Process for the preparation of cellulose ethers from ammonia-activated cellulose
Assignee: Hoechst AG
•
Filing: 1983-10-27
•
Granted: 1985-01-01
•
Expires: 2003-10-27
Abstract
Abstract A process is disclosed for the preparation of water-soluble cellulose ethers, comprising the steps of activating cellulose with ammonia, alkalizing the activated cellulose, and etherifying the alkali cellulose. In the process, the activated cellulose is alkalized in the presence of ammonia and, optionally, in the presence of an organic solvent, and the ammonia is removed from the alkali cellulose in the presence of the alkalizing agent and, optionally, the organic solvent. Etherification proceeds in a medium which contains at least portions of said organic solvent. The organic solvent comprises, in particular, an alkanol which has from 1 to 6 carbon atoms. For the etherification step, carboxymethylation or hydroxyethylation is preferred.
Inventors
- 👤 Karl Bredereck
- 👤 Emy Togelang
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 16:32
CPC Classifications
C; C08; C08B; C08B1/00; C08B1/08; C08B11/00
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
76 words
A process for the preparation of water-soluble cellulose ethers, comprising the steps of: (a) activating cellulose with ammonia; (b) alkalizing the activated cellulose with an alkalizing agent in the presence of ammonia, said alkalizing agent comprising an aqueous solution of an alkali metal hydroxide; (c) removing the ammonia from the alkali cellulose in the presence of the alkalizing agent; and (d) etherifying the alkali cellulose with an etherifying agent in the presence of an organic solvent.
Claim 2
Dependent Claim
76 words
A process for the preparation of water-soluble cellulose ethers, comprising the steps of: (a) activating cellulose with ammonia; (b) alkalizing the activated cellulose with an alkalizing agent in the presence of ammonia, said alkalizing agent comprising an aqueous solution of an alkali metal hydroxide; (c) removing the ammonia from the alkali cellulose in the presence of the alkalizing agent; and (d) etherifying the alkali cellulose with an etherifying agent in the presence of an organic solvent.
Claim 3
Dependent Claim
15 words
A process according to claim 1, wherein said organic solvent is present during step (b).
Claim 4
Dependent Claim
23 words
A process according to claim 1, further comprising the adding of said organic solvent during removal of said ammonia from said alkali cellulose.
Claim 5
Dependent Claim
20 words
A process according to claim 3, wherein said organic solvent is added after removal of the bulk of said ammonia.
Claim 6
Dependent Claim
20 words
A process according to claim 1, wherein said organic solvent comprises an alkanol having from 1 to 6 carbon atoms.
Claim 7
Dependent Claim
18 words
A process according to claim 1, wherein said activation of the cellulose is carried out using liquid ammonia.
Claim 8
Dependent Claim
23 words
A process according to claim 6, wherein said activating step is carried out at a temperature ranging from about -33° to -60° C.
Claim 9
Dependent Claim
13 words
A process according to claim 1, wherein said etherifying comprises carboxymethylation or hydroxyethylation.
Claim 10
Dependent Claim
26 words
A process according to claim 8, wherein said etherifying agent is selected from the group consisting of monochloroacetic acid, salts and esters thereof, and ethylene oxide.
Claim 11
Dependent Claim
22 words
A process according to claim 8, wherein said carboxymethylation results in a sodium carboxymethyl cellulose having a DS from 0.3 to 0.8.
Claim 12
Dependent Claim
17 words
A process according to claim 1, wherein an aqueous NaOH solution is used as said alkalizing agent.
Claim 13
Dependent Claim
31 words
A process according to claim 1, wherein the amount of said alkali metal hydroxide used in step (b) is in the range of 0.6 to 6.0 moles per mole of cellulose.
Claim 14
Dependent Claim
30 words
A process according to claim 1, wherein the amount of said etherifying agent used in step (d) is in the range of 0.1 to 10 moles per mole of cellulose.
Claim 15
Dependent Claim
37 words
A process according to claim 1, wherein step (b) is run at a temperature between about 15° and 30° C., and step (d) is run at a temperature ranging from about 30° C. up to 90° C.
Claim 16
Dependent Claim
20 words
A process according to claim 1, wherein step (b) is carried out in the presence of an excess of water.
References Cited (Backward Citations)
US1682294A
Cited
CA546633A
Cited
US2290888A
Cited
GB463056A
Cited
US2110526A
Cited
US2294924A
Cited
US2145273A
Cited
US2157083A
Cited
US2294925A
Cited
US2308692A
Cited
US2296829A
Cited
US2671780A
Cited
US2729535A
Cited
US3069409A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-01-01 | 1988-07-02 | 1989-01-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-01-01 | 1992-07-02 | 1993-01-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-01-01 | 1996-07-02 | 1997-01-01 | $7700.00 | Window Closed / Lapsed |