Method for forming glass fibers
Assignee: Owens Corning Fiberglas Technology Inc
•
Filing: 1983-04-11
•
Granted: 1984-12-18
•
Expires: 2003-04-11
Abstract
Abstract A glass fiber attenuation apparatus and process wherein molten glass is supplied from a molten glass body to an orifice plate at substantially atmospheric pressure to prevent molten glass flow through an orifice at which attenuation has ceased, thus permitting continuation of the attenuation process despite breakouts at individual orifices. The preferred embodiment of the method includes the steps of cooling the orifice plate undersurface to a non-wetting temperature and delivering molten glass to the orifice plate at a pressure less than the internal, surface tension-generated pressure of any bead formed on the undersurface of the orifice plate upon attenuation cessation at that orifice. The preferred embodiment of the apparatus includes a perforate pressure plate immersed in the body of molten glass and superimposed over the orifice plate to effect a pressure drop upon normal attenuation flow which is sufficient to reduce the pressure immediately above the orifice plate to substantially atmospheric pressure or, in any event, to a pressure less than the internal pressure of a bead or globule formed on attenuation cessation at an orifice. The orifice plate may be of either the planar, non-tipped type or of the tipped type, and the orifice plate may be cooled to the appropriate temperature either by gas flow cooling directed at the undersurface of the orifice plate or by fin shields.
Inventors
- 👤 Lawrence J. Grubka
- 👤 Clarence E. Fracker, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 06:45
CPC Classifications
C; C03; C03B; C03B37/00; C03B37/01; C03B37/02; C03B37/08; C03B37/081; C03B37/083; C03B37/09; C03B37/091
Claims Analysis
Total Claims: 34
Claim 1
Independent Claim
86 words
The method of forming continuous glass filaments comprising: (1) delivering forming cones of molten glass from spaced-apart orifices in a wall retaining a body of molten glass; (2) attenuating a continuous glass filament from each of the cones; and (3) reducing the pressure of the molten glass at the orifices to a pressure less than the internal pressure of a bead formed at an orifice upon the cessation of filament attenuation at that orifice, but greater than the internal pressure of the forming cones during attenuation.
Claim 2
Independent Claim
86 words
The method of forming continuous glass filaments comprising: (1) delivering forming cones of molten glass from spaced-apart orifices in a wall retaining a body of molten glass; (2) attenuating a continuous glass filament from each of the cones; and (3) reducing the pressure of the molten glass at the orifices to a pressure less than the internal pressure of a bead formed at an orifice upon the cessation of filament attenuation at that orifice, but greater than the internal pressure of the forming cones during attenuation.
Claim 3
Dependent Claim
27 words
The method of claim 1 wherein the step (3) is carried out by delivering the molten glass through a flow resistance located closely above the orificed wall.
Claim 4
Dependent Claim
96 words
In a method of attenuating glass fibers from a body of molten glass overlying an orifice plate having a plurality of orifices therein from which the molten glass is attenuated as fibers from forming cones, the improvement comprising the step of reducing the pressure of the body of glass immediately over the orifice plate to a pressure which (a) is less than the internal pressure of a bead formed upon attenuation interruption at an orifice of said plate and (b) is greater than the pressure internally of the cone at said orifice during steady state attenuation.
Claim 5
Dependent Claim
96 words
In a method of attenuating glass fibers from a body of molten glass overlying an orifice plate having a plurality of orifices therein from which the molten glass is attenuated as fibers from forming cones, the improvement comprising the step of reducing the pressure of the body of glass immediately over the orifice plate to a pressure which (a) is less than the internal pressure of a bead formed upon attenuation interruption at an orifice of said plate and (b) is greater than the pressure internally of the cone at said orifice during steady state attenuation.
Claim 6
Dependent Claim
13 words
The method of claim 3 wherein glass fibers are continuously attenuated as filaments.
Claim 7
Dependent Claim
13 words
The method of claim 3 wherein glass fibers are discontinuously attenuated as filaments.
Claim 8
Independent Claim
102 words
The method of continuously attenuating glass fibers in a steady state operation from a body of molten glass overlying an orifice plate having a plurality of vertical orifices therein, comprising the steps of (1) reducing the pressure of the body of glass immediately over the orifice plate to a pressure less than the internal pressure of a bead formed upon attenuation interruption at an orifice of said plate, (2) forming a forming cone at each orifice, and (3) attenuation a fiber from each cone, the pressure of step (1) being greater than the internal pressure of the cones during steady state attenuation.
Claim 9
Independent Claim
102 words
The method of continuously attenuating glass fibers in a steady state operation from a body of molten glass overlying an orifice plate having a plurality of vertical orifices therein, comprising the steps of (1) reducing the pressure of the body of glass immediately over the orifice plate to a pressure less than the internal pressure of a bead formed upon attenuation interruption at an orifice of said plate, (2) forming a forming cone at each orifice, and (3) attenuation a fiber from each cone, the pressure of step (1) being greater than the internal pressure of the cones during steady state attenuation.
Claim 10
Dependent Claim
25 words
The method as defined in claim 6, wherein the orifice plate is tipless and has a lower surface at which the forming cones are formed.
Claim 11
Dependent Claim
26 words
The method as defined in claim 6 wherein the orifice plate is provided with tips defining the individual orifices at which the forming cones are formed.
Claim 12
Dependent Claim
39 words
The method as defined in claim 6, wherein the pressure reducing step is carried out by flowing glass from the body of molten glass through an apertured plate located within the body and spaced vertically above the orifice plate.
Claim 13
Independent Claim
250 words
A method of making glass fibers, comprising the steps of: (1) providing a body of molten glass of appreciable depth over an orifice plate having a plurality of vertical orifices therethrough; (2) flowing molten glass from said body through each orifice to form an individual bead at the outlet of each orifice, the molten glass pressure above the orifice plate being greater than the internal pressure of the beads; (3) attenuating the beads to form a fiber cone at each orifice and a fiber drawn from each cone; (4) during the performance of step (3), reducing the pressure on the molten glass immediately above the plate to a pressure less than the internal pressure of a bead formed at an orifice upon interruption of fiber attenuation at that orifice but greater than the internal pressure of the cones during attenuation; (5) cooling the undersurface of the orifice plate to temperature (a) which is less than the temperature of the glass above the orifice plate and (b) which is less than the temperature at which the molten glass will flood across the orifice plate; and (6) in the event of fiber forming interruption at any given orifice, converting the cone at said given orifice into a globule at the outlet of the orifice because of the glass surface tension which causes a positive pressure interiorly of the globule to prevent the flow of glass through the orifice from the glass overlying the orifice plate at the reduced pressure of step (4).
Claim 14
Independent Claim
250 words
A method of making glass fibers, comprising the steps of: (1) providing a body of molten glass of appreciable depth over an orifice plate having a plurality of vertical orifices therethrough; (2) flowing molten glass from said body through each orifice to form an individual bead at the outlet of each orifice, the molten glass pressure above the orifice plate being greater than the internal pressure of the beads; (3) attenuating the beads to form a fiber cone at each orifice and a fiber drawn from each cone; (4) during the performance of step (3), reducing the pressure on the molten glass immediately above the plate to a pressure less than the internal pressure of a bead formed at an orifice upon interruption of fiber attenuation at that orifice but greater than the internal pressure of the cones during attenuation; (5) cooling the undersurface of the orifice plate to temperature (a) which is less than the temperature of the glass above the orifice plate and (b) which is less than the temperature at which the molten glass will flood across the orifice plate; and (6) in the event of fiber forming interruption at any given orifice, converting the cone at said given orifice into a globule at the outlet of the orifice because of the glass surface tension which causes a positive pressure interiorly of the globule to prevent the flow of glass through the orifice from the glass overlying the orifice plate at the reduced pressure of step (4).
Claim 15
Dependent Claim
16 words
A method as defined in claim 10, wherein the horizontal orifice plate is planar and tipless.
Claim 16
Dependent Claim
63 words
A method as defined in claim 10, wherein step (4) is carried out by flowing molten glass from said body through a perforate pressure plate immersed in said body and located above the orifice plate and imposing a pressure drop in the flow to the orifice plate sufficient to reduce the pressure in the body above the orifice plate to substantially atmospheric pressure.
Claim 17
Dependent Claim
45 words
A method as defined in claim 12, wherein the orifice plate is planar and tipless and the step (5) is carried out by electrically heating both the pressure plate and the orifice plate and flowing a coolant gas across the undersurface of said orifice plate.
Claim 18
Independent Claim
136 words
A method of making glass fibers, comprising the steps of: (1) flowing molten glass at a first flow rate through an orifice to form an individual bead at the outlet of the orifice; (2) attenuating the bead to form a forming cone and a filament; (3) increasing the flow rate to a second flow rate through the orifice while simultaneously reducing the pressure of the molten glass to a pressure (a) less than the internal pressure of a bead formed at the orifice upon interruption of attenuation at that orifice and (b) greater than the internal pressure of said cone during the performance of step (2); and (4) in the event of fiber forming interruption at the orifice, utilizing the internal pressure of the resultant bead to prevent the flow of molten glass through the orifice.
Claim 19
Independent Claim
136 words
A method of making glass fibers, comprising the steps of: (1) flowing molten glass at a first flow rate through an orifice to form an individual bead at the outlet of the orifice; (2) attenuating the bead to form a forming cone and a filament; (3) increasing the flow rate to a second flow rate through the orifice while simultaneously reducing the pressure of the molten glass to a pressure (a) less than the internal pressure of a bead formed at the orifice upon interruption of attenuation at that orifice and (b) greater than the internal pressure of said cone during the performance of step (2); and (4) in the event of fiber forming interruption at the orifice, utilizing the internal pressure of the resultant bead to prevent the flow of molten glass through the orifice.
Claim 20
Dependent Claim
259 words
In a method of making glass fibers, the steps of: (1) forming a pool of molten glass in a bushing over an orifice plate having a plurality of orifices therein and an intermediate perforate plate immersed in said pool and overlying said orifice plate; (2) initially flowing molten glass through the intermediate plate and said orifice plate at a pressure sufficient to extrude a globular bead at each orifice; (3) attenuating said globular beads to provide a forming cone at each orifice of said orifice plate and to draw a fiber from each such cone, while maintaining the orifice plate at a temperature at which the cones will not flood across the lower surface of the orifice plate; (4) drawing fibers in a steady state operation with appreciable downward flow of molten glass through said intermediate plate reducing the pressure of the molten glass above the orifice plate to a pressure less than the internal pressure of a bead formed at an orifice upon interruption of fiber drawing at that orifice; and (5) in the event of breakage of an individual fiber; (a) a globular bead is formed at the corresponding orifice because of the molten glass surface tension, (b) the surface tension generates a positive pressure internally of said globular bead which is greater than the pressure above the orifice plate, and (c) the greater internal pressure of said globular bead prevents the flow of glass into the bead from the glass above the orifice plate and prevents bead drop and orifice plate flooding due to bead growth.
Claim 21
Dependent Claim
259 words
In a method of making glass fibers, the steps of: (1) forming a pool of molten glass in a bushing over an orifice plate having a plurality of orifices therein and an intermediate perforate plate immersed in said pool and overlying said orifice plate; (2) initially flowing molten glass through the intermediate plate and said orifice plate at a pressure sufficient to extrude a globular bead at each orifice; (3) attenuating said globular beads to provide a forming cone at each orifice of said orifice plate and to draw a fiber from each such cone, while maintaining the orifice plate at a temperature at which the cones will not flood across the lower surface of the orifice plate; (4) drawing fibers in a steady state operation with appreciable downward flow of molten glass through said intermediate plate reducing the pressure of the molten glass above the orifice plate to a pressure less than the internal pressure of a bead formed at an orifice upon interruption of fiber drawing at that orifice; and (5) in the event of breakage of an individual fiber; (a) a globular bead is formed at the corresponding orifice because of the molten glass surface tension, (b) the surface tension generates a positive pressure internally of said globular bead which is greater than the pressure above the orifice plate, and (c) the greater internal pressure of said globular bead prevents the flow of glass into the bead from the glass above the orifice plate and prevents bead drop and orifice plate flooding due to bead growth.
Claim 22
Dependent Claim
13 words
The method of claim 15, wherein the orifice plate is planar and non-tipped.
Claim 23
Independent Claim
96 words
The method of preventing bead drop during the attenuation of glass filaments comprising: (a) delivering molten glass to the upper surface of an orifice plate having orifices and issuing streams of molten glass downwardly through said orifices; (b) attenuating glass filaments from the streams; and (c) during the performance of step (a) reducing the pressure of the molten glass during attenuation to an extent such that, upon a filament break at one of the orifices, the flow of molten glass from said orifice stops, yet the pressure is sufficient for fiber attenuation at the other orifices.
Claim 24
Independent Claim
96 words
The method of preventing bead drop during the attenuation of glass filaments comprising: (a) delivering molten glass to the upper surface of an orifice plate having orifices and issuing streams of molten glass downwardly through said orifices; (b) attenuating glass filaments from the streams; and (c) during the performance of step (a) reducing the pressure of the molten glass during attenuation to an extent such that, upon a filament break at one of the orifices, the flow of molten glass from said orifice stops, yet the pressure is sufficient for fiber attenuation at the other orifices.
Claim 25
Independent Claim
126 words
The method of preventing bead drop during the attenuation of glass filaments comprising: (a) flowing molten glass from a body of such glass downwardly through a plurality of individual orifices, the molten glass issuing from each orifice as a continuous stream; (b) attenuating each stream into a glass filament; and (c) during the performance of step (a), flowing the molten glass downwardly through a perforate pressure plate located in the body of glass above the orifices, the flow of molten glass through said plate being sufficient to feed glass during attenuation, but reducing the pressure of the molten glass beneath the plate to an extent such that, upon a filament break at one of the orifices, the flow of molten glass from said one orifice ceases.
Claim 26
Independent Claim
126 words
The method of preventing bead drop during the attenuation of glass filaments comprising: (a) flowing molten glass from a body of such glass downwardly through a plurality of individual orifices, the molten glass issuing from each orifice as a continuous stream; (b) attenuating each stream into a glass filament; and (c) during the performance of step (a), flowing the molten glass downwardly through a perforate pressure plate located in the body of glass above the orifices, the flow of molten glass through said plate being sufficient to feed glass during attenuation, but reducing the pressure of the molten glass beneath the plate to an extent such that, upon a filament break at one of the orifices, the flow of molten glass from said one orifice ceases.
Claim 27
Independent Claim
89 words
The method of preventing bead drop during the attenuation of glass filaments, comprising: (a) flowing molten glass through a flow resistance to and through a plurality of orifices in an orifice plate; (b) attenuating a glass fiber at each orifice; and (c) the pressure of molten glass between said flow resistance and said orifice plate being sufficient for fiber attenuation during the performance of steps (a) and (b) but being insufficient to flow glass through a given one of said orifices should attenuation be interrupted at said given orifice.
Claim 28
Independent Claim
89 words
The method of preventing bead drop during the attenuation of glass filaments, comprising: (a) flowing molten glass through a flow resistance to and through a plurality of orifices in an orifice plate; (b) attenuating a glass fiber at each orifice; and (c) the pressure of molten glass between said flow resistance and said orifice plate being sufficient for fiber attenuation during the performance of steps (a) and (b) but being insufficient to flow glass through a given one of said orifices should attenuation be interrupted at said given orifice.
Claim 29
Dependent Claim
79 words
In a method of making glass fibers wherein molten glass is supplied to the orifices of an orifice plate, and a glass fiber is attenuated at each orifice, the improvement of preventing bead drop during fiber attenuation by supplying molten glass to said orifices at a pressure which is sufficient to feed glass during attenuation, but which is less than the internal pressure of a bead formed at any one orifice upon interruption of attenuation at said one orifice.
Claim 30
Dependent Claim
79 words
In a method of making glass fibers wherein molten glass is supplied to the orifices of an orifice plate, and a glass fiber is attenuated at each orifice, the improvement of preventing bead drop during fiber attenuation by supplying molten glass to said orifices at a pressure which is sufficient to feed glass during attenuation, but which is less than the internal pressure of a bead formed at any one orifice upon interruption of attenuation at said one orifice.
Claim 31
Independent Claim
75 words
The method of making glass filaments comprising: (a) flowing molten glass downwardly through a pressure resistance and then through a plurality of orifices to issue molten glass from the orifices as individual streams; (b) attenuating each of said streams into a filament; and (c) the pressure of the molten glass at each individual orifice being sufficient to fed glass during attenuation, but insufficient to flow molten glass through that orifice in the absence of attenuation.
Claim 32
Independent Claim
75 words
The method of making glass filaments comprising: (a) flowing molten glass downwardly through a pressure resistance and then through a plurality of orifices to issue molten glass from the orifices as individual streams; (b) attenuating each of said streams into a filament; and (c) the pressure of the molten glass at each individual orifice being sufficient to fed glass during attenuation, but insufficient to flow molten glass through that orifice in the absence of attenuation.
Claim 33
Dependent Claim
80 words
In a method of making glass fibers wherein molten glass is supplied to the orifices of an orifice plate, the improvment of preventing bead drop during fiber attenuation by attenuating fibers from forming cones at the individual orifices while the molten glass at each orifice is at a pressure greater than the internal pressure of the respective cones and at a pressure less than the internal pressure of a bead formed at any orifice at which attenuation has been interrupted.
Claim 34
Dependent Claim
80 words
In a method of making glass fibers wherein molten glass is supplied to the orifices of an orifice plate, the improvment of preventing bead drop during fiber attenuation by attenuating fibers from forming cones at the individual orifices while the molten glass at each orifice is at a pressure greater than the internal pressure of the respective cones and at a pressure less than the internal pressure of a bead formed at any orifice at which attenuation has been interrupted.
References Cited (Backward Citations)
US21863A
Cited
US2212528A
Cited
USRE21863E
Cited
US2189822A
Cited
US2257767A
Cited
US2577213A
Cited
US2947027A
Cited
US2947028A
Cited
US3187076A
Cited
US3328144A
Cited
US3390972A
Cited
US3416906A
Cited
US3401536A
Cited
US3556753A
Cited
US3492104A
Cited
US3840358A
Cited
US4046535A
Cited
US3920429A
Cited
US3926600A
Cited
US3988135A
Cited
US4026689A
Cited
US4167403A
Cited
US4161396A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-12-18 | 1988-06-18 | 1988-12-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-12-18 | 1992-06-18 | 1992-12-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-12-18 | 1996-06-18 | 1996-12-18 | $7700.00 | Window Closed / Lapsed |