Production of age hardenable aluminum extruded sections
Assignee: Rio Tinto Alcan International Ltd
•
Filing: 1982-12-03
•
Granted: 1985-01-22
•
Expires: 2002-12-03
Abstract
Abstract In the thermal ageing of extruded sections of age-hardenable aluminum alloys the sections are progressed through a system having an initial low temperature zone and a subsequent high temperature zone. In order to secure uniform ageing the sections are progressed in a direction transverse to their length and conveniently are arranged in a single layer and spaced apart to ensure acceptably uniform rate of heating to ageing temperature.
Inventors
- 👤 Walter Bennett
- 👤 John H. Ablewhite
- 👤 Anthony J. Bryant
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 01:44
CPC Classifications
C; C22; C22F; C22F1/00; C22F1/04; C22F1/05
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
87 words
In a method of producing extruded sections of an age hardenable alloy, in which extruded sections are extruded onto a run out table and laterally moved therefrom to a cooling and stretching station the improvement which comprises progressing the cooled and stretched sections into, through and out of a relatively low temperature first thermal ageing zone while travelling in a direction transverse to their length and into, through and out of a second, higher ageing temperature zone also while travelling in a direction transverse to their length.
Claim 2
Dependent Claim
87 words
In a method of producing extruded sections of an age hardenable alloy, in which extruded sections are extruded onto a run out table and laterally moved therefrom to a cooling and stretching station the improvement which comprises progressing the cooled and stretched sections into, through and out of a relatively low temperature first thermal ageing zone while travelling in a direction transverse to their length and into, through and out of a second, higher ageing temperature zone also while travelling in a direction transverse to their length.
Claim 3
Dependent Claim
25 words
A method according to claim 1 in which said extruded sections are progressed individually and successively through said zones in one or more discrete layers.
Claim 4
Dependent Claim
50 words
A method according to claim 1 in which the rate of travel through the second zone is controllable with relation to the rate of travel in the first zone in order to control the dwell time in the second zone in relation to the dwell time in the first zone.
Claim 5
Dependent Claim
46 words
A method according to claim 1 in which the extrusions are progressed through a relatively low temperature zone held at 160°-200° C. during a period of 45-60 minutes and are progressed through a high temperature zone held at 230°-260° C. during a period of 10-20 minutes.
Claim 6
Dependent Claim
51 words
A method according to claim 1 in which said sections are progressed through said zones while secured to spline members arranged substantially perpendicular to said sections, said splines being in a vertical position and said sections being spaced from each other and lying one above the other in the vertical direction.
Claim 7
Dependent Claim
92 words
A method according to claim 1 further comprising extruding aluminium magnesium silicide alloy sections onto a table, moving said sections laterally on said table, cooling and stretching said sections, advancing said sections longitudinally to a sawing station and sawing said sections to desired sawn lengths at said sawing station, slewing said sawn lengths through an angle of the order of 90° at the sawing station and then advancing said sawn lengths of extruded section through said low temperature zone and high temperature zone while arranged in a direction transverse to their lengths.
References Cited (Backward Citations)
US1920090A
Cited
US3018885A
Cited
US3198676A
Cited
US3668910A
Cited
JPS5039412A
Cited
US4212451A
Cited
US4030947A
Cited
SU724600A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-01-22 | 1988-07-23 | 1989-01-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-01-22 | 1992-07-23 | 1993-01-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-01-22 | 1996-07-23 | 1997-01-22 | $7700.00 | Window Closed / Lapsed |