Method of forming a urethane prepolymer and its use in consolidating aggregate material
Assignee: Gravi-Mechanics Co
•
Filing: 1983-05-10
•
Granted: 1985-01-22
•
Expires: 2003-05-10
Abstract
Abstract A method of forming a urethane prepolymer comprising the steps of gradually adding an isocyanate compound to a hydrophilic polyether or polyester compound without substantial added mixing whereby a relatively dense isocyanate layer and a polyether or polyester layer overlying the isocyanate layer are formed, and a urethane prepolymer-forming reaction occurs at the interface between the layers. The resulting urethane prepolymer may be reacted with water to form a cellular urethane polymer, or with an aqueous slurry of unconsolidated aggregate material to form a consolidated aggregate product, such as a plant growth supporting rooting medium.
Inventors
- 👤 Richard R. Dedolph
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 19:40
CPC Classifications
C; C09; C09K; C09K17/00; C09K17/14; C09K17/18; C09K17/30; A; A01; A01G; A01G24/00; A01G24/40; A01G24/48; A01G31/00; A01G31/02; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/40; C08G18/48; C08G18/4833; C08G2310/00; Y; Y02; Y02P; Y02P60/00; Y02P60/20; Y02P60/21
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
147 words
A method of forming a urethane prepolymer, said method comprising the steps of: (a) adding to a polyether or polyester compound under substantially anhydrous conditions a stoichiometric excess of a compound containing at least two active isocyanate groups per molecule to initiate an exothermic condensation reaction between said polyether or polyester compound and said isocyanate compound, the temperature of said reactants being such that the temperature of the reactants after addition of isocyanate is less than or equal to about 120° C., the density of said isocyanate compound being greater than the density of said polyether or polyester compound and said isocyanate compound being added gradually to said polyether or polyester without substantial added mixing whereby a relatively dense isocyanate layer and a polyether or polyester layer overlying said isocyanate layer are formed; and, (b) allowing said reaction to proceed in order to form said urethane prepolymer.
Claim 2
Independent Claim
147 words
A method of forming a urethane prepolymer, said method comprising the steps of: (a) adding to a polyether or polyester compound under substantially anhydrous conditions a stoichiometric excess of a compound containing at least two active isocyanate groups per molecule to initiate an exothermic condensation reaction between said polyether or polyester compound and said isocyanate compound, the temperature of said reactants being such that the temperature of the reactants after addition of isocyanate is less than or equal to about 120° C., the density of said isocyanate compound being greater than the density of said polyether or polyester compound and said isocyanate compound being added gradually to said polyether or polyester without substantial added mixing whereby a relatively dense isocyanate layer and a polyether or polyester layer overlying said isocyanate layer are formed; and, (b) allowing said reaction to proceed in order to form said urethane prepolymer.
Claim 3
Dependent Claim
48 words
The method of claim 1 wherein the surface area and/or time of persistence of the interface between said polyester or polyether layer and said isocyanate layer is controlled in order to control the rate and nature of reaction between said isocyanate compound and said polyether or polyester compound.
Claim 4
Dependent Claim
145 words
A urethane prepolymer prepared by the method comprising the steps of: (a) adding to a polyether or polyester compound under substantially anhydrous conditions a stoichiometric excess of a compound containing at least two active isocyanate groups per molecule to initiate an exothermic condensation reaction between said polyether or polyester compound and said isocyanate compound, the temperature of said reactants being such that the temperature of the reactants after addition of isocyanate is less than or equal to about 120° C., the density of said isocyanate compound being greater than the density of said polyether or polyester compound and said isocyanate compound being added gradually to said polyether or polyester without substantially adding mixing whereby a relatively dense isocyanate layer and a polyether or polyester layer overlying said isocyanate layer are formed; and, (b) allowing said reaction to proceed in order to form said urethane prepolymer.
Claim 5
Dependent Claim
145 words
A urethane prepolymer prepared by the method comprising the steps of: (a) adding to a polyether or polyester compound under substantially anhydrous conditions a stoichiometric excess of a compound containing at least two active isocyanate groups per molecule to initiate an exothermic condensation reaction between said polyether or polyester compound and said isocyanate compound, the temperature of said reactants being such that the temperature of the reactants after addition of isocyanate is less than or equal to about 120° C., the density of said isocyanate compound being greater than the density of said polyether or polyester compound and said isocyanate compound being added gradually to said polyether or polyester without substantially adding mixing whereby a relatively dense isocyanate layer and a polyether or polyester layer overlying said isocyanate layer are formed; and, (b) allowing said reaction to proceed in order to form said urethane prepolymer.
