layer correspnding to the metal layer.
Claim 8
Dependent Claim
15 words
The solar cell of claim 1 wherein the guasi insulating layer is doped with copper.
Claim 9
Dependent Claim
16 words
The solar cell of claim 1 wherein the insulating layer is zinc selenide doped with copper.
Claim 10
Independent Claim
37 words
A method for making MIS or SIS solar cells having a doped quasi insulating layer comprising depositing a very thin film of the dopant material in the quasi insulating layer, and carrying out a temperature treatment thereafter.
Claim 11
Independent Claim
37 words
A method for making MIS or SIS solar cells having a doped quasi insulating layer comprising depositing a very thin film of the dopant material in the quasi insulating layer, and carrying out a temperature treatment thereafter.
Claim 12
Dependent Claim
61 words
The method as claimed in claim 9, wherein said solar cell is a cadmium selenide/zinc selenide MIS solar cell, the zinc selenide layer is doped with a material selected from the group consisting of silver, antimony, gold, arsenic, and copper, and wherein a single temperature treatment between 130° and 170° C. is carried out after the completion of the solar cell.
Claim 13
Dependent Claim
35 words
The method as claimed in claim 10, wherein the film made of the doping material has a thickness of 0.1-1 nm, and is applied on a zinc selenide layer having a thickness of 2-10 nm.
Claim 14
Dependent Claim
20 words
A method as in claim 11, wherein the film made of the doping material has a thickness of 0.5 nm.
Claim 15
Dependent Claim
17 words
A method as in claim 11, wherein the zinc selenide layer has a thickness of 5 nm.
Claim 16
Dependent Claim
14 words
The method of claim 10 wherein the zinc selenide layer is doped with copper.
References Cited (Backward Citations)
US3990097A
Cited
US4338482A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-01-22 | 1988-07-23 | 1989-01-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-01-22 | 1992-07-23 | 1993-01-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-01-22 | 1996-07-23 | 1997-01-22 | $7700.00 | Window Closed / Lapsed |