Hydrocarbon conversion catalyst and process using said catalyst

Claim 2

A hydrocracking process comprising contacting a hydrocarbon feed containing substantial amounts of materials boiling above 95° C. in a reaction zone with hydrogen and a catalyst under hydrocracking conditions, wherein said catalyst comprises a composite containing: (A) a porous amorphous matrix selected from the group consisting of alumina-silica, alumina-silica-titania and alumina-silica-zirconia polygels, said polygel having an alumina-to-silica weight ratio in the range of from about 0.2-20 to 1, respectively; (B) a hydrogenation component of (1) nickel or cobalt or any combination thereof in an amount, calculated as metal, in the range of from about 1 to 10 weight percent of said matrix, and (2) molybdenum or tungsten, or any combination thereof, in an amount, calculated as metal in the range of from about 5 to 25 weight percent of said matrix, said hydrogenation component being (1) in the form of metal or oxide or sulfide or any combination thereof and (2) dispersed through said matrix; and (C) a finely divided intermediate pore size silicaceous crystalline molecular sieve component substantially in the ammonium or hydrogen form, said molecular sieve being (1) substantially free of such hydrogenation component, (2) dispersed through said matrix and (3) selected from the group consisting of (i) crystalline aluminosilicates of the ZSM series including crystalline admixtures of members of the ZSM series and (ii) essentially alumina-free silicates of the crystalline silica polymorph or chromia silicate or ferrosilicate families.

Claim 3

The process as in claim 1 wherein said matrix of said catalyst contains (1) at least 15 weight percent of silica, and (2) an amount of titania, calculated as metal, in the range of from about 1 to 10 weight percent and said composite contains an amount of said molecular sieve in the range of from about 1 to 50 weight percent and has a surface area above about 200 m 2 /gram.

Claim 4

The process as in claim 2 wherein said amount of molecular sieve is about 17%, said hydrogenating component is nickel and tungsten in amounts of about 7 and 17 weight percent, respectively, and wherein said matrix contains about 7 weight percent of titania.

Claim 5

A process as in claim 1 wherein said feed has a content of nitrogen-containing impurities, calculated as nitrogen, which is below about 10 ppmw.

Claim 6

A process as in claim 4 wherein said feed is a petroleum distillate and at least a fraction of the resulting product is a lube oil having, relative to said feed, an improved pour point.

Claim 7

A process as in claim 1 wherein said hydrocracking conditions are controlled so as to maintain a feed conversion level in the range of from about 5 to 75 volume percent.

Claim 8

A process as in claim 1 wherein said feed has an initial normal boiling point of at least about 315° C.

Claim 9

A process as in claim 5 wherein said distillate has a normal boiling point in the range of from about 315° C. to 590° C.

Claim 10

A process as in claim 1 wherein said hydrocarbon feed is selected from the group consisting of petroleum distillates, solvent deasphalted residua, and shale oils.

Claim 11

A process as in claim 4 wherein said catalyst is disposed downstream of a reaction zone in which a hydrocarbon feed is contacted under hydroprocessing conditions with an active hydrodenitrogenation catalyst.

Claim 12

A process as in claim 10 wherein said hydrodenitrogenation catalyst is disposed in a single reactor with said composite containing a molecular sieve component.

Claim 13

A process as in claim 11 wherein said reactor contains at least 2 parts by volume hydrodenitrogenation catalyst upstream of one part by volume of said composite containing a molecular sieve component.

Claim 14

A process as in claim 10, 11 or 12 in which said hydrodenitrification catalyst is a porous composite containing an inorganic matrix oxide selected from the group consisting of alumina, silica, magnesia, and mixtures thereof, and at least one hydrogenation component selected from Group VIB and Group VIII elements, present as metals, oxides or sulfides.

Claim 15

A hydrocracking process comprising contacting a hydrocarbon feed containing substantial amounts of materials boiling above 95° C., said feed having a content of nitrogen-containing impurities, calculated as nitrogen, which is below about 10 ppmw, in a reaction zone with hydrogen and a catalyst under hydrocracking conditions wherein said catalyst comprises a composite containing: (A) A porous amorphous matrix selected from the group consisting of alumina-silica, alumina-silica-titania and alumina-silica-zirconia polygels, said polygels having an alumina-silica weight ratio in the range of from about 0.2-20 to 1 respectively; (B) A hydrogenation component of (1) nickel in an amount, calculated as metal, in the range of from about 1 to 10 weight percent of said matrix, and (2) tungsten, in an amount calculated as metal, in the range of from about 5 to 25 weight percent of said matrix, said hydrogenation component being in the form of metal or oxide or sulfide or any combination thereof and (3) dispersed through said matrix; and (C) A finely divided intermediate pore size silicaceous crystalline molecular sieve component substantially in the ammonium or hydrogen form, said molecular sieve being (1) substantially free of such hydrogenation component, (2) dispersed through said matrix and (3) selected from the group consisting of (i) crystalline aluminosilicates of the ZSM series including crystalline admixtures of members of the ZSM series and (ii) essentially alumina-free silicates of the crystalline silica polymorphs or chromia silicate or ferrosilicate families.

Claim 16

A hydrocracking process comprising contacting a hydrocarbon feed containing substantial amounts of materials boiling above 95° C., said feed having a content of nitrogen-containing impurities, calculated as nitrogen, which is below about 10 ppmw, in a reaction zone with hydrogen and a catalyst under hydrocracking conditions wherein said catalyst comprises a composite containing: (A) A porous amorphous matrix selected from the group consisting of alumina-silica, alumina-silica-titania and alumina-silica-zirconia polygels, said polygels having an alumina-silica weight ratio in the range of from about 0.2-20 to 1 respectively; (B) A hydrogenation component of (1) nickel in an amount, calculated as metal, in the range of from about 1 to 10 weight percent of said matrix, and (2) tungsten, in an amount calculated as metal, in the range of from about 5 to 25 weight percent of said matrix, said hydrogenation component being in the form of metal or oxide or sulfide or any combination thereof and (3) dispersed through said matrix; and (C) A finely divided intermediate pore size silicaceous crystalline molecular sieve component substantially in the ammonium or hydrogen form, said molecular sieve being (1) substantially free of such hydrogenation component, (2) dispersed through said matrix and (3) selected from the group consisting of (i) crystalline aluminosilicates of the ZSM series including crystalline admixtures of members of the ZSM series and (ii) essentially alumina-free silicates of the crystalline silica polymorphs or chromia silicate or ferrosilicate families.

Claim 17

The process as in claim 14 wherein said matrix of said catalyst contains (1) at least 15 weight percent of silica, and (2) an amount of titania, calculated as metal, in the range of from about 1 to 10 weight percent and said composite contains an amount of said molecular sieve in the range of from about 1 to 50 weight percent and has a surface area above about 200 m 2 /gram.

Claim 18

The process as in claim 15 wherein said amount of molecular sieve is about 17%, said hydrogenating component is nickel and tungsten in amounts of about 7 and 17 weight percent, respectively, and wherein said matrix contains about 7 weight percent of titania.

Claim 19

A process as in claim 14 wherein said feed is a petroleum distillate and at least a fraction of the resulting product is a lube oil having, relative to said feed, an improved pour point.

Claim 20

A process as in claim 14 wherein said hydrocracking conditions are controlled so as to maintain a feed conversion level in the range of from about 5 to 75 volume percent.

Claim 21

A process as in claim 14 wherein said feed has an initial normal boiling point of at least about 315° C.

Claim 22

A process as in claim 17 wherein said distillate has a normal boiling point in the range of from about 315° C. to 590° C.

Claim 23

A process as in claim 14 wherein said catalyst is disposed downstream of a reaction zone in which a hydrocarbon feed is contacted under hydroprocessing conditions with an active hydrodenitrogenation catalyst.

Claim 24

A process as in claim 21, in which said hydrodenitrification catalyst is a porous composite containing an inorganic matrix oxide selected from the group consisting of alumina, silica, magnesia, and mixtures thereof, and at least one hydrogenation component selected from Group VIB and Group VIII elements, present as metals, oxides or sulfides.

Claim 25

A process as in claim 1, 4, 14 or 22 wherein said intermediate pore silicaceous crystalline molecular sieve is an essentially alumina-free silicate.

Claim 26

A process as in claim 23 wherein said molecular sieve has a silica-alumina atomic ratio of greater than 500-1.

Claim 27

A process as in claim 23 wherein said molecular sieve is silicalite.

Claim 28

A process as in claim 23 wherein said molecular sieve is substantially in the hydrogen form.

Claim 29

A process according to claim 1 wherein the molecular sieve component is a member of the ZSM series.

Claim 30

A process according to claim 1 wherein the molecular sieve component is silicalite.

Claim 31

A process according to claim 1 wherein the molecular sieve component is a chromia silicate.

Claim 32

A process according to claim 1 wherein the chromia silicate component is a CZM zeolite.

Claim 33

A process according to claim 1 wherein the molecular sieve component has an effective pore size range from about 5 to about 6.5 Angstroms.