Claim 6
Independent Claim
160 words
A method of forming a cellular urethane polymer, said method comprising the steps of: (a) adding to a polyether or polyester compound under substantially anhydrous conditions a stoichiometric excess of a compound containing at least two active isocyanate groups per molecule to initiate an exothermic condensation reaction between said polyether or polyester compound and said isocyanate compound, the temperature of said reactants being such that the temperature of said reactants after addition of isocyanate is less than or equal to about 120° C., the density of said isocyanate compound being greater than the density of said polyether or polyester compound and said isocyanate compound being added gradually to said polyether or polyester without substantial added mixing whereby a relatively dense isocyanate layer and a polyether or polyester layer overlying said isocyanate layer are formed; (b) allowing said reaction to proceed in order to form a urethane prepolymer; and, (c) reacting said prepolymer with water to form said cellular urethane polymer.
Claim 7
Independent Claim
160 words
A method of forming a cellular urethane polymer, said method comprising the steps of: (a) adding to a polyether or polyester compound under substantially anhydrous conditions a stoichiometric excess of a compound containing at least two active isocyanate groups per molecule to initiate an exothermic condensation reaction between said polyether or polyester compound and said isocyanate compound, the temperature of said reactants being such that the temperature of said reactants after addition of isocyanate is less than or equal to about 120° C., the density of said isocyanate compound being greater than the density of said polyether or polyester compound and said isocyanate compound being added gradually to said polyether or polyester without substantial added mixing whereby a relatively dense isocyanate layer and a polyether or polyester layer overlying said isocyanate layer are formed; (b) allowing said reaction to proceed in order to form a urethane prepolymer; and, (c) reacting said prepolymer with water to form said cellular urethane polymer.
Claim 8
Dependent Claim
42 words
The method of claim 4 wherein the surface area of the interface between said polyester or polyether layer and said isocyanate layer is controlled in order to control the rate of reaction between said isocyanate compound and said polyether or polyester compound.
Claim 9
Dependent Claim
158 words
A cellular urethane polymer prepared by the method comprising the steps of: (a) adding to a polyether or polyester compound under substantially anhydrous conditions a stoichiometric excess of a compound containing at least two active isocyanate groups per molecule to initiate an exothermic condensation reaction between said polyether or polyester compound and said isocyanate compound, the temperature of said reactants being such that the temperature of the reactants after addition of isocyanate is less than or equal to about 120° C. the density of said isocyanate compound being greater than the density of said polyether or polyester compound and said isocyanate compound being added gradually to said polyether or polyester without substantial added mixing whereby a relatively dense isocyanate layer and a polyether or polyester layer overlying said isocyanate layer are formed; (b) allowing said reaction to proceed in order to form a urethane prepolymer; and, (c) reacting said prepolymer with water to form said cellular urethane polymer.
Claim 10
Dependent Claim
158 words
A cellular urethane polymer prepared by the method comprising the steps of: (a) adding to a polyether or polyester compound under substantially anhydrous conditions a stoichiometric excess of a compound containing at least two active isocyanate groups per molecule to initiate an exothermic condensation reaction between said polyether or polyester compound and said isocyanate compound, the temperature of said reactants being such that the temperature of the reactants after addition of isocyanate is less than or equal to about 120° C. the density of said isocyanate compound being greater than the density of said polyether or polyester compound and said isocyanate compound being added gradually to said polyether or polyester without substantial added mixing whereby a relatively dense isocyanate layer and a polyether or polyester layer overlying said isocyanate layer are formed; (b) allowing said reaction to proceed in order to form a urethane prepolymer; and, (c) reacting said prepolymer with water to form said cellular urethane polymer.
Claim 11
Independent Claim
186 words
A method of consolidating aggregate material to form an integral, resilient, water-permeable mass, said method comprising the steps of: (a) adding to a polyether or polyester compound under substantially anhydrous conditions a stoichiometric excess of a compound containing at least two active isocyanate groups per molecule to initiate an exothermic condensation reaction between said polyether or polyester and said isocyanate compound, the temperature of said reactants being such that the temperature of the reactants after addition of isocyanate is less than or equal to about 120° C., the density of said isocyanate compound being greater than the density of said polyether or polyester compound and said isocyanate compound being added gradually to said polyether or polyester without added mixing whereby a relatively dense isocyanate layer and a polyether or polyester layer overlying said isocyanate are formed; (b) allowing said reaction to proceed in order to form a urethane prepolymer; (c) forming an aqueous slurry of unconsolidated aggregate material; and, (d) combining said slurry and said prepolymer whereby the water in said slurry reacts with said prepolymer to form a cellular polymer which binds said aggregate material.
Claim 12
Independent Claim
186 words
A method of consolidating aggregate material to form an integral, resilient, water-permeable mass, said method comprising the steps of: (a) adding to a polyether or polyester compound under substantially anhydrous conditions a stoichiometric excess of a compound containing at least two active isocyanate groups per molecule to initiate an exothermic condensation reaction between said polyether or polyester and said isocyanate compound, the temperature of said reactants being such that the temperature of the reactants after addition of isocyanate is less than or equal to about 120° C., the density of said isocyanate compound being greater than the density of said polyether or polyester compound and said isocyanate compound being added gradually to said polyether or polyester without added mixing whereby a relatively dense isocyanate layer and a polyether or polyester layer overlying said isocyanate are formed; (b) allowing said reaction to proceed in order to form a urethane prepolymer; (c) forming an aqueous slurry of unconsolidated aggregate material; and, (d) combining said slurry and said prepolymer whereby the water in said slurry reacts with said prepolymer to form a cellular polymer which binds said aggregate material.
Claim 13
Dependent Claim
42 words
The method of claim 7 wherein the surface area of the interface between said polyether or polyester layer and said isocyanate layer is controlled in order to control the rate of reaction between said isocyanate compound and said polyether or polyester compound.
Claim 14
Dependent Claim
190 words
A consolidated aggregate material in the form of an integral, resilient, water-permeable mass prepared by the method comprising the steps of: (a) adding to a polyether or polyester compound under substantially anhydrous conditions a stoichiometric excess of a compound containing at least two active isocyanate groups per molecule to initiate an exothermic condensation reaction between said polyether or polyester and said isocyanate compound, the temperature of said reactants being such that the temperature of the reactants after addition of isocyanate is less than or equal to about 120° C., the density of said isocyanate compound being greater than the density of said polyether or polyester compound and said isocyanate compound being added gradually to said polyether or polyester without substantial added mixing whereby a relatively dense isocyanate layer and a polyether or polyester layer overlying said isocyanate layer are formed; (b) allowing said reaction to proceed in order to form a urethane prepolymer; (c) forming an aqueous slurry of unconsolidated aggregate material; and, (d) combining said slurry and said prepolymer whereby the water in said slurry reacts with said prepolymer to form a cellular polymer which binds said aggregate material.
Claim 15
Dependent Claim
190 words
A consolidated aggregate material in the form of an integral, resilient, water-permeable mass prepared by the method comprising the steps of: (a) adding to a polyether or polyester compound under substantially anhydrous conditions a stoichiometric excess of a compound containing at least two active isocyanate groups per molecule to initiate an exothermic condensation reaction between said polyether or polyester and said isocyanate compound, the temperature of said reactants being such that the temperature of the reactants after addition of isocyanate is less than or equal to about 120° C., the density of said isocyanate compound being greater than the density of said polyether or polyester compound and said isocyanate compound being added gradually to said polyether or polyester without substantial added mixing whereby a relatively dense isocyanate layer and a polyether or polyester layer overlying said isocyanate layer are formed; (b) allowing said reaction to proceed in order to form a urethane prepolymer; (c) forming an aqueous slurry of unconsolidated aggregate material; and, (d) combining said slurry and said prepolymer whereby the water in said slurry reacts with said prepolymer to form a cellular polymer which binds said aggregate material.
References Cited (Backward Citations)
US3373009A
Cited
US3479325A
Cited
US3814736A
Cited
US3805532A
Cited
US3805531A
Cited
US3805532B1
Cited
US3723393A
Cited
US3812619A
Cited
US4127515A
Cited
US4241537A
Cited
US4329436A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-01-22 | 1988-07-23 | 1989-01-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-01-22 | 1992-07-23 | 1993-01-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-01-22 | 1996-07-23 | 1997-01-22 | $7700.00 | Window Closed / Lapsed |