Resilient high modulus polyurethane elastomer

Claim 2

A high modulus polyurethane elastomeric article, comprising the cured admixture of: (A) about 0.97 to about 1.10 NCO equivalents of a polyurethane prepolymer prepared from a composition consisting essentially of: (1) about 3.1 to about 3.4 NCO equivalents of 4,4'-diphenylmethane diisocyanate, (2) about 0.35 to about 0.45 OH equivalents of a low moleculer weight triol selected from the group consisting of trimethylol ethane, trimethylol propane, trimethylol butane, trimethylol pentane and mixtures thereof, and (3) about 1.0 OH equivalent of polyoxytetramethylene glycol, with (B) 1.0 OH equivalent of hydroquinone di-(β-hydroxyethyl) ether; said elastomeric article characterized as being resilient, strong and crack resistant, and having a high rigidity.

Claim 3

A high modulus polyurethane elastomer structural member, comprising the cured admixture of: (A) about 5.0 to about 5.4 parts by weight of a polyurethane prepolymer prepared from a composition consisting essentially of: (1) about 3.10 moles to about 3.40 moles of 4,4'-diphenylmethane diisocyanate, (2) about 0.22 mole to about 0.32 mole of a low molecular weight triol, selected from the group consisting of trimethylol ethane, trimethylol propane, trimethylol butane, trimethylol pentane and mixtures thereof, and (3) 1.0 mole of polyoxytetramethylene glycol, with (B) 1.0 part by weight of a hydroquinone di-(β-hydroxyethyl) ether acting as a chain extender; said elastomer member characterized as being resilient, strong and crack resistant, and having a high rigidity.

Claim 4

A high modulus polyurethane elastomer structural member, comprising the cured admixture of: (A) about 5.0 to about 5.4 parts by weight of a polyurethane prepolymer prepared from a composition consisting essentially of: (1) about 3.10 moles to about 3.40 moles of 4,4'-diphenylmethane diisocyanate, (2) about 0.22 mole to about 0.32 mole of a low molecular weight triol, selected from the group consisting of trimethylol ethane, trimethylol propane, trimethylol butane, trimethylol pentane and mixtures thereof, and (3) 1.0 mole of polyoxytetramethylene glycol, with (B) 1.0 part by weight of a hydroquinone di-(β-hydroxyethyl) ether acting as a chain extender; said elastomer member characterized as being resilient, strong and crack resistant, and having a high rigidity.

Claim 5

A high modulus polyurethane elastomer structural member in circumferential contact with a launchable missile, comprising the cured admixture of: (A) about 5.0 to about 5.4 parts by weight of a polyurethane prepolymer prepared from a composition consisting essentially of: (1) about 3.10 moles to about 3.40 moles of 4,4'-diphenylmethane diisocyanate, (2) about 0.22 mole to about 0.32 mole of a low molecular weight triol selected from the group consisting of trimethylol ethane, trimethylol propane, trimethylol butane, trimethyl pentane and mixtures thereof, and (3) 1.0 mole of polyoxytetramethylene glycol, with (B) 1.0 part by weight of hydroquinone di-(β-hydroxyethyl) ether acting as sole chain extender; said elastomer member characterized as being resilient, strong and crack resistant, and rigid.

Claim 6

A high modulus polyurethane elastomer structural member in circumferential contact with a launchable missile, comprising the cured admixture of: (A) about 5.0 to about 5.4 parts by weight of a polyurethane prepolymer prepared from a composition consisting essentially of: (1) about 3.10 moles to about 3.40 moles of 4,4'-diphenylmethane diisocyanate, (2) about 0.22 mole to about 0.32 mole of a low molecular weight triol selected from the group consisting of trimethylol ethane, trimethylol propane, trimethylol butane, trimethyl pentane and mixtures thereof, and (3) 1.0 mole of polyoxytetramethylene glycol, with (B) 1.0 part by weight of hydroquinone di-(β-hydroxyethyl) ether acting as sole chain extender; said elastomer member characterized as being resilient, strong and crack resistant, and rigid.

Claim 7

The structural member of claim 3, where the triol is trimethylol propane.

Claim 8

The structural member of claim 3, mounted as a launch seal on a missile.

Claim 9

The structural member of claim 3, mounted as a launch seal on a launch tube surrounding a missile.

Claim 10

The structural member of claim 3, mounted as a shock isolator pad on a missile.

Claim 11

The structural member of claim 3, mounted as a shock isolator pad on a launch tube surrounding a missile.

Claim 12

The structural member of claim 3, wherein the triol is trimethylol propane having three hydroxy methyl groups attached to the same carbon atom, the prepolymer has about 8.1 % NCO, the weight ratio of prepolymer: chain extender is about 5.2:1, and the mole ratio of (diisocyanate):(triol):(glycol) is about (3.2):(0.26): (1.0).

Claim 13

The structural member of claim 3 attached to a launchable missile having a bottom firing end and disposed inside a launch tube, said structural member being a launch seal having a beam pointing downward toward the missile firing end, said seal beam circumferentially contacting the inside of the launch tube and being effective to retain gas pressure generated at the firing end of the missile.

Claim 14

The structural member of claim 9 attached to a launchable missile having a bottom firing end and disposed inside a launch tube, said structural member being a launch seal having a beam pointing downward toward the missile firing end, said seal beam circumferentially contacting the inside of the launch tube and being effective to retain gas pressure generated at the firing end of the missile.