Semiconductive ceramic materials with a voltage-dependent nonlinear resistance, and process for preparation

Assignee: Taiyo Yuden Co Ltd
•
Filing: 1983-12-16
•
Granted: 1984-12-25
•
Expires: 2003-12-16
📄 Original PDF 🌐 Google Patents 🔄 Sync Now

Abstract

Abstract Semiconductive ceramic materials suitable for use in varistors, consisting essentially of a major proportion of Sr( 1-x )Ca x TiO 3 , where x is from about 0.01 to about 0.50, the balance being at least one of Nb 2 O 5 , Ta 2 O 5 , WO 3 , La 2 O 3 , CeO 2 , Nd 2 O 3 , Y 2 O 3 , Sm 2 O 3 , Pr 6 O 11 and Dy 2 O 3 , and Na 2 O. The ceramic materials may further comprise a minor proportion of at least one of Ag 2 O, CuO, MnO 2 and SiO 2 , and/or a minor proportion of Al 2 O 3 . For the fabrication of ceramic bodies of the above compositions there are prepared mixtures of the noted ingredients in powdered form in various possible combinations, plus an organic binder. The mixtures are molded under pressure into desired shape. The moldings are first fired in a reductive or neutral atmosphere and then refired in an oxidative atmosphere. Na 2 O can be included in the initial mixtures in the form of Na 2 O itself and/or other Na compound such as NaF. Alternatively, either Na 2 O itself or NaF is pasted and coated on the moldings after the initial firing thereof. The subsequent refiring of the coated moldings causes thermal diffusion of Na 2 O therein.

Inventors

  • 👤 Masaru Masuyama
  • 👤 Susumu Hirooka
  • 👤 Nobutatsu Yamaoka

Bibliographic Details

Application Number —
Jurisdiction US
Data Source google_patents
Last Synchronized 2026-11-06 11:11
CPC Classifications
H; H01; H01C; H01C7/00; H01C7/10; H01C7/105; H01C7/108; H01C7/115; C; C04; C04B; C04B35/00; C04B35/01; C04B35/46; C04B35/462; C04B35/465; C04B35/47

Claims Analysis

Total Claims: 9
Claim 1
Independent Claim 197 words
A process for fabricating bodies of a semiconductive ceramic material with a voltage-dependent nonlinear resistance, which comprises providing a mixture of 100 mole parts of Sr.sub.(1-x) Ca x TiO 3 in finely divided form, where x is a numeral from about 0.01 to about 0.50, from about 0.01 to about 3.00 mole parts of at least one metal oxide in finely divided form selected from the group consisting of Nb 2 O 5 , Ta 2 O 5 , WO 3 , La 2 O 3 , CeO 2 , Nd 2 O 3 , Y 2 O 3 , Sm 2 O 3 , Pr 6 O 11 and Dy 2 O 3 , and an organic binder, forming the mixture into moldings of desired shape and size, firing the moldings in a temperature range from about 1300° C. to about 1500° C. in a nonoxidative atmosphere, refiring thee moldings in a temperature range from about 850° C. to about 1350° C. in an oxidative atmosphere to complete ceramic bodies, and adding from about 0.02 to about 2.50 mole parts of Na 2 O to the ceramic bodies not later than the refiring of the moldings.
Claim 2
Dependent Claim 197 words
A process for fabricating bodies of a semiconductive ceramic material with a voltage-dependent nonlinear resistance, which comprises providing a mixture of 100 mole parts of Sr.sub.(1-x) Ca x TiO 3 in finely divided form, where x is a numeral from about 0.01 to about 0.50, from about 0.01 to about 3.00 mole parts of at least one metal oxide in finely divided form selected from the group consisting of Nb 2 O 5 , Ta 2 O 5 , WO 3 , La 2 O 3 , CeO 2 , Nd 2 O 3 , Y 2 O 3 , Sm 2 O 3 , Pr 6 O 11 and Dy 2 O 3 , and an organic binder, forming the mixture into moldings of desired shape and size, firing the moldings in a temperature range from about 1300° C. to about 1500° C. in a nonoxidative atmosphere, refiring thee moldings in a temperature range from about 850° C. to about 1350° C. in an oxidative atmosphere to complete ceramic bodies, and adding from about 0.02 to about 2.50 mole parts of Na 2 O to the ceramic bodies not later than the refiring of the moldings.
Claim 3
Dependent Claim 32 words
A process as defined in claim 1, wherein the Na 2 O is included in the initially provided mixture in the form of at least one sodium compound in finely divided form.
Claim 4
Dependent Claim 50 words
A process as defined in claim 1, wherein the Na 2 O is thermally diffused in the moldings by forming a layer of at least one sodium compound on each molding after the firing thereof and then by refiring the moldings together with the layers of the sodium compound thereon.
Claim 5
Dependent Claim 25 words
A process as defined in claim 2 or 3, wherein the sodium compound is selected from the group consisting of Na 2 O and NaF.
Claim 6
Dependent Claim 33 words
A process as defined in claim 3, wherein the moldings together with the layers of the sodium compound thereon are refired in a temperature range from about 900° C. to about 1300° C.
Claim 7
Dependent Claim 48 words
A process as defined in claim 1, 2 or 3, wherein the mixture further comprises from about 0.01 to about 3.00 mole parts of at least one oxide in finely divided form selected from the group consisting of Ag 2 O, CuO, MnO 2 and SiO 2 .
Claim 8
Dependent Claim 29 words
A process as defined in claim 6, wherein the mixture further comprises from about 0.01 to about 1.50 mole parts of Al 2 O 3 in finely divided form.
Claim 9
Dependent Claim 32 words
A process as defined in claim 1, 2 or 3, wherein the mixture further comprises from about 0.01 to about 1.50 mole parts of Al 2 O 3 in finely divided form.

References Cited (Backward Citations)

US4073846A Cited
US4339511A Cited
EP0044981A2 Cited
US4380559A Cited

USPTO Annuity & Maintenance Windows

Annuity Stage Window Opens Payment Deadline Surcharge Period Until Estimated Fee Status
3.5 Years (Year 4) 1987-12-25 1988-06-25 1988-12-25 $2000.00 Window Closed / Lapsed
7.5 Years (Year 8) 1991-12-25 1992-06-25 1992-12-25 $3760.00 Window Closed / Lapsed
11.5 Years (Year 12) 1995-12-25 1996-06-25 1996-12-25 $7700.00 Window Closed / Lapsed

Assigned Categories & Tags

No categories assigned to this patent yet.

Assign Category Tag