US4495228A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Hydraulic cement composition and method for use as protective coating for substrates
Assignee: Individual
•
Filing: 1982-11-16
•
Granted: 1985-01-22
•
Expires: 2002-11-16
Abstract
Abstract A corrosion resistant and fireproof coating for the protection of metal and sealing concrete, brick, mortar and other cementitious substrate by spraying or brushing a coating 4 to 30 mils thickness and allowing the coating to set until hard. Hydraulic cements are combined with selected inorganic minerals and a water reducer that are milled until they all pass through a 100 mesh or finer screen. The blended powder is combined with potable water that are mixed together just before application.
Inventors
- 👤 Charles E. Cornwell
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 23:36
CPC Classifications
C; C04; C04B; C04B28/00; C04B28/02; C04B35/00; C04B35/66; C04B2111/00; C04B2111/00474; C04B2111/00482; C04B2111/20; C04B2111/28; Y; Y02; Y02W; Y02W30/00; Y02W30/50; Y02W30/91
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
36 words
A corrosion resistant and fireproof coating composition consisting essentially of a hydraulic cement, water reducer, thixotropic agent, finely divided minerals, color pigments and combined with water to make a coating suitable for application on various substrates.
Claim 2
Dependent Claim
36 words
A corrosion resistant and fireproof coating composition consisting essentially of a hydraulic cement, water reducer, thixotropic agent, finely divided minerals, color pigments and combined with water to make a coating suitable for application on various substrates.
Claim 3
Dependent Claim
169 words
A composition according to claim 1, wherein said cement is portland or calcium aluminate; the water reducers are selected from the group consisting of polymers comprising the alkali metal salts of melamine sulfonic acid partially condensed with formaldehyde, the alkali metal salt of naphthalene sulfonic acid partially condensed with formaldehyde, and about 30-90 percent of the alkali metal salt of a high molecular weight condensation product of naphthalene-sulfonic acid and the balance 70-10 percent of the alkali salt of gluconic acid; the thixotropic agents are selected from the group consisting of, a synthetic percipitated amorphous hydrated silicon dioxide, a silica produced from silicon tetrachloride in a flame hydrolysis process with oxygen-hydrogen gas, amorphous silica percipitated as ultrafine, spherical particles in powder form; the finely divided minerals are selected from the group consisting of silica flour, amorphous silica, calcium metasilicate CaSiO 3 with acicular crystalline structure, fly ash, frit, mica and calcium carbonate; the color pigments are selected from the group consisting of titanium dioxide, iron oxides and chromium oxide.
Claim 4
Dependent Claim
193 words
A composition according to claim 1, wherein the dry components of the composition comprise in weight percent a mineral cement selected from the group consisting of portland or calcium aluminate, 100; a water reducer selected from the group consisting of polymers comprising the alkali metal salts of melamine sulfonic acid partially condensed with formaldehyde, the alkali metal salt of naphthalene sulfonic acid partially condensed with formaldehyde, and about 30-90 percent of the alkali metal salt of a high molecular weight condensation product of naphthalene-sulfonic acid and the balance 70-10 percent of the alkali salt of gluconic acid, 0.5-1.5; a thixotropic mineral selected from the group consisting of, a synthetic percipitated amorphous hydrated silicon dioxide, a silica produced from silicon tetrachloride in a flame hydrolysis with oxygen-hydrogen gas, amorphous silica percipitated as ultrafine, spherical particles in powder form, 0-0.5; a mineral aggregate of 100 mesh or finer selected from the group consisting of silica flour, 0-15; amorphous silica, 0-15; calcium metasilicate CaSiO 3 with acicular crystalline structure, 7-35; fly ash, 0-10; frit, 0-20; calcium carbonate, 0-10; a color pigment selected from the group consisting of titanium dioxide, 0-5; iron oxides, 0-3; chromium oxide, 0-3.
Claim 5
Dependent Claim
41 words
A process for coating a substrate with corrosion resistant and fireproof coating composition of about 4 mils to 40 mils thick comprising applying the coating composition of claim 1 to a substrate by air spraying, airless spraying, brushing or roller technique.
References Cited (Backward Citations)
US4088804A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-01-22 | 1988-07-23 | 1989-01-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-01-22 | 1992-07-23 | 1993-01-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-01-22 | 1996-07-23 | 1997-01-22 | $7700.00 | Window Closed / Lapsed |