Method for making fluorescent light-collectors
Assignee: BLUENERGY SOLARWIND Inc
•
Filing: 1983-09-19
•
Granted: 1985-01-08
•
Expires: 2003-09-19
Abstract
Abstract A method for making a light-collector of a transparent plastic and a fluorescent dye, wherein the monomers forming transparent plastics are mass-prepolymerized in the presence of radical catalysts and the fluorescent dye is added before, during or at the end of prepolymerization, and then polymerizing the mixture to completion by adding another catalyst, also at pressures of from 2 to 20 bars and at temperatures of from 50 DEG to 160 DEG C., and the use of the light-collector thus produced in combination with photovoltaic elements, preferably based on Ga/As or Si.
Inventors
- 👤 Uwe Claussen
- 👤 Josef Merten
- 👤 Harry Rohr
- 👤 Bernd Melchior
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 12:19
CPC Classifications
H; H10; H10F; H10F77/00; H10F77/40; H10F77/42; H10F77/45; C; C08; C08F; C08F2/00; C08F2/44; Y; Y02; Y02E; Y02E10/00; Y02E10/50; Y02E10/52
Claims Analysis
Total Claims: 3
Claim 1
Independent Claim
121 words
A method for making a light-collector from a transparent plastic containing a fluorescent dye, wherein the monomers forming transparent plastics are mass-prepolymerized at temperatures of from 50° to 160° C. and under pressures of from 2 to 20 bars using a radical catalyst from the group consisting of percarbonates, acyl sulfonyl peroxides, perketones, or azodiiso butyric acid esters, and the fluorescent dye is added either before, during, or at the end of prepolymerization, and the mixture is then polymerized to completion after adding another catalyst from the group consisting of percarbonates, acyl sulfonyl peroxides, perketones, azoisobutyronitrile or azoisobutyric acid esters, hydroperoxides, and perketals, also under pressures of from 2 to 20 bars and at temperatures of from 50° to 160° C.
Claim 2
Independent Claim
121 words
A method for making a light-collector from a transparent plastic containing a fluorescent dye, wherein the monomers forming transparent plastics are mass-prepolymerized at temperatures of from 50° to 160° C. and under pressures of from 2 to 20 bars using a radical catalyst from the group consisting of percarbonates, acyl sulfonyl peroxides, perketones, or azodiiso butyric acid esters, and the fluorescent dye is added either before, during, or at the end of prepolymerization, and the mixture is then polymerized to completion after adding another catalyst from the group consisting of percarbonates, acyl sulfonyl peroxides, perketones, azoisobutyronitrile or azoisobutyric acid esters, hydroperoxides, and perketals, also under pressures of from 2 to 20 bars and at temperatures of from 50° to 160° C.
Claim 3
Dependent Claim
18 words
A method as claimed in claim 1, wherein coumarin derivatives or perylene compounds are used as the dye.
References Cited (Backward Citations)
US4260219A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-01-08 | 1988-07-09 | 1989-01-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-01-08 | 1992-07-09 | 1993-01-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-01-08 | 1996-07-09 | 1997-01-08 | $7700.00 | Window Closed / Lapsed